WO2010080228A1 - Shape memory polymer - Google Patents
Shape memory polymer Download PDFInfo
- Publication number
- WO2010080228A1 WO2010080228A1 PCT/US2009/065830 US2009065830W WO2010080228A1 WO 2010080228 A1 WO2010080228 A1 WO 2010080228A1 US 2009065830 W US2009065830 W US 2009065830W WO 2010080228 A1 WO2010080228 A1 WO 2010080228A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- group
- polymerizable composition
- multicyclic
- diene
- shape
- Prior art date
Abstract
Description
Claims