WO2009153968A1 - Method for producing carbon fiber - Google Patents
Method for producing carbon fiber Download PDFInfo
- Publication number
- WO2009153968A1 WO2009153968A1 PCT/JP2009/002725 JP2009002725W WO2009153968A1 WO 2009153968 A1 WO2009153968 A1 WO 2009153968A1 JP 2009002725 W JP2009002725 W JP 2009002725W WO 2009153968 A1 WO2009153968 A1 WO 2009153968A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- carbon fiber
- catalyst
- mass
- compound containing
- resin
- Prior art date
Abstract
Description
With the method (1) using a platy substrate carrier, since the size of the catalytic metal to be supported can be arbitrarily controlled by applying various film formation techniques, this method is usually used in laboratory demonstration of research. For example, NPL 1 discloses that using those in which an aluminum layer having thickness of 10 nm, an iron layer having thickness of 1 nm, and a molybdenum layer having thickness of 0.2 nm are generated on a silicon substrate can give a tube-like mulitiwall nanotube or a double-wall nanotube having a fiber diameter of approximately 10 to 20 nm. Also, PTL 4 discloses a catalyst by supporting a metal composed of a combination of Ni, Cr, Mo and Fe or a combination of Co, Cu, Fe and Al on a platy substrate carrier by a sputtering method or the like. And PTL 4 describes manufacture of a carbon fiber therewith. In order to use the carbon nanotube as filler obtained by this method using a platy substrate carrier to be added into a resin or the like, it is necessary to be separated from the substrate and collected. The carbon nanotube collected as the above substantially contains only catalytic metal component as impurities, but since generation efficiency of the carbon nanotube with respect to a catalyst mass is markedly low, the content of the catalytic metal component in the carbon nanotube is likely to be high. Moreover, if this method is to be industrially utilized, since a platy substrate surface area can not be ensured unless a number of substrates are arranged, not only that device efficiency is low but also many processes such as supporting of the catalytic metal on the substrate, synthesis of the carbon nanotube, collection of the carbon nanotube from the substrate and the like are needed, which is not economical, and industrial utilization has not been realized yet.
However, with the method using the particulate carrier, a catalyst carrier is unavoidably mixed in a carbon fiber product, and it is difficult to obtain a carbon fiber with high purity.
As a method for reducing the amount of impurities in the carbon fiber obtained by the method using the particulate carrier, (1) a method of heat treatment at a high temperature; and (2) a method of washing and removing with acid or base are known, but both of the methods have complicated processes and are not economical. Particularly, in the washing and removing of the impurities with acid or base, since the catalyst carrier and the catalytic metal in the carbon fiber are covered by a carbon overcoat in many cases, it is difficult to fully remove the impurities unless the carbon overcoat is removed by using an oxidizing acid such as nitric acid or by performing partial oxidization. If an oxidizing acid is used, not only the carbon overcoat on the surface of the carrier or the catalyst but also the carbon fiber itself might be damaged and become defective. The carbon fiber affected by an acid might have lowered electric conductivity or lowered heat conductivity, or dispersibility or filling performance into a resin or the like might be deteriorated.
[PTL 2] Japanese Patent Laid-Open No. 2003-205239
[PTL 3] International Publication No. WO2006/50903
[PTL 4] U.S. Patent No. 6518218
[PTL 5] Japanese Patent Laid-Open No. 2001-80913
As mentioned above, it has been difficult to obtain a carbon fiber which can give high heat conductivity and high electric conductivity when used as filler and contains a low content of impurities with a lower cost.
The present invention has an object to provide a method for efficiently producing a carbon fiber in which generation efficiency (weight gain) of the carbon fiber per catalyst mass is high, temperature dependency of the generation efficiency is low, a data spread in impurity concentration is small, electric conductivity and heat conductivity are high, and filling performance and dispersibility in a resin or the like is excellent.
(1) A method for producing a carbon fiber comprising a step dissolving or dispersing [I] a compound containing Co element; [II] a compound containing at least one element selected from the group consisting of Ti, V, Cr, and Mn; and [III] a compound containing at least one element selected from the group consisting of W and Mo in a solvent to obtain a solution or a fluid dispersion, a step of impregnating a particulate carrier with the solution or the fluid dispersion to prepare a catalyst, and a step of bringing a carbon source into contact with the catalyst in a vapor phase.
(2) The method for producing a carbon fiber described in (1), in which a total amount of the element [I], the element [II], and the element [III] is 1 to 200 % by mass with respect to the particulate carrier.
(3) The method for producing a carbon fiber described in (1) or (2), in which the carrier is alumina, magnesia, titania, silica, calcium carbonate, calcium hydroxide or calcium oxide.
(4) The method for producing a carbon fiber described in any one of (1) to (3), in which a temperature in the step of bringing the carbon source into contact with the catalyst in the vapor phase is 500 degrees cent. to 1000 degrees cent.
(5) The method for producing a carbon fiber described in any one of (1) to (4), further comprising a step of reduction treatment of the catalyst before the step of bringing the carbon source into contact with the catalyst in a vapor phase.
(6) A method for producing a composite material, comprising a step of dissolving or dispersing [I] a compound containing Co element; [II] a compound containing at least one element selected from the group consisting of Ti, V, Cr, and Mn; and [III] a compound containing at least one element selected from the group consisting of W and Mo in a solvent to obtain a solution or a fluid dispersion, a step of impregnating a particulate carrier with the solution or the fluid dispersion to prepare a catalyst, a step of bringing a carbon source into contact with the catalyst in a vapor phase to obtain a carbon fiber, and a step of kneading the carbon fiber and a resin.
The carbon fiber obtained by the producing method in the present invention can be uniformly dispersed when filled in metal, resin, ceramics and the like, high heat conductivity and high electric conductivity can be given, and strength deterioration or the like of a composite material obtained by adding the carbon fiber in the metal, resin, ceramics and the like is not caused. Moreover, the carbon fiber obtained by the producing method in the present invention is suitably used as an electron emitting material for FED (Field Emission Display), as a catalyst carrier for various reactions, moreover as a medium for storing hydrogen, methane or like various gases, or as an electrode material of an electrochemical element such as a battery, a capacitor, a hybrid capacitor and the like.
The element [II] is at least one element selected from the group consisting of Ti, V, Cr, and Mn. In the elements [II], at least one element selected from the group consisting of Ti, V, and Cr is preferable, at least one element selected from the group consisting of Ti and V is more preferable, and V is particularly preferable from the viewpoint of the generation efficiency.
Since Cr includes a plurality of types with different oxidation numbers as divalent, trivalent and hexavalent and Mn includes oxidation numbers as divalent, tetravalent and heptavalent, control of the oxidation number in catalyst preparation is required, and a catalyst preparation process might become complicated, but Cr gives higher generation efficiency when a calcium carbonate carrier is used. Ti is stable with the oxidation number of tetravalent, and the above-mentioned particular control is not needed and the catalyst performance is stable without using a complicated catalyst preparation method.
The element [III] is at least one element selected from the group consisting of W and Mo.
The combination of the catalytic metal elements in the present invention includes Co-Ti-Mo, Co-Mn-Mo, Co-V-Mo, Co-Cr-Mo, Co-Ti-W, Co-V-W, Co-Cr-W, and Co-Mn-W.
The element [III] is preferably 1 to 100 % by mol, more preferably 5 to 50 % by mol, or still more preferably 5 to 20 % by mol with respect to the element [I].
When each compound is selected so that the proportions of the element [I], the element [II] and the element [III] satisfy the above ranges respectively, a carbon fiber with less total metal element content can be likely obtained.
The catalytic metal elements may be supported on the carrier, by impregnating the particulate carrier with a liquid containing all of the compound containing the element [I], the compound containing the element [II], and the compound containing the element [III]; or by impregnating the particulate carrier with a liquid containing the compound containing the element [I], a liquid containing the compound containing the element [II], and a liquid containing the compound containing the element [III] in random order.
For example, there is a method in which the catalyst is set in a vertical-type or horizontal-type reactor heated to a predetermined temperature and the carbon source is fed with a carrier gas into the reactor.
The catalyst may be set in a fixed-bed reactor in which it is placed on a boat (a boat made of quartz, for example) in the reactor or may be set in a fluidized-bed reactor in which it is fluidized by the carrier gas in the reactor. Since the catalyst might be in an oxidized state, the catalyst can be reduced by feeding a gas containing a reducing gas before the carbon source is fed. A temperature at the reduction is preferably 300 to 1000 degrees cent., or more preferably 500 to 700 degrees cent., and a reduction time is preferably 10 minutes to 5 hours, or more preferably 10 to 60 minutes.
A reaction temperature in the vapor phase growth is preferably 500 to 1000 degrees cent., or more preferably 550 to 750 degrees cent. Within this temperature range can easily produce a tube-like carbon fiber with a multilayer structure composed of a portion in which graphite layers are regularly arrayed in a straight line state and a portion in which they are arrayed irregularly.
The metal elements derived from these catalyst carriers may be contained preferably in 0.1 to 20 times, more preferably 0.1 to 10 times, or particularly preferably 0.1 to 5 times, with respect to the total mass of the element [I], the element [II] and the element [III] derived from the catalytic metal. The content of the metal element derived from the carrier in the carbon fiber are preferably 5 % by mass or less, more preferably 3 % by mass or less, still more preferably 2 % by mass or less, or particularly preferably 1 % by mass or less.
The total content of the element [I], the element [II] and the element [III] derived from the catalytic metal is preferably 4.4 % by mass or less, more preferably 2.9 % by mass or less, still more preferably 1.8 % by mass or less, or particularly preferably 0.9 % by mass or less, if the element [II] is Mn. If the element [II] is Ti, V or Cr, the total content of the element [I], the element [II] and the element [III] derived from the catalytic metal is preferably 2.8 % by mass or less, more preferably 1.8 % by mass or less, still more preferably 1.1 % by mass or less, or particularly preferably 0.6 % by mass or less.
The contents of these metal elements in the carbon fiber can be determined by measuring the solution obtained by sulfuric nitric acid - decomposition of the carbon fiber using ICP-AES (Inductively Coupled Plasma - Atomic Emission Spectrometry).
The R value is an intensity ratio ID/IG between peak intensity (ID) in the vicinity of 1360 cm-1 and the peak intensity (IG) in the vicinity of 1580 cm-1 measured by Raman spectroscopic spectrum. The R value was determined under a condition of excitation wavelength of 532 nm using Series 5000 made by Kaiser Optical Systems. Inc. The smaller R value indicates the larger growth level of the graphite layer in the carbon fiber. If the R value satisfies the above range, the heat conductivity and electric conductivity of the resin or the like can be raised when the fiber is added to the resin or the like.
A length of the graphite layer is preferably 0.02 times or more and 15 times or less as long as the fiber diameter. The shorter the length of the graphite layer is, the higher the contact strength between the carbon fiber and the resin becomes when being filled in the resin or the like, and the mechanical strength of a composite of the resin and the carbon fiber becomes higher. The length of the graphite layer and the inclination angle of the graphite layer can be determined by observation using an electronic microscope photographs and the like.
The carbon fiber obtained by the producing method in the present invention is preferably 30 % or more and 90 % or less in a ratio of the number of graphite layers being less than twice as long as the fiber diameter.
Also, the preferred embodiment of the carbon fiber is in a tube state having a hollow at the center part of the fiber. The hollow part may be continuous in the fiber longitudinal direction or may be discontinuous. A ratio (d0 / d) between a fiber diameter d and a hollow inner diameter d0 is not particularly limited but it is preferably 0.1 to 0.8, or more preferably 0.1 to 0.6.
The former carbon fiber with the shell inner layer composed of the crystalline carbon and the shell outer layer composed of the carbon containing the thermal decomposition layer has a higher contact strength between the carbon fiber and the resin when being filled in the resin or the like, and the mechanical strength of the composite of the resin and the carbon fiber becomes higher.
With the carbon fiber with the portion where the graphite layers are arrayed regularly in parallel and the portion where the graphite layers are arrayed irregularly at random, if the layer made up of the irregular carbon atom array is thick, fiber strength might easily become weak, while if the layer made up of the irregular carbon atom array is thin, interface strength with the resin might easily become weak. In order to enhance the fiber strength and the interface strength with the resin, it is preferable that the layer made up of the irregular carbon atom array (irregular graphite layer) is present with an appropriate thickness or that a thick irregular graphite layer and a thin irregular graphite layer are mixed or distributed in a single fiber.
The reason why the carbon fiber obtained by the producing method in the present invention shows excellent dispersibility to the matrix is not known, but it is assumed that the thermal decomposition of the carbon source is appropriately promoted in the vapor phase, and a thermal decomposition layer with an appropriate thickness is formed on the surface of the fiber.
The metal to which the carbon fiber obtained by the producing method in the present invention is added includes gold, silver, aluminum, iron, magnesium, lead, copper, tungsten, titanium, niobium, hafnium as well as their alloys and mixtures.
As the resin to which the carbon fiber obtained by the producing method in the present invention is added, either of thermoplastic resin and thermosetting resin can be employed. For further improvement of impact resistance, a resin in which thermoplastic elastomer or rubber component is added to the above thermoplastic resin can be employed.
Therefore, in order to realize even dispersion while suppressing the fracture of the carbon fiber, kneading with reduced shear with the same-direction twin-screw extruder not using the kneading disk, kneading for a long time with a device such as a pressurized kneader which does not apply high shear or kneading with using a special mixing element in the single-screw extruder is preferable.
(Content of impurities)
The content of impurities was measured using a CCD multi-element simultaneous type ICP emission spectrophotometer (made by Varian Inc.: VISTA-PRO) at high-frequency output of 1200 W and measurement time of 5 seconds.
In a quartz beaker, 0.1g of carbon fiber was precisely weighed and subjected to sulfuric nitric acid decomposition. After cooling, it was measured off in a volume of 50 ml. This solution was diluted as appropriate, and each element was quantified by ICP-AES (Atomic Emission Spectrometer). Mass ratio of the impurities to the mass of the carbon fiber is shown in Table. The "total metal element" in the Table refers to the total of metal elements derived from the catalyst carrier, and the element [I], the element [II] and the element [III] derived from the catalytic metal, the "element [I] + [II] + [III]" in the Table refers to the total of element [I], the element [II], and the element [III] derived from the catalytic metal, and the "carrier" in the Table refers to the amount of the metal element derived from the catalyst carrier.
Using a twin-screw extruder with a screw diameter of 30 mm (Japan Steel Works, Ltd., TEX 30 alfa), 5 parts by mass of the carbon fiber and 95 parts by mass of polycarbonate resin (made by Mitsubishi Engineering Plastics Corporation, Iupilon S3000) were kneaded at a temperature of 270 degrees cent. under a condition of screw rotation number of 80 rpm. Extrusion molding was performed using a dice with three holes of 5 mm phi so as to obtain a rod of 5 mm phi * 150 mm. The surface of the rod was touched by hand, and feeling of irregularity was evaluated.
S : Smooth
C : Coarse
This is represented by a ratio of the mass of the generated carbon fiber to the mass of the used catalyst (mass of carbon fiber / mass of catalyst).
In 0.9 part by mass of methanol, 1.24 parts by mass of cobalt (II) nitrate hexahydrate was added and dissolved, and 0.3 part by mass of nitric acid 70 % solution was added. Then, 0.10 part by mass of titanium (IV) tetra-n- butoxide tetramer was added and dissolved so as to obtain a solution A.
The solution A was dripped and mixed with 1 part by mass of magnesia (made by Ube Material Industries, Ltd.; 500A). After the mixing, it was vacuum-dried at 100 degrees cent. for 4 hours. After the drying, it was crushed in a mortar and pestle so as to obtain a powder A.
In 0.9 part by mass of water, 0.075 part by mass of hexaammonium heptamolybdate tetrahydrate was added and dissolved so as to obtain a solution B.
The solution B was dripped and mixed with the powder A. After the mixing, it was vacuum-dried at 100 degrees cent. for 4 hours. After the drying, it was crushed in a mortar and pestle so as to obtain a catalyst.
The catalyst contained 10 % by mol of Mo and 10 % by mol of Ti with respect to Co, and 25 % by mass of Co was supported on magnesia.
While the temperature of 690 degrees cent. was maintained, the nitrogen gas was switched to a mixed gas A of nitrogen gas (100 parts by volume) and hydrogen gas (400 parts by volume), and the mixed gas A was made to flow through the reactor for 30 minutes to conduct reduction reaction. After the reduction reaction, while the temperature of 690 degrees cent. was maintained, the mixed gas A was switched to a mixed gas B of hydrogen gas (250 parts by volume) and ethylene gas (250 parts by volume), and the mixed gas B was made to flow through the reactor for 60 minutes to conduct vapor phase growth reaction. The mixed gas B was switched to nitrogen gas, the inside of the reactor was replaced by the nitrogen gas, and the temperature was decreased to the room temperature. The reactor was opened, and the quartz boat was taken out. A carbon fiber grown with the catalyst as a core was obtained. The carbon fiber was tubular, and its shell was in a multi-walled structure. The evaluation result of the carbon fiber is shown in Table 1. The relative proportions of the metal elements contained in the carbon fiber were the same as those of the catalyst.
In 0.9 part by mass of methanol, 1.24 parts by mass of cobalt (II) nitrate hexahydrate was added and dissolved, and then 0.3 part by mass of nitric acid 70 % solution was added. Then, 0.050 part by mass of ammonium metavanadate and 0.075 part by mass of hexaammonium heptamolybdate tetrahydrate were added and dissolved so as to obtain a solution.
The solution was dripped and mixed with 1 part by mass of magnesia (made by Ube Material Industries, Ltd.; 500A). After the mixing, it was vacuum-dried at 100 degrees cent. for 4 hours. After the drying, it was crushed in a mortar and pestle so as to obtain a catalyst.
The catalyst contained 10 % by mol of Mo and 10 % by mol of V with respect to Co, and 25 % by mass of Co was supported on magnesia.
Using the catalyst, a carbon fiber was obtained by the same manner as in the Example 1. The carbon fiber was tubular, and its shell was in a multi-walled structure. The evaluation result of the carbon fiber is shown in Table 1. The relative proportions of the metal elements contained in the carbon fiber were the same as those of the catalyst.
In 1.2 parts by mass of water, 1.24 parts by mass of cobalt (II) nitrate hexahydrate was added and dissolved, and then 0.170 part by mass of chromium (III) nitrate nonahydrate and 0.075 part by mass of hexaammonium heptamolybdate tetrahydrate were added and dissolved so as to obtain a solution.
The solution was dripped and mixed with 1 part by mass of magnesia (made by Ube Material Industries, Ltd.; 500A). After the mixing, it was vacuum-dried at 100 degrees cent. for 4 hours. After the drying, it was crushed in a mortar and pestle so as to obtain a catalyst.
The catalyst contained 10 % by mol of Mo and 10 % by mol of Cr with respect to Co, and 25 % by mass of Co was supported on magnesia.
Using the catalyst, a carbon fiber was obtained by the same manner as in the Example 1. The carbon fiber was tubular, and its shell was in a multi-walled structure. The evaluation result of the carbon fiber is shown in Table 1. The relative proportions of the metal elements contained in the carbon fiber were the same as those of the catalyst.
In 1.2 parts by mass of water, 1.24 parts by mass of cobalt (II) nitrate hexahydrate was added and dissolved, and then 0.73 part by mass of manganese (II) nitrate hexahydrate and 0.075 part by mass of hexaammonium heptamolybdate tetrahydrate were added and dissolved so as to obtain a solution.
The solution was dripped and mixed with 1 part by mass of magnesia (made by Ube Material Industries, Ltd.; 500A). After the mixing, it was vacuum-dried at 100 degrees cent. for 4 hours. After the drying, it was crushed in a mortar and pestle so as to obtain a catalyst.
The catalyst contained 10 % by mol of Mo and 60 % by mol of Mn with respect to Co, and 25 % by mass of Co was supported on magnesia.
Using the catalyst, a carbon fiber was obtained by the same manner as in the Example 1. The carbon fiber was tubular, and its shell was in a multi-walled structure. The evaluation result of the carbon fiber is shown in Table 1. The relative proportions of the metal elements contained in the carbon fiber were the same as those of the catalyst.
In 1.2 parts by mass of water, 1.24 parts by mass of cobalt (II) nitrate hexahydrate was added and dissolved, and then 0.075 part by mass of hexaammonium heptamolybdate tetrahydrate was added and dissolved so as to obtain a solution.
The solution was dripped and mixed with 1 part by mass of magnesia (made by Ube Material Industries, Ltd.; 500A). After the mixing, it was vacuum-dried at 100 degrees cent. for 4 hours. After the drying, it was crushed in a mortar and pestle so as to obtain a catalyst.
The catalyst contained 10 % by mol of Mo with respect to Co, and 25 % by mass of Co was supported on magnesia.
Using the catalyst, a carbon fiber was obtained by the same manner as in the Example 1. The evaluation result is shown in Table 1. The relative proportions of the metal elements contained in the carbon fiber were the same as those of the catalyst.
In 0.9 part by mass of methanol, 1.24 parts by mass of cobalt (II) nitrate hexahydrate was added and dissolved, and then 0.3 part by mass of nitric acid 70 % solution was added. Then, 0.10 part by mass of ammonium metatungstate hydrate and 0.10 part by mass of titanium (IV) tetra-n-butoxide tetramer were added and dissolved so as to obtain a solution.
The solution was dripped and mixed with 1 part by mass of magnesia (made by Ube Material Industries, Ltd.; 500A). After the mixing, it was vacuum-dried at 100 degrees cent. for 4 hours. After the drying, it was crushed in a mortar and pestle so as to obtain a catalyst.
The catalyst contained 10 % by mol of Ti and 10 % by mol of W with respect to Co, and 25 % by mass of Co was supported on magnesia.
Using the catalyst, a carbon fiber was obtained by the same manner as in the Example 1. The carbon fiber was tubular, and its shell was in a multi-walled structure. The evaluation result is shown in Table 2. The relative proportions of the metal elements contained in the carbon fiber were the same as those of the catalyst.
In 0.9 part by mass of methanol, 1.24 parts by mass of cobalt (II) nitrate hexahydrate was added and dissolved, and then 0.3 part by mass of nitric acid 70 % solution was added. Then, 0.050 part by mass of ammonium metavanadate and 0.10 part by mass of ammonium metatungstate hydrate were added and dissolved so as to obtain a solution.
The solution was dripped and mixed with 1 part by mass of magnesia (made by Ube Material Industries, Ltd.; 500A). After the mixing, it was vacuum-dried at 100 degrees cent. for 4 hours. After the drying, it was crushed in a mortar and pestle so as to obtain a catalyst.
The catalyst contained 10 % by mol of W and 10 % by mol of V with respect to Co, and 25 % by mass of Co was supported on magnesia.
Using the catalyst, a carbon fiber was obtained by the same manner as in the Example 1. The carbon fiber was tubular, and its shell was in a multi-walled structure. The evaluation result is shown in Table 2. The relative proportions of the metal elements contained in the carbon fiber were the same as those of the catalyst.
In 1.2 parts by mass of water, 1.24 parts by mass of cobalt (II) nitrate hexahydrate was added and dissolved, and then 0.170 part by mass of chromium (III) nitrate nonahydrate and 0.10 part by mass of ammonium metatungstate hydrate were added and dissolved so as to obtain a solution.
The solution was dripped and mixed with 1 part by mass of magnesia (made by Ube Material Industries, Ltd.; 500A). After the mixing, it was vacuum-dried at 100 degrees cent. for 4 hours. After the drying, it was crushed in a mortar and pestle so as to obtain a catalyst.
The catalyst contained 10 % by mol of Cr and 10 % by mol of W with respect to Co, and 25 % by mass of Co was supported on magnesia.
Using the catalyst, a carbon fiber was obtained by the same manner as in the Example 1. The carbon fiber was tubular, and its shell was in a multi-walled structure. The evaluation result is shown in Table 2. The relative proportions of the metal elements contained in the carbon fiber were the same as those of the catalyst.
In 1.2 parts by mass of water, 1.24 parts by mass of cobalt (II) nitrate hexahydrate was added and dissolved, and then 1.46 parts by mass of manganese (II) nitrate hexahydrate and 0.10 part by mass of ammonium metatungstate hydrate were added and dissolved so as to obtain a solution.
The solution was dripped and mixed with 1 part by mass of magnesia (made by Ube Material Industries Ltd.; 500A). After the mixing, it was vacuum-dried at 100 degrees cent. for 4 hours. After the drying, it was crushed in a mortar and pestle so as to obtain a catalyst.
The catalyst contained 120 % by mol of Mn and 10 % by mol of W with respect to Co, and 25 % by mass of Co was supported on magnesia.
Using the catalyst, a carbon fiber was obtained by the same manner as in the Example 1. The carbon fiber was tubular, and its shell was in a multi-walled structure. The evaluation result is shown in Table 2. The relative proportions of the metal elements contained in the carbon fiber were the same as those of the catalyst.
In 1.2 parts by mass of water, 1.24 parts by mass of cobalt (II) nitrate hexahydrate was added and dissolved, and then 0.10 part by mass of ammonium metatungstate hydrate was added and dissolved so as to obtain a solution.
The solution was dripped and mixed with 1 part by mass of magnesia (made by Ube Material Industries Ltd.; 500A). After the mixing, it was vacuum-dried at 100 degrees cent. for 4 hours. After the drying, it was crushed in a mortar and pestle so as to obtain a catalyst.
The catalyst contained 10 % by mol of W with respect to Co, and 25 % by mass of Co was supported on magnesia.
Using the catalyst, a carbon fiber was obtained by the same manner as in the Example 1. The evaluation result is shown in Table 2. The relative proportions of the metal elements contained in the carbon fiber were the same as those of the catalyst.
In 0.9 part by mass of methanol, 1.24 parts by mass of cobalt (II) nitrate hexahydrate was added and dissolved, and then 0.18 part by mass of iron (III) nitrate nonahydrate was added and dissolved so as to obtain a solution. The solution was dripped and mixed with 1 part by mass of magnesia (made by Ube Material Industries Ltd.; 500A). After the mixing, it was vacuum-dried at 100 degrees cent. for 4 hours. After the drying, it was crushed in a mortar and pestle so as to obtain a catalyst. The catalyst contained 10 % by mol of Fe with respect to Co, and 25 % by mass of Co was supported on magnesia.
Using the catalyst, a carbon fiber was obtained by the same manner as in the Example 1. The relative proportions of the metal elements contained in the carbon fiber were the same as those of the catalyst. The weight gain was 7 times. In content of impurities, the amount of total metal element was 11.4 % by mass, the amount of Fe element was 8.6 % by mass, and the amount of Mg element derived from the carrier was 2.9 % by mass.
A catalyst was obtained by the same manner as in the Example 4 except that the cobalt (II) nitrate hexahydrate was not used. Using of the obtained catalyst in vapor phase growth reaction by the same manner as in the Example 4 had almost failed to gain a carbon fiber.
A catalyst was obtained by the same manner as in the Example 7 except that the cobalt (II) nitrate hexahydrate was not used. Using of the obtained catalyst in vapor phase growth reaction by the same manner as in the Example 7 had almost failed to gain a carbon fiber.
Claims (6)
- A method for producing a carbon fiber, comprising steps of :
dissolving or dispersing [I] a compound containing Co element; [II] a compound containing at least one element selected from the group consisting of Ti, V, Cr, and Mn; and [III] a compound containing at least one element selected from the group consisting of W and Mo in a solvent to obtain a solution or a fluid dispersion,
impregnating a particulate carrier with the solution or the fluid dispersion to prepare a catalyst, and
bringing a carbon source into contact with the catalyst in a vapor phase. - The method for producing a carbon fiber according to the claim 1, wherein a total amount of the element [I], the element [II], and the element [III] is 1 to 200 % by mass with respect to the particulate carrier.
- The method for producing a carbon fiber according to the claim 1 or 2, wherein the carrier is alumina, magnesia, titania, silica, calcium carbonate, calcium hydroxide or calcium oxide.
- The method for producing a carbon fiber according to any one of the claims 1 to 3, wherein a temperature in the step of bringing the carbon source into contact with the catalyst in the vapor phase is 500 degrees cent. to 1000 degrees cent.
- The method for producing a carbon fiber according to any one of the claims 1 to 4, further comprising
a step of reduction treatment of the catalyst before the step of bringing the carbon source into contact with the catalyst in a vapor phase. - A method for producing a composite material, comprising steps of:
dissolving or dispersing [I] a compound containing Co element; [II] a compound containing at least one element selected from the group consisting of Ti, V, Cr, and Mn; and [III] a compound containing at least one element selected from the group consisting of W and Mo in a solvent to obtain a solution or a fluid dispersion,
impregnating a particulate carrier with the solution or the fluid dispersion to prepare a catalyst,
bringing a carbon source into contact with the catalyst in a vapor phase to obtain a carbon fiber, and
kneading the carbon fiber and a resin.