WO2009103848A1 - Post formable plywood product and its manufacturing method - Google Patents
Post formable plywood product and its manufacturing method Download PDFInfo
- Publication number
- WO2009103848A1 WO2009103848A1 PCT/FI2009/050131 FI2009050131W WO2009103848A1 WO 2009103848 A1 WO2009103848 A1 WO 2009103848A1 FI 2009050131 W FI2009050131 W FI 2009050131W WO 2009103848 A1 WO2009103848 A1 WO 2009103848A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- polyolefin film
- post
- plywood product
- film
- polyolefin
- Prior art date
Abstract
Description
Claims