WO2010075024A1 - Non-woven sheet containing fibers with sheath/core construction - Google Patents
Non-woven sheet containing fibers with sheath/core construction Download PDFInfo
- Publication number
- WO2010075024A1 WO2010075024A1 PCT/US2009/067833 US2009067833W WO2010075024A1 WO 2010075024 A1 WO2010075024 A1 WO 2010075024A1 US 2009067833 W US2009067833 W US 2009067833W WO 2010075024 A1 WO2010075024 A1 WO 2010075024A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- polymer
- fibers
- pps
- pet
- woven
- Prior art date
Abstract
Description
Claims