WO2009099937A1 - Catalysts, systems and methods utilizing non-zeolitic metal-containing molecular sieves having the cha crystal structure - Google Patents
Catalysts, systems and methods utilizing non-zeolitic metal-containing molecular sieves having the cha crystal structure Download PDFInfo
- Publication number
- WO2009099937A1 WO2009099937A1 PCT/US2009/032610 US2009032610W WO2009099937A1 WO 2009099937 A1 WO2009099937 A1 WO 2009099937A1 US 2009032610 W US2009032610 W US 2009032610W WO 2009099937 A1 WO2009099937 A1 WO 2009099937A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- catalyst
- sapo
- nox
- metal
- hours
- Prior art date
Abstract
Description
Claims