CORROSION INHIBITING COMPOSITIONS
The present invention relates to corrosion inhibiting compositions for metals and metal alloys in the presence of water, oxygen or high ionic activity aqueous or semi- aqueous solutions. More particularly, there is provided corrosion inhibiting compositions containing monomeric chelating agents which form 5-8 membered ring chelating structures with a base metal including iron and iron alloys, such as steel, together with a film forming polymeric chelating agent which are used with aqueous and/or organic solvents.
Background off the Imvemfrioπi
Corrosion inhibitors are commonly found in cleaning and stripping compositions used in the semiconductor industries where various metals such as aluminum, aluminum alloys, titanium, titanium alloys, titanium/tungsten, tungsten, copper, etc are utilized.
The different functional classifications by which corrosion inhibitor compounds can be categorized are as follows:
1. Chelating agents
2. Reducing agents
3. Oxygen scavengers
4. Film forming agents
5. Oxidizing agents which form a protective film, typically of metal oxide. None of the corrosion inhibitor types are effective for all mechanisms of corrosion or for all metal or metal alloys. Oxygen scavengers are not particularly effective at
eliminating oxygen induced corrosion of iron or its alloys in the presence of an aqueous solution of high ionic character. Neither prior art corrosion inhibitors used in the semiconductor industry that are chelating agents or oxygen scavengers are effective in preventing corrosion of iron or carbon steel in the presence of water, oxygen or high ionic activity aqueous or semi-aqueous solutions.
Patent No. 3,996,147 to Settineri et al discloses the use of sulfonium corrosion inhibitors which inhibit corrosion of metal surfaces, particularly ferrous and cuprous metal surfaces in aqueous acid solutions alone or in combination with other chelating agents such as an aminocarboxylic acid, for example, ethylene diaminetetraacetic acid (EDTA).
Patent No. 5,334,332 to Lee et al, which is herein incorporated by reference discloses chelating agents and solvent systems which can be used with the inhibitors of the present invention. The reference does not disclose a film forming polymeric chelating agent.
Patent Nos. 5,707,947 and 5,753,601, which are herein incorporated by reference, disclose phenol derivatives that adsorb onto or absorb into the surface of neutral (zero valent) metals and/or chelation of their anions with the oxidized cationic metal surface which reduces the dissolution rate of the oxidized surface.
Summary off the Imventiom
The present invention relates to corrosion inhibiting compositions and the methods for their use containing film forming polymeric chelating agents which form 5,
6, 7, or 8-membered ring structures with a transition metal, which is oxidizable to a single or multivalent stable state including surfaces of iron and iron alloys. The film forming polymeric chelating agents are neutralized to about neutral or caustic pH.
Optionally, there is included a monomelic chelating agent.
The ratio of monomelic chelating agent to film forming agent is about 5: 1 to 1 : 5.
Advantageously, the neutralizing agent is a sterically hindered amine or a non- metal hydroxide. Such a sterically hindered amine can also be used in combinations with a metal hydroxide base to obtain the desired pH. Use of a metal hydroxide base alone will provide inferior corrosion protection from the composition of the invention.
Additionally, it is advantageous to include in the corrosion inhibiting compositions an effective oxygen scavenger.
It is a general object of the present invention to provide a corrosion inhibiting composition which can be used on a large variety of metal surfaces.
It is another object of the invention to provide a corrosion inhibiting composition containing chelating agents which form a 5, 6, 7, or 8-membered chelating rings with the atomic or surface metal elements or alloy.
It is yet another object of the invention to provide about neutral or alkaline cleaning, stripping and abrasive lapping compositions which contain corrosion inhibitors including a film forming chelating agent.
It is still another object of the invention to provide corrosion inhibitors for lapping, polishing (as in chemical mechanical polishing/planarization) and wire cutting systems that employ abrasive slurries and cleaners.
Description of the Preferred Embodiments
There is provided corrosion inhibiting compositions which contain a monomelic chelating agent in combination with a film forming polymeric chelating agent that forms 5-8 membered rings with the metal atoms or surface metal elements of a transition metal or alloy which is oxidizable to a single or multivalent stable state including but not limited to iron and iron alloy surfaces. The preferred film forming polymeric chelating agent is one which forms a stable chelating ring, preferably of 5, 6, or 7-elements or atoms (such elements will typically include, but not limited to the atom of the metal substrate, C, O, N and others). Examples of film forming polymeric chelating agents which can be used include:
1. Poly ortho-di or trihydroxyl, carboxy or sulfoxy aromatic compounds, for example novolacs, poly o-di or tricarboxylic acid styrenes, resoles, and
2. Polyacrylic acids and co-polymers thereof such as polyacrylic-co-maleic acid (PACM) which are miscible with water and compatible with many polar solvents.
The monomelic chelating agents include the known multi (ie; 1-3) hydroxy phenols, (ie; catechol, pyrogallol, 1, 2 or 1, 8- di-hydroxy naphthalene, which form 5 or 6-membered rings, etc.) multi-functional aromatic acids and the multi-functional aliphatic carboxylic or amino acids, hemi mallitic acid and trimallitic acid and polymers and copolymers thereof. The above plus dianions of alpha or beta bifunctional aliphatic acids can chelate and form 6, 7, or 8-membered rings for example, malonic acid and EDTA.. The ratio of monomelic chelating agents to film forming agents is about 5: 1 tol :5.
Aromatic chelating agents include gallic acid, pyrogallol, catechol, o- benzodicarboxylic acid, benzoic acid, ammonium benzoate, phthalic anhydride, mallitic acid, tetramethyl ammonium gallate, and derivatives thereof, and the like.
Other chelating agents glutaric acid which forms an 8-membered ring and compounds of the general formulas:
1. HO2C - (CH2)H - CO2H wherein n is 0-3
2. HO2C - (NH2)D - CO2H wherein n is 1-3
3. HO2C - (SH)n - CO2H wherein n is 1-3
4. HO2C - CH2 - NH - (CH2)n - CO2H wherein n is O or 1
5. H2N - (CHR)n - CO2H wherein n is 1 -4 and R is hydrogen, alkyl of 1-4 carbon atoms, alkylene of 1-4 carbon atoms, aryl or benzo.
6. HO2 - (CHR)n - SH - CO2H wherein R is hydrogen or alkyl and n is 1-3
Multifunctinal aliphatic or non aromatic cyclic chelating agents include malonic acid, EDTA, CDTA, imino diacetic acid, maleic acid, malic acid, D,L-maleic acid, cyclohexanl 1,2-dicarboxylic acid and the like, form stable 6, 7 or 8 membered rings with the base metals at or about neutral or caustic pH. The preferred monomelic chelating agent is malonic acid which is also neutralized in the same manner as the polymeric chelating film formor.
Although neutralization of the chelating agent can be performed with alkali or alkaline earth metal caustic such as barium, magnesium, sodium or potassium hydroxide, or an organic base, the strongest chelation occurs when the neutralizing base is a sterically hindered amine or a non-metal hydroxide such as triethanolamine (TEA) and tetramethylammonium hydroxide (TMAH) or other alkanolamines. In this manner, the counter positive ion of the neutralizing base is large and bulky, not allowing for the close proximity to the negatively charged polymer or monomelic agent. This means that the negative charge on the polymer or monomelic agent is more isolated from the positive counter ion and is more available for the formation of a strong chelation bond with the base metal. A preferred method of neutralization is to partially neutralize with an alkali metal caustic such as NaOH or KOH and then complete the neutralization with a sterically hindered amine, or substituted ammonium hydroxide.
To prevent the corrosion of iron and iron alloys, the combination of an effective film forming chelation compound and a strong monomer chelation compound provide an effective corrosion inhibitor system. However, further effectiveness can be achieved by the addition of an oxygen scavenger. Some chelating agents are also oxygen scavengers. The most common oxygen scavengers are nitrates, sulfites, and hydroquinone. The oxygen scavengers include tetramethylaminosulfite (TMAS), tetramethylaminonitrite, alkali metal sulfite including sodium sulfite, and potassium sulfite, alkali metal nitrite including sodium nitrite and potassium nitrite, ammonium sulfite, ammonium nitrite, and the like. Other O2 scavengers known include ascorbic acid, multi-hydroxy aromatics such as catechol, pyrogallol, hydroquinone, a hydroxyl-N-heterocyclic such as
8-hydroxyquinoline and others. Most preferred is hydroquinone. The oxygen scavengers can be utilized in an amount of about 0.1 to 50% of the total inhibitor composition.
The corrosion inhibitors of the invention have been found to be particularly more advantageous in high ionic aqueous media than prior art corrosion inhibitors. They are especially more advantageous over previous inhibitors for iron and steel products. They are preferably used in compositions having a pH of 6.0 to 11.0.
The inhibitors of the invention can be formulated with aqueous and semi-aqueous organic solvent systems in an amount of about 0.25 to 10% by weight of composition, preferably about 0.5 to 5%. The solvents and various co-solvents and cleaning compositions in which the corrosion inhibitors may be used are seen, for example, in U.S. Pat. No. 5,334,332 to Lee, U.S. Pat. Nos. 4,395,479; 4,428,871; and 4,401748 issued to Ward et al and U.S. Patent No. 5,308,745 issued to Schwartzkopf, which are herein incorporated by reference. Preferred solvents in the patents include water solutions of tetramethylammonium hydroxide (TMAH), various pyrrolidinone compounds such as N- methylpyrrolidnone (NMP), gamma-butyrolactone (BLO), diethyleneglycol monoalkyl ether, alkanolamines including monoethanolamine, triethanolamine (TEA), 2-amino-2- ethoxyethanol, polar solvents including alkylene glycol, poly-alkylene glycols, ethylenediamine, alkyl and dialkyl aliphatic amides such as DMAC and the like.
A typical lapping or slurry composition comprises; about 1-30% by weight of in situ formed aqueous or semi aqueous aluminum hydroxide,
about 1 to 30% by weight of salt compounds selected from the group consisting of sodium or potassium sulfate, tetramethylammonium sulfate, tetraethylammonium sulfate and alkali or alkaline earth metal sulfate,
about 0.25 to 10% by weight of a corrosion inhibitor comprising polyacrylic-co-maleic acid at a film forming average molecular weight of about 1500 or greater and malonic acid. The polyacrylic-co-maleic acid and malonic acid being present in a ratio of 5 : 1 to 1 :5,
about 1-50% by weight of an abrasive material, the remainder being water.
Optionally, an oxygen scavenger can be included.
The following Examples are illustrative of the invention and are not limited to the scope of the invention.
Example 1
A corrosion inhibitor composition of the invention was prepared by admixing the following:
Ingredient Pants by Weight
Polyacrylic acid - co-maleic acid (PACM) 1.00
(mols. Wt. 1500)
Malonic acid 1.00
Hydroquinone 0.25
0.5 to 5% by weight of the corrosion inhibitors can be added to an aqueous abrasive slurry, lapping, stripping and cleaning composition that may include triethanolamine (TEA), which is also a neutralizing base, and dissolved salts create a high ionic strength aqueous mixture.
Example 2
Tests were conducted measuring the effect of the corrosion inhibitor system visually and by optical microscopy without an oxygen scavenger using carbon steel. The compositions were prepared by partially neutralizing the corrosion inhibitor with 1.0N sodium hydroxide and then bringing the pH to 8.5 with TEA. One half of sample strips of spring carbon steel were suspended into the test media comprising a 15% salt solution of neutralized aluminum sulfate for six hours at ambient temperature. At the end of the time the test pieces were rinsed with D.I. water and blown dry with nitrogen. The results were as follows:
% Aqueous % Commercial Neutralized Corrosion
Salt SoIutioE % MaIonk % PACM Ferrous CJ. to pH Results
15 0.5 0.5 8.5 No Corrosion
15 0.75 1.5 8.5 No Corrosion
15 1 2 8.5 No Corrosion
15 1.25 1.25 8.5 No Corrosion
15 1.5 0.75 8.5 No Corrosion
15 - DeCore BEPS 8.5 Visual Surface
1- 2% Etching
15 - - Colacor-400 ~ -8.0 Significant Surface 0.05-0.5% Corrosion
15 - - DeCore -APCI-95 - -8.0 Significant Surface
1-2% Corrosion
15 - - DeCore -1MT 100LF ~ 8.0 Significant Surface 0.2-.05% Corrosion
15 - DeTrope CA-100 - 8.0 Surface Corrosion 1-2% Visual
Example 3
Stripping and cleaning compositions for photoresists were prepared as follows with the corrosion inhibitor of Example 1 and tested according to Example 2.
Ingredient Wt. % Wt. % Corrosion Corrosion on a Ferrous
Inhibitor Steel Surface
1. Triethanol amine 90 1.5 None
Water 10
2. Triethanol amine 30 1.5 None
Water 50
Ethylene glycol 20
Monoethyl ether
3. Polyethylene glycol 50 1.5 None
Water 50 (neutralized w/NaOH)
4. N-methylpyrrolidinone 45 1.5 None
Water 40
Sulfolane 15
5. Hydroxylamine 30 1.5 None (50% aq. solution) 2-amino-2-ethoxyethanol 20 Water 50
6. DMAc 55 1.5 None
MEA 15
Water 30
7. Water 70 1.5 None
TEA 10
50% H.A. aq. 20