WO2010138378A2 - High strength multi-layer brazing sheet structures with good controlled atmosphere brazing (cab) brazeability - Google Patents
High strength multi-layer brazing sheet structures with good controlled atmosphere brazing (cab) brazeability Download PDFInfo
- Publication number
- WO2010138378A2 WO2010138378A2 PCT/US2010/035571 US2010035571W WO2010138378A2 WO 2010138378 A2 WO2010138378 A2 WO 2010138378A2 US 2010035571 W US2010035571 W US 2010035571W WO 2010138378 A2 WO2010138378 A2 WO 2010138378A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- brazing sheet
- aluminum brazing
- layer
- series
- alloy
- Prior art date
Abstract
Description
Claims