WO2010124923A1 - NICKEL BASE γ/ γ' SUPERALLOY WITH MULTIPLE REACTIVE ELEMENTS AND USE OF SAID SUPERALLOY IN COMPLEX MATERIAL SYSTEMS - Google Patents
NICKEL BASE γ/ γ' SUPERALLOY WITH MULTIPLE REACTIVE ELEMENTS AND USE OF SAID SUPERALLOY IN COMPLEX MATERIAL SYSTEMS Download PDFInfo
- Publication number
- WO2010124923A1 WO2010124923A1 PCT/EP2010/054593 EP2010054593W WO2010124923A1 WO 2010124923 A1 WO2010124923 A1 WO 2010124923A1 EP 2010054593 W EP2010054593 W EP 2010054593W WO 2010124923 A1 WO2010124923 A1 WO 2010124923A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- alloy
- superalloy
- sum
- nickel base
- components
- Prior art date
Abstract
Description
Claims