WO2010114643A1 - Polyurethane dispersion, method of producing the same, coated articles, and method for coating articles - Google Patents
Polyurethane dispersion, method of producing the same, coated articles, and method for coating articles Download PDFInfo
- Publication number
- WO2010114643A1 WO2010114643A1 PCT/US2010/023458 US2010023458W WO2010114643A1 WO 2010114643 A1 WO2010114643 A1 WO 2010114643A1 US 2010023458 W US2010023458 W US 2010023458W WO 2010114643 A1 WO2010114643 A1 WO 2010114643A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- polyols
- prepolymers
- polyurethane dispersion
- coating
- polyurethane
- Prior art date
Abstract
Description
Claims