WO2011025052A1 - Processing additive, molding composition, masterbatch of processing additive and molding article - Google Patents
Processing additive, molding composition, masterbatch of processing additive and molding article Download PDFInfo
- Publication number
- WO2011025052A1 WO2011025052A1 PCT/JP2010/064978 JP2010064978W WO2011025052A1 WO 2011025052 A1 WO2011025052 A1 WO 2011025052A1 JP 2010064978 W JP2010064978 W JP 2010064978W WO 2011025052 A1 WO2011025052 A1 WO 2011025052A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- processing additive
- fluoropolymer
- melt
- additive according
- mass
- Prior art date
Abstract
Description
Claims