WO2010081118A1 - Formation of thin uniform coatings on blade edges using isostatic press - Google Patents
Formation of thin uniform coatings on blade edges using isostatic press Download PDFInfo
- Publication number
- WO2010081118A1 WO2010081118A1 PCT/US2010/020686 US2010020686W WO2010081118A1 WO 2010081118 A1 WO2010081118 A1 WO 2010081118A1 US 2010020686 W US2010020686 W US 2010020686W WO 2010081118 A1 WO2010081118 A1 WO 2010081118A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- coating
- ptfe
- hip
- blade
- isostatic press
- Prior art date
Abstract
Description
Claims