WO2010142502A1 - Materials comprising a matrix and process for preparing them - Google Patents
Materials comprising a matrix and process for preparing them Download PDFInfo
- Publication number
- WO2010142502A1 WO2010142502A1 PCT/EP2010/056312 EP2010056312W WO2010142502A1 WO 2010142502 A1 WO2010142502 A1 WO 2010142502A1 EP 2010056312 W EP2010056312 W EP 2010056312W WO 2010142502 A1 WO2010142502 A1 WO 2010142502A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- matrix
- polymeric material
- groups
- weight
- isocyanate
- Prior art date
Abstract
Description
Claims