WO2009102952A2 - Crosslinked polyalkyleneimine hydrogels with tunable degradation rates - Google Patents
Crosslinked polyalkyleneimine hydrogels with tunable degradation rates Download PDFInfo
- Publication number
- WO2009102952A2 WO2009102952A2 PCT/US2009/034050 US2009034050W WO2009102952A2 WO 2009102952 A2 WO2009102952 A2 WO 2009102952A2 US 2009034050 W US2009034050 W US 2009034050W WO 2009102952 A2 WO2009102952 A2 WO 2009102952A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- polyalkylene glycol
- crosslinking agent
- polymeric composition
- glycol diacid
- wound
- Prior art date
Abstract
Description
Claims