WO2010003035A1 - Coated reactor tube, method of making the coated tube, method for making bismuth containing glass frit powders using aerosol decomposition in said reactor tube. - Google Patents
Coated reactor tube, method of making the coated tube, method for making bismuth containing glass frit powders using aerosol decomposition in said reactor tube. Download PDFInfo
- Publication number
- WO2010003035A1 WO2010003035A1 PCT/US2009/049469 US2009049469W WO2010003035A1 WO 2010003035 A1 WO2010003035 A1 WO 2010003035A1 US 2009049469 W US2009049469 W US 2009049469W WO 2010003035 A1 WO2010003035 A1 WO 2010003035A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- tube
- coated
- bismuth
- reactor tube
- glass
- Prior art date
Abstract
Description
Claims