WO2010047439A1 - Supported catalyst for synthesizing carbon nanotubes, method for preparing thereof and carbon nanotube using the same - Google Patents
Supported catalyst for synthesizing carbon nanotubes, method for preparing thereof and carbon nanotube using the same Download PDFInfo
- Publication number
- WO2010047439A1 WO2010047439A1 PCT/KR2008/007781 KR2008007781W WO2010047439A1 WO 2010047439 A1 WO2010047439 A1 WO 2010047439A1 KR 2008007781 W KR2008007781 W KR 2008007781W WO 2010047439 A1 WO2010047439 A1 WO 2010047439A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- supported catalyst
- based polymer
- catalyst
- carbon nanotubes
- carbon nanotube
- Prior art date
Abstract
The present invention provides a new supported catalyst for synthesizing carbon nanotubes. The supported catalyst has a metal catalyst which is one or more selected from Fe, Co and Ni, and which is supported onto an alumina, magnesium oxide or silica supporting body, and the supported catalyst has an average diameter of about 30 to about 100 μm.
Description
[DESCRIPTION] [Invention Title]
SUPPORTED CATALYST FOR SYNTHESIZING CARBON NANOTUBES, METHOD FOR PREPARING THEREOF AND CARBON NANOTUBE USING THE SAME
[Technical Field]
<i> The present invention relates to a supported catalyst for synthesizing carbon nanotubes, a method for preparation thereof and carbon nanotubes manufactured using the same. More particularly, the present invention relates to a supported catalyst having even size and uniform spherical shape prepared by spray-drying a catalytic solution comprising water-soluble polymer, and carbon nanotubes with improved productivity and uniformity prepared in a fixed bed reactor or a fluidized bed reactor using the supported catalysts.
<2>
[Background Art]
<3> Carbon nanotubes discovered by Iijima in 1991 have hexagon beehive-like structures connecting one carbon atom thereof with three other neighboring carbon atoms and the hexagon structures thereof are repeated and rolled into a cylinder or a tube form.
<4> Since the discovery of carbon nanotubes, theses publications and patent applications have increased and there has been much theoretical research and development regarding industrial applications of carbon nanotubes. Carbon nanotubes have excellent mechanical properties, electrical select ivities, field emission properties, hydrogen storage properties, adaptiveness to polymer composite, and the like, and they are known as nearly flawless and perfect advanced materials. Carbon nanotubes are mainly synthesized by arc discharge method, laser ablation, chemical vapor deposition, and the like, and they are classified as single-walled, double-walled, or multi-walled carbon nanotubes according to the numbers of walls. Despite these various synthetic methods and structures, there are many limitations, such as high production cost, to synthesis of carbon nanotubes with high yields and
purity.
<5> Recently, there have been many studies of new technology for synthesis of carbon nanotubes that can produce quantities of carbon nanotubes at once, as well as a proper catalytic synthetic method of carbon nanotubes with high yields and purity. Among the various synthetic methods, the thermal chemical vapor deposition is absolutely advantageous with regard to large-scale production and needs simple equipment. The thermal chemical vapor deposition is classified as a fixed bed reactor or a fluidized bed reactor method. The fixed bed reactor method is not largely influenced by relative shapes or sizes of metal supporting bodies, but it cannot produce quantities of carbon nanotubes at once due to space limitation inside the reactor. The fluidized bed reactor can synthesize quantities of carbon nanotubes at once more easily than the fixed bed reactor because the reactor stands up vertically. Because the fluidized bed reactor can produce quantities of carbon nanotubes at once continuously compared with the fixed bed reactor, there are many studies of the fluidized bed reactor. However, the fluidized bed reactor needs metal supporting bodies of even shapes and sizes to float the metal supporting bodies evenly. Accordingly, there is a need to develop a method of synthesizing a catalyst having metal supporting body of even shape and size, which is essential to the fluidized bed reactor.
<6> To solve this problem, the present inventor has developed a supported catalyst for synthesizing carbon nanotubes especially suitable to a fluidized bed reactor (which needs floatabi lity of catalyst) as well as a fixed bed reactor by making the catalyst able to maintain spherical shape during a firing process using water-soluble polymer as a binder in a metal- catalytic solution.
<7>
[Disclosure] [Technical Problem]
<8> An object of the present invention is to provide a supported catalyst of spherical shape for synthesizing carbon nanotubes.
<9> Another object of the present invention is to provide a supported catalyst having even spherical shape and diameter. <io> Another object of the present invention is to provide a supported catalyst that can mass-produce carbon nanotubes and save time and expense using said metal nano catalyst. <ii> Another object of the present invention is to provide a supported catalyst that can be applied to both fluidized bed reactors and fixed bed reactors in regard to synthesis of carbon nanotubes. <12> Another object of the present invention is to provide a supported catalyst especially suitable to a fluidized bed reactor. <i3> Another object of the present invention is to provide a new manufacturing process of supported catalyst of spherical shape. <14> Another object of the present invention is to provide a supported catalyst having high efficiency of productivity, selectivity, and high purity. <15> Other aspects, features and advantages of the present invention will be apparent from the ensuing disclosure and appended claims.
<16>
[Technical Solution]
<17> An aspect of the present invention provides a supported catalyst for synthesizing carbon nanotubes. The supported catalyst has a metal catalyst selected from Fe, Co and Ni and an aluminum oxide, magnesium oxide, or silicon dioxide supporting body and has spherical shape with about 30 to about 100 μm of average diameter.
<18>
<19> In one exemplary embodiment of the present invention, the supported catalyst may have mole ratio as follow: <20> (Co)Fe : Mo : (Mg)Al = x : y : z <2i> (wherein, l≤x≤lO, 0<y<5 and 2<z<70).
<22>
<23> In another exemplary embodiment, the supported catalyst may have mole
ratio as follow:
<24> Fe : Mo : Al = x : y : z
<25> (wherein, l≤x≤ lO , 0 <y<5 and 2 < z <70) .
<26>
<27> The supported catalyst is empty inside.
<28> Another aspect of the present invention provides a process of synthesizing the supported catalyst. The synthetic process comprises preparing a mixing catalytic solution by mixing water-soluble polymer and catalytic aqueous solution which comprises metal catalyst and supporting body; preparing catalyst powder by spray-drying the mixing catalytic solution; and firing the catalyst powder.
<29> In exemplary embodiments, the metal catalyst may be at least one selected from Fe(N03)3, Co(N03)2, Ni(N03)2, Fe(OAc)2, Co(OAc)2, and Ni(OAc)2.
<30> The supporting body may be at least one selected from aluminum nitrate, magnesium nitrate, and silicon dioxide. Preferably, the metal catalyst and the supporting body are in an aqueous phase.
<3i> In exemplary embodiments, the water-soluble polymer may be urea based polymer, melamine based polymer, phenol based polymer, unsaturated polyester based polymer, epoxy based polymer, resorcinol based polymer, acetic acid vinyl based polymer, poly vinyl alcohol based polymer, vinyl chloride based polymer, polyvinylacetal based polymer, acryl based polymer, saturated polyester based polymer, polyamide based polymer, polyethylene based polymer, vinyl based polymer, starch, glue, gelatin, albumin, casein, dextrin, acid modified starch, and cellulose, and the like.
<32> In exemplary embodiments, the water-soluble polymer may be used in amount of about 1 to about 50 % by weight based on the total weight of the solids in aqueous catalytic solution.
<33> The spray-drying may be performed at a temperature of about 200 to about 300 "C , about 5,000 to about 20,000 rpm of a disc-revolution speed, and about 15 to about 100 mL/min of solution injecting rate.
<34> The firing may be performed at a temperature of about 350 to about
1,100 °C. The supported catalyst prepared by the above process has a spherical shape.
<35> Another aspect of the present invention provides a carbon nanotube manufactured using the supported catalyst. The carbon nanotube may be synthesized in a fluidized bed layered reactor or in a fixed bed reactor, preferably in a fluidized bed layered reactor. In exemplary embodiments, the carbon nanotube may be prepared by injection of hydrocarbon gas at a temperature of about 650 to about 1,100 °C in the presence of the supported catalyst.
<36>
[Description of Drawings] <37> FIG. Ka), (b) are schematic views of the supported catalyst for synthesizing carbon nanotubes of the present invention. <38> FIG. 2(a) is a transmission electron microscope (TEM) image of spray-dried particles prepared in Example 1, and 2(b) is a transmission electron microscope (TEM) image of the supported catalysts prepared in
Example 1. <39> FIG. 3(a), (b) are transmission electron microscope (TEM) images of carbon nanotubes prepared in Example 1. <40> FIG. 4 is a transmission electron microscope (TEM) image of carbon nanotube prepared using the supported catalyst of Example 2. <4i> FIG. 5 is a transmission electron microscope (TEM) image of supported catalysts prepared in Comparative Example 1.
<42>
[Best Mode]
<43> Supported catalyst
<44> The present invention provides a supported catalyst for synthesizing carbon nanotubes. FIG. Ka) is a schematic view of a supported catalyst for synthesizing carbon nanotubes of the present invention. The metal catalysts(2) are supported in the supporting body(l) of the supported catalyst and the supported catalyst has substantially spherical shape.
Hereupon, the spherical shape comprises an oval shape as well as a perfect globular shape as an image observed by a transmission electron microscope (TEM) of 500 magnifications. In exemplary embodiments, an oval form may have about 0 to about 0.2 flattening rate. The supporting body(l) may form pores on its surface as described in FIG. Kb). The crookedness and projections may be formed on the surface of the supported catalyst of the present invention. The supported catalyst has hollow structure such that the interior of the supported catalyst is empty. The metal catalyst(2) is distributed in the hollow interior as well as on the surface of the supporting body. <45> As the metal catalyst, Fe, Co, Ni, alloy or combinations thereof may be used. As the supporting body, aluminium oxide, magnesium oxide, silicon dioxide, or combinations thereof may be used. The supported catalyst of the present invention has about 30 to about 100 μm of average diameter, preferably about 40 to about 95 μm, more preferably about 50 to about 90 μm. In an exemplary embodiment, the supported catalyst of the present invention may have about 35 to about 50 μm of average diameter. In another exemplary embodiment, the supported catalyst of the present invention may have about 55 to about 80 μm or about 75 to about 100 μm of average diameter.
<46>
<47> In an exemplary embodiment of the present invent ion, the supported catalyst may have mole rat io as fol low: <48> (Co)Fe : Mo : (Mg)Al = x : y : z
<49> (wherein, l <x < 10, 0<y< 5 and 2 < z ≤ 70) .
<50>
<5i> In an exemplary embodiment, the supported catalyst may have mole ratio as follow:
<52> Fe : Mo : Al = x : y : z
<53> (wherein, l <χ < 10, 0<y< 5 and 2< z < 70) .
<54>
<55> The manufacturing process of the supported catalyst
<56> Another aspect of the present invention provides the manufacturing
process of the supported catalyst. The manufacturing process comprises preparing a mixing catalytic solution by dissolving a water-soluble polymer into an aqueous catalytic solution in which metal catalyst and supporting bodies are compounded; preparing catalyst powder by spray-drying the mixing catalytic solution; and firing the catalyst powder. <57> In exemplary embodiments, Fe(N0s)3, Co(NU3)2, Ni (103)2, Fe(0Ac)2,
Co(OAc)2, or Ni(0Ac)2 may be used as the metal catalyst and these materials may be used singly or together with two or more other materials. In exemplary embodiments, the metal catalyst may have a hydrate form. For example, it may be used as a form of Iron(III) nitrate nonahydrate or Cobalt nitrate nonahydrate.
<58> The supporting body may be aluminum nitrate, magnesium nitrate silicon dioxide or the others and is not necessarily limited to these examples.
<59> Preferably, aluminum nitrate nonahydrate may be used.
<60> The metal catalyst and the supporting body are dissolved into water respectively and are mingled into aqueous solution phase together.
<6i> In another exemplary embodiment, lumping of metal catalysts may be prevented by introducing molybdenum activator such as Ammonium Molybdate tetrahydrate during firing process at high temperature. In another exemplary embodiment, citric acid may be used as an activator. The aqueous catalytic solution containing the metal catalysts and the supporting bodies and selectively the molybdenum activator are stirred into complete dissociation.
<62> The mixing catalytic solution is prepared by injecting and dissolving a water-soluble polymer into the aqueous catalytic solution containing the metal catalysts and the supporting bodies. In the present invention, the water-soluble polymer is used as a binder to maintain the spherical shape. Because the catalyst particles may be easily broken during heat treatment such as the firing process after spray-drying, the water-soluble polymer is added to aqueous catalytic solution to prevent breaking of the metal catalyst and to maintain the catalyst as a spherical shape.
<63> The water-soluble polymer can be dissolved in water and any polymer which has an adhesive property can be used as the water-soluble polymer. For example, the water-soluble polymer may comprise the polymer of urea based polymer, melamine based polymer, phenol based polymer, unsaturated polyester based polymer, epoxy based polymer, resorcinol based polymer, acetic acid vinyl based polymer, poly vinyl alcohol based polymer, vinyl chloride based polymer, polyvinylacetal based polymer, acryl based polymer, saturated polyester based polymer, polyamide based polymer, polyethylene based polymer, vinyl based polymer, starch, glue, gelatin, albumin, casein, dextrin, acid modified starch, cellulose, and the like and is not necessarily limited to these examples.
<64> Non-aqueous polymer like polyethylene may also be mingled into aqueous catalytic solution by pretreatment . The non-aqueous polymer may be used alone or in combination with another non-aqueous polymer.
<65> In exemplary embodiments, the water-soluble polymer may be injected in amount of about 1 to about 50 % by weight, preferably about 15 to about 25 % by weight based on the total solids dissolved in the aqueous catalytic solution. In exemplary embodiments, about 5 to about 20 % by weight of the water-soluble polymer may be used more preferably. In another exemplary embodiment, about 20 to about 45 % by weight of the water-soluble polymer may be used.
<66> The mixing catalytic solution dissolving the water-soluble polymer is changed into particle form of spherical shape by a spray-drying method.
<67> The spray-drying method is the easiest way to produce a large quantity of products among the methods to synthesize the metal supporting body having even spherical shape and even size. The spray-drying method sprays the fluid-state supply into the hot drying gas so that drying happens nearly instantly. The reason that dryness happens so fast is that the fluid-state supply is sprayed by the atomizer and as a result its surface area becomes very large. The atomizer influences the size of catalyst powder which is also influenced by density of solution, quantity of spraying, and rotation rate of
atomizer disc. In exemplary embodiments, the spray-drying may be performed at about 200 to about 300 °C, preferably about 270 to about 300 °C. There are two types of spraying methods, nozzle-type and disc-type which forms and sprays the drops of solution by the disc rotation. In an exemplary embodiment, the supported catalyst powder of more even size is synthesized by applying the disc-type. The particle size and distribution can be regulated by disc rotation rate, inlet capacity of solution, density of solution and the like. In exemplary embodiments of the present invention, the disc rotation rate may be about 5,000 to about 20,000 rpm, and inlet capacity of solution may be about 15 to about 100 mL/min. In another exemplary embodiment, the disc rotation rate may be about 10,000 to about 18,000 rpm, about 12,000 to about 19,000 rpm or about 5,000 to about 9,000 rpm. The spray-drying may be performed with about 15 to about 60 mL/min, about 50 to about 75 mL/min or about 80 to about 100 mL/min of inlet capacity of solution.
<68> The catalyst powder synthesized by spray-drying is heat-treated through firing. The crystallization to metal catalyst is accomplished by such firing process. The diameter and the property of carbon nanotube vary with temperature and firing time of catalyst powder. In exemplary embodiments, the firing process may be performed at about 500 to about 800 °C , preferably about 450 to about 900 °C , more preferably about 350 to about 1,100 °C of temperature. In another exemplary embodiment, the firing process may be performed at about 350 to about 500 °C , about 550 to about 700 "C, about 650 to about 900 °C or about 750 to about 1,100 °C of temperature. The firing process may be performed about 15 minutes to about 3 hours, preferably about 30 minutes to about 1 hour. Usually, the spherical shape-particle prepared by spray-drying may be easily broken during firing process. However, in the present invention the spherical shape can be maintained during the high temperature firing process because the water-soluble polymer acts as a binder. Here, the water-soluble polymer does not remain in the final products by volatilization during firing process. The supported catalyst synthesized
by the method of present invention shows the characteristic of having a substantially spherical shape.
<69>
<70> Carbon nanotube
<7i> Another aspect of the present invention provides a carbon nanotube synthesized using the supported catalyst. The supported catalyst of the present invention can be applied to both a fluidized bed reactor and a fixed bed reactor, and preferably a floating layer reactor. In the fluidized bed reactor, a large quantity of carbon nanotube can be synthesized at once, and the supported catalyst of the present invention can be applied preferably to the fluidized bed reactor because the supported catalyst of the present invention having even spherical shape and even diameter can float well.
<72> In exemplary embodiments, the carbon nanotube can be prepared by injection of hydrocarbon gas at a temperature of about 650 to about 1,100 °C , for example about 670 to about 950 0C, in the presence of the supported catalyst. In one exemplary embodiment, the carbon nanotube can be prepared at the temperature of about 650 to about 800 °C . In other exemplary embodiments, the carbon nanotube can be prepared at about 800 to about 990 0C temperature, and in other exemplary embodiments, the carbon nanotube can be prepared at about 980 to about 1,100 "C temperature. The hydrocarbon gas may include but is not limited to methane, ethane, acetylene, LPG, and the like, and combinations thereof. The hydrocarbon gas is supplied for about 15 minutes to about 2 hours, for example about 30 to about 60 minutes.
<73>
<74> The present invention may be better understood by reference to the following examples which are intended to illustrate the present invention and do not limit the scope of the present invention, which is defined in the claims appended hereto.
<75>
[Mode for Invent ion] <76> Example 1
<77> Catalyst powder was prepared by mixing about 20 % by weight of polyvinylpyrrolidone (PVP) aqueous polymer based on the total weight of solid with a aqueous catalytic solution comprising Fe, Co, Mo, Al2O3 (Mole ratio of
Fe : Co : Mo : Al2O3 = 0.24 : 0.36 : 0.02 : 1.44); spraying the mixture into interior of Niro Spray-Dryer (the trade name ); and simultaneously drying the sprayed mist using hot air of 290 °C . Figure 2(a) is a transmission electron microscope (TEM) image of catalyst powder prepared at about 8,000 rpm of the disc revolution speed and about 30 mL/min of injection volume of solution. A supported catalyst was prepared by firing the catalyst powder at temperature of about 550 °C and normal pressure for 30 minutes in air atmosphere. Figure 2(b) is a transmission electron microscope (TEM) image of the supported catalyst powder. The metal catalyst maintained sphere shape thereof despite the heat treatment as shown in Figure 2(b).
<78> A carbon nanotube was prepared by pouring 100/100 seem of ethylene and hydrogen gas (1:1 ratio) over the supported catalyst of about 0.03 g for 45 minutes.
<79> Figure 3(a) and (b) are respectively transmission electron microscope (TEM) images of 35 magnifications and 100 magnifications. The prepared carbon nanotube had an even diameter as shown in Figure 3.
<80>
<8i> Example 2
<82> Example 2 was performed in the same manner as the above Example 1 except using polyvinylalcohol (PVC) as aqueous polymer. The spherical shape of the prepared supported catalyst was confirmed by transmission electron microscope (TEM) images. Carbon nanotube was prepared in the same manner as the above Example 1 using the prepared supported catalyst. The diameter of catalyst and the yield of carbon nanotube are shown in Table 1.
<83>
<84> [Table 1]
<85> <86> *Yield: (weight of prepared CNT - weight of catalyst)/ weight of catalyst X 100
<87> <88> Comparative Example 1 <89> Comparative Example 1 was performed in the same manner as the above Example 1 except firing catalyst solution at 550 °C for 30 minutes in air atmosphere without spray-drying process. Figure 5 shows transmission electron microscope (TEM) images of prepared supported catalyst. The prepared supported catalyst did not have a spherical shape which is essential to fluidized reactor as shown in Figure 5.
<90> <91> Simple changes and modifications of the present invention can be easily carried out by a person of ordinary skill in the art, and these changes and modifications can be considered to be included in the scope of the present invention.
Claims
[CLAIMS] [Claim 1]
<93> A supported catalyst for synthesizing carbon nanotubes, <94> wherein metal catalysts comprising one or more selected from Co and Fe, are supported onto an alumina, magnesium oxide or silica supporting body, and the supported catalyst has an average diameter of about 30 to about 100 μm.
<95>
[Claim 2] <96> The supported catalyst for synthesizing carbon nanotubes of claim 1, wherein the supported catalyst has mole ratio as follow^ <97> (Co)Fe : Mo ,: (Mg)Al = x : y : z <98> (wherein, l≤x≤lO, 0<y<5 and 2<z<70).
<99>
[Claim 3] <ioo> The supported catalyst for synthesizing carbon nanotubes of claim 1, wherein the supported catalyst has mole ratio as follow- <ioi> Fe : Mo : Al = x : y : z <iO2> (wherein, l≤x≤lO, 0<y<5 and 2<z<70).
<103>
[Claim 4]
<iO4> The supported catalyst for synthesizing carbon nanotubes of claim 1, wherein the supported catalyst has hollow structure.
<105>
[Claim 5] <iO6> . A method of preparing a supported catalyst for synthesizing carbon nanotubes, comprising the steps of: <iO7> preparing a mixing catalytic solution by mixing water-soluble polymer and catalytic aqueous solution which comprises metal catalyst and supporting body; <iO8> preparing catalyst powder by spray-drying the mixing catalytic solution; and <iO9> firing the catalyst powder. <110>
[Claim 6]
<πi> The method of claim 5, <ii2> wherein the metal catalyst is at least one selected from Fe(N0s)3,
Co(N03)2) Ni(NOs)2, Fe(OAc)2, Ni(OAc)2, and Co(OAc)2.
<113>
[Claim 7]
<ii4> The method of claim 5,
<ii5> wherein the supporting body is at least one selected from the group consisting of aluminum nitrate, magnesium nitrate, and silicon dioxide.
<116>
[Claim 8]
<ii7> The method of claim 5,
<ii8> wherein the metal catalyst and the supporting body are in an aqueous phase.
<119>
[Claim 9]
<12O> The method of claim 5,
<i2i> wherein the water-soluble polymer is at least one selected from the group consisting of urea based polymer, melamine based polymer, phenol based polymer, unsaturated polyester based polymer, epoxy based polymer, resorcinol based polymer, acetic acid vinyl based polymer, poly vinyl alcohol based polymer, vinyl chloride based polymer, polyvinylacetal based polymer, acryl based polymer, saturated polyester based polymer, polyamide based polymer, polyethylene based polymer, vinyl based polymer, starch, glue, gelatin, albumin, casein, dextrin, acid modified starch, and cellulose.
<122>
[Claim 10] <123> The method of claim 5, <124> wherein the water-soluble polymer is used in amount of about 1 to about 50 % by weight based on the total weight of the solids in aqueous catalytic solution.
<125>
[Claim 11]
<126> The method of claim 5,
<127> wherein the spray-drying is performed at about 200 to about 300 °C temperature.
<128>
[Claim 12]
<i29> The method of claim 11, <i30> wherein the spray-drying is performed at about 5,000 to about 20,000 rpm of disc-revolution speed, and about 15 to about 100 mL/min of solution injecting rate.
<131>
[Claim 13]
<132> The method of claim 5,
<133> wherein the firing is performed at a temperature of about 350 to about 1,100 0C.
<134>
[Claim 14]
<135> A supported catalyst for synthesizing carbon nanotubes having spherical shape which is prepared by the method as defined in any of claims 5 to 13.
<136>
[Claim 15]
<137> A carbon nanotube synthesized using the supported catalyst as defined in any of claims 1 to 4.
<138>
[Claim 16]
<139> The carbon nanotube of claim 15, <i40> wherein the carbon nanotube is synthesized in a fluidized bed reactor. <141>
[Claim 17]
<142> The carbon nanotube of claim 15, <143> wherein the carbon nanotube is synthesized by injection of hydrocarbon gas at a temperature of about 650 to about 1,100 °C in the presence of the supported catalyst.