WO2009093081A1

WO2009093081A1 - Fuel cells

Info

Publication number: WO2009093081A1
Application number: PCT/GB2009/050066
Authority: WO
Inventors: Kathryn Knuckey; David Rochester
Original assignee: Acal Energy Limited
Priority date: 2008-01-23
Filing date: 2009-01-23
Publication date: 2009-07-30
Also published as: EP2238642B1; JP2011510465A; GB0801195D0; JP5468017B2; US20110027671A1; EP2238642A1

Abstract

A redox fuel cell comprising an anode and a cathode separated by an ion selective polymer electrolyte membrane; means for supplying a fuel to the anode region of the cell; means for supplying an oxidant to the cathode region of the cell; means for providing an electrical circuit between the anode and the cathode; a catholyte solution comprising a modified ferrocene species comprising at least one bridging unit between the cyclopentadienyl rings, the modified ferrocene species being at least partially reduced at the cathode in operation of the cell, and at least partially re-generated by reaction with the oxidant after such reduction at the cathode.

Description

FUEL CELLS

The present invention relates to fuel cells, in particular to indirect or redox fuel cells which have applications as power sources for: portable products such as portable electronics products; for transport vehicles such as automobiles, both main and auxiliary; auxiliary power for caravans and other recreational vehicles, boats etc; stationary uses such as uninterruptible power for hospitals computers etc and combined heat and power for homes and businesses. The invention also relates to certain catholyte solutions for use in such fuel cells.

Fuel cells have been known for portable applications such as automotive and portable electronics technology for very many years, although it is only in recent years that fuel cells have become of serious practical consideration. In its simplest form, a fuel cell is an electrochemical energy conversion device that converts fuel and oxidant into reaction product(s), producing electricity and heat in the process. In one example of such a cell, hydrogen is used as fuel, and air or oxygen as oxidant and the product of the reaction is water. The gases are fed respectively into catalysing, diffusion-type electrodes separated by a solid or liquid electrolyte which carries electrically charged particles between the two electrodes. In an indirect or redox fuel cell, the oxidant (and/or fuel in some cases) is not reacted directly at the electrode but instead reacts with the reduced form (oxidized form for fuel) of a redox couple to oxidise it, and this oxidised species is fed to the cathode (anode for fuel) There are several types of fuel cell characterised by their different electrolytes. The liquid electrolyte alkali electrolyte fuel cells have inherent disadvantages in that the electrolyte dissolves CO₂ and needs to be replaced periodically. Polymer electrolyte or PEM-type cells with proton-conducting solid cell membranes are acidic and avoid this problem. However, it has proved difficult in practice to attain power outputs from such systems approaching the theoretical maximum level, due to the relatively poor electrocatalysis of the oxygen reduction reaction.

In addition expensive noble metal electrocatalysts are often used. It would be preferable to use a less costly inert electrode, such as one formed of or coated with carbon, nickel or titanium. However, prior art cells in which inert electrodes have been utilised have produced unsatisfactory power output.

Many current fuel cell technologies employ cathodes where oxygen gas is flowed directly to the electrode where it then reacts with a catalyst to produce water. In many cases the catalyst employed is platinum, a precious metal. Not only does this increase the costs of the overall fuel cell, but the inefficiency of the reaction leads to a loss in available power.

US-A-3152013 discloses a gaseous fuel cell comprising a cation-selective permeable membrane, a gas permeable catalytic electrode and a second electrode, with the membrane being positioned between the electrodes and in electrical contact only with the gas permeable electrode. The electrodes are formed of platinum, iridium or other noble metal eiectrocatalysts. An aqueous catholyte is provided in contact with the second electrode and the membrane, the catholyte including an oxidant couple therein. Means are provided for supplying a fuel gas to the permeable electrode, and for supplying a gaseous oxidant to the catholyte for oxidising reduced oxidant material. The preferred catholyte and redox couple is HBr/KBr/Br2. Nitrogen oxide is disclosed as a preferred catalyst for oxygen reduction, but with the consequence that pure oxygen was required as oxidant, the use of air as oxidant requiring the venting of noxious nitrogen oxide species.

An acknowledged problem concerning electrochemical fuel cells is that the theoretical potential of a given electrode reaction under defined conditions can be calculated but never completely attained. Imperfections in the system inevitably result in a loss of potential to some level below the theoretical potential attainable from any given reaction. Previous attempts to reduce such imperfections include the selection of mediators which undergo oxidation-reduction reactions in the catholyte solution. For example, US-A- 3294588 discloses the use of quinones and dyes in this capacity. However, despite the electrodes being coated with platinum, relatively low output was obtained during running of the cell. Another redox couple which has been tried is the vanadate/vanadyl couple, as disclosed in US-A-3279949. In this case, the slow rate of reduction and oxidation of the vanadium couple reduces its performance. This problem is exacerbated by the insolubility of the vanadium couple. The same vanadium couple was used in US4396687. According to US-A-3540933, certain advantages could be realised in electrochemical fuel cells by using the same electrolyte solution for both catholyte and anolyte. This document discloses the use of a liquid electrolyte containing more than two redox couples therein, with equilibrium potentials not more than 0.8V apart from any other redox couple in the electrolyte.

The matching of the redox potentials of different redox couples in the electrolyte solution is also considered in US-A-3360401 , which concerns the use of an intermediate electron transfer species to increase the rate of flow of electrical energy from a fuel cell. The use of platinum coated electrodes is also disclosed.

US 3607420 discloses an electrolyte in which the only soluble redox species present is the catalyst species. The electrolyte comprises a Cu^(l)/Cu^(ll) catalyst.

WO-A-2006/057387 discloses a bio fuel cell making use of a material which participates in the donation and receiving of electrons, the cell being said to exhibit an enhanced output power density. The material comprises an electron conductor of a specified external surface area, a redox polymer and a bio catalyst.

US-A-2003/0152823 discloses a fuel cell having an anode and a cathode with an anode enzyme disposed on the anode and a cathode enzyme disposed on the cathode. US-A-2001/0028977 discloses a method for preparing a high energy density electrolyte solution for use in ore-vanadium redox cells.

Prior art fuel cells all suffer from one or more of the following disadvantages:

They are inefficient; they are expensive and/or expensive to assemble; they use expensive and/or environmentally unfriendly materials; they yield inadequate and/or insufficiently maintainable current densities and/or cell potentials; they are too large in their construction; they operate at too high a temperature; they produce unwanted by-products and/or pollutants and/or noxious materials; they have not found practical, commercial utility in portable applications such as automotive and portable electronics.

it is an object of the present invention to overcome or ameliorate one or more of the aforesaid disadvantages. It is a further object of the present invention to provide an improved catholyte solution for use in redox fuel cells.

PCT/GB2007/050420 describes the use of modified ferrocene species as effective mediators in PEM fuel cells. Ferrocene itself is not ideally suited to this purpose as it is uncharged, insufficiently soluble and the Fe(III) form has a positive charge which makes it unsuitable for use in PEM fuel ceϋs employing a cation exchange membrane. PCT/GB2007/050420 describes the chemical modification of ferrocene to improve its solubility and allow the charge of the species to be manipulated. If the ferrocene species is to be used in a catholyte in a PEM fuel cell comprising a cation exchange membrane, it will preferably be non-ionic in its oxidised form, or more preferably anionic. PCT/GB2007/050420 discloses that anionic charge can be introduced by modifying ferrocene with anionic charge inducing groups such as carboxylate, phosphate or phosphonate groups. Stronger acid groups such as sulphonate and sulphate can also be introduced.

Alternatively, when the modified ferrocene species is to be used as a catholyte in a PEM cell comprising a anion exchange membrane, it will preferably be non-ionic in its reduced form, or more preferably, cationic. PCT/GB2007/050420 discloses that cationic charge can be introduced to ferrocene by modifying it with cationic charge inducing groups such as protonated amines or quaternary amine groups.

It would however be desirable to extend the lifetime of the oxidised form of some ferrocene-based mediators. This would increase the stability and lifetime of the ferrocene species in the catholyte and the number of times it can be repeatedly oxidised and reduced without having to be replaced.

Accordingly, the present invention provides a redox fuel cell comprising an anode and a cathode separated by a ion selective polymer electrolyte membrane; means for supplying a fuel to the anode region of the cell; means for supplying an oxidant to the cathode region of the cell; means for providing an electrical circuit between the anode and the cathode; a catholyte solution comprising at least one non-volatile catholyte component flowing in fluid communication with the cathode, the catholyte solution comprising a modified ferrocene species comprising at least one bridging unit between the cyclopentadienyl rings, the modified ferrocene species being at least partially reduced at the cathode in operation of the cell, and at least partially regenerated by reaction with the oxidant after such reduction at the cathode by direct reaction with the oxidant, or by indirect reaction therewith using a redox catalyst catalysing the regeneration of the ferrocene mediator.

The use of modified ferrocenes with bridging units between the cyclopentadienyl rings can provide access to mediators with increased stability. The ferrocene bridging unit increases the likelihood of reversible redox behaviour over alternative reaction pathways,

Furthermore, the bridging unit provides extra sites for the incorporation of functional groups which can tailor potential, aid solubility and/or manipulate the overall charge on the complex.

In one preferred form of fuel cell in accordance with the invention, the modified ferrocene species may be represented by the formula:

wherein:

A-(B)_n-C together comprise a divalent heteroannular bridging group; and n is from 1 to 6.

The divalent heteroannular bridging group may be selected for example from C1-C20 alkylidene, C3-C20 cycloalkylidene, Ce-C₂O arylidene, C₇-C_2O alkylarylidene, C₂-C₂O alkenylidene, optionally containing one or more heteroatoms. Heteroatoms when present may be selected from oxygen, nitrogen, phosphorus and sulphur, for example.

A, B¹ - B⁶ and C are independently selected from carbon, sulphur, oxygen, nitrogen and phosphorus and from functional groups comprising those atoms;

The number of bridging units (A-(B)_n-C) between the cyclopentadienyl rings can be between 1 and 5. In each case n can be between 1 and 6. Preferably the number of bridging units should be 1-3, more preferably 2-3. Each bridging unit (A-(B)_n-C) may be the same or different.

Preferably n will be 1-3, more preferably 1-2.

Identity of the atoms A, B, and C, and further progressions of atoms which may be labelled as B¹, B², B³...etc. may or may not be carbon, sulphur, oxygen, nitrogen, phosphorous and functional groups comprising these atoms The identity of the atoms A, B¹, B², B³, B⁴, B⁵, B⁶ and C may or may not be identical but never mutually exclusive

The or each bridging unit A-(B)_n-C may be the same or different, and -A-, -B¹- , -B²-, -B³-, -B⁴-, -B⁵-, -B⁶- and -C- are preferably independently selected from compatible combinations of substituted and unsubstituted, branched- and straight-chain -(CH₂)-, -CH(alkyl)-, -C(alkyl)₂-, -CH(alkenyl)-, -C(alkenyl)₂-

, -CH(alkynyl)-, -C(alkynyl)₂-, CH(aryl), CH(heteroaryl), -O-, -S-, -(NH)-, -

N(alkyl)-, -CH(OH)-, -CH(O-alkyl)-, -C(=O)-, -C-O-C(=O)- or -O-C(=O)-O- C(=O)-O-

The ferrocene bridging units A, B, and C, may carry further substituent groups which are independently selected from hydrogen and from functional groups comprising halogen, hydroxy, amino, protonated amino, imino, nitro, cyano, acyl, acyloxy, sulphate, sulphonyl, sulphinyl, alkylamino, protonated alkylamino, quaternary alkylammonium, carboxy, carboxylic acsd, ester, ether, amido, sulphonate, sulphonic acid, sulphonamide, phosphonic acid, phosphonate, phosphate, alkylsulphonyl, arylsulphonyi, alkoxycarbonyl, alkylsulphinyl, alkylthio, arylthio, alkyl, alkoxy, oxyester, oxyamido, aryl, arylamino, aryloxy, heterocycloalkyl, heteroaryl, (C2-C5)alkenyl (C2- C5)alkynyl, azido, phenylsulphonyloxy o amino acid conjugates having the formula -CO-W-OH, where W is an amino acid , and from alkyl, alkenyi, aryl, cycloalkyl, alkaryl, aikenaryi, aralkyl, aralkenyl groups substituted with one ore more of the aforesaid functional groups Especially preferred substituents include fluoro, hydroxy, amino, protonated amino, nitro, alkylamino, protonated alkylamino, quaternary alkyiammonium, carboxylic acid, sulphonate, sulphonic acid, phosphonic acid, phosphonate, and from alkyl, alkenyl, aryl, cycloalkyl, alkaryl, alkenaryl, aralkyl, aralkenyl groups substituted with one or more of the aforesaid functional groups.

The or each bridging unit may be further branched and/or extended at any bridging atom on any bridge by any suitable number of spacer and/or functional groups, for example, alkyl, alkenyl, aryl, heteroaryl, cycloalkyl, alkaryl, alkenaryl, acetylene, etc. The spacer group may also be a straight or branched and a combination of the aforesaid units.

Each bridging unit A, Bⁿ and C may bear any number of substituents and in each case these substituents may be the same of different.

Any ferrocene sites without heteroannular bridging units attached may be independently substituted with hydrogen or with functional groups comprising halogen, hydroxy, amino, imino, nitro, cyano, acyl, acyioxy, sulphate, sulphonyl, sulphinyl, alkylamino, carboxy, carboxylic acid, ester, ether, amido, sulphonate, sulphonic acid, sulphonamide, phosphonic acid, phosphonate, phosphonic acid, phosphate, alkylsulphonyl, arylsulphonyl, alkoxycarbonyl, alkylsulphinyf, arylsulphinyl, aikylthio, arylthio, alkyl, alkoxy_s oxyester, Gxyamϊdo, aryl, aryiamino, aryloxy, heterocycloalkyl, heteroaryl, (C-₂- C₅)alkenyl_! (C₂-C₅)alkynyl, azido phenylsulphonyloxy or amino acid conjugates having the formula -CO-W-OH, where W is an amino acid, and

- io - from alkyi, alkenyl, aryl, cycloalkyl, alkaryl alkenaryl, aralkyl, aralkenyl groups substituted with one or more of the aforesaid functional groups.

Especially preferred substituents include fluoro, hydroxy, amino, protonated amino, nitro, alkylamino, protonated alkylamino, quaternary alkylammonium, carboxylic acid, sulphonate, sulphonic acid, phosphonic acid, phosphonate, and from alkyl, alkenyl, aryl, cycloalkyl, alkaryl, alkenaryl, aralkyl, aralkenyl groups substituted with one or more of the aforesaid functional groups.

Examples of such modified ferrocene species for use in the fuel cell of the invention include:

Thus, it can be seen that it is possible to introduce one or more divalent heteroannular bridging units to increase the stability of ferrocene mediator species. Additionally, the charge carried on the modified ferrocene species of the present invention can be easily modified to allow the ferrocene properties to be tailored to the particular conditions of the cell with which it is to be used. For example, it can be tailored to the pH of the catholyte, and the charge of the exchangeable ions in the membrane. Furthermore, the introduction of

- i ? - either electron donating substituents or electron withdrawing substituents to either the cyclopentadienyl rings or the bridge itself can be used to tailor the redox potential of the ferrocene species.

Also provided in accordance with the invention is a catholyte solution for use in such a redox fuel cell.

The concentration of the modified ferrocene species in the catholyte solution is preferably at least about 0,0001 M, more preferably at least about 0.005M, and most preferably at least about 0.001 M.

In one preferred embodiment of the invention, the ion selective PEM is a cation selective membrane which is selective in favour of protons versus other cations. In cases where the PEM is a cation selective membrane, the pH of the catholyte is preferably below 7, more preferably below 4, even more preferably below 2 and most preferably below 1.

The cation selective polymer electrolyte membrane may be formed from any suitable material, but preferably comprises a polymeric substrate having cation exchange capability. Suitable examples include fluororesin-type ion exchange resins and non-fluororesin-type ion exchange resins. Fluororesin- type ion exchange resins include perfluorocarboxylic acid resins, perfluorosulphonic acid resins, and the like. Perfluorocarboxylic acid resins are preferred, for example "Nafion" (Du Pont Inc.), "Flemion" (Asahi Gas Ltd),"Aciplex" (Asahi Kasei !nc), and the like. Non-fluororesin-type ion exchange resins include polyvinyl alcohols, polyalkylene oxides, styrene- divinylbenzene ion exchange resins, and the like, and metal salts thereof. Preferred non-fluororesin-type ion exchange resins include polyalkylene oxide-alkali metal salt complexes. These are obtainable by polymerizing an ethylene oxide oligomer in the presence of lithium chlorate or another alkali metal salt, for example. Other examples include phenolsulphonic acid, polystyrene sulphonic, polytriflurostyrene sulphonic, sulphonated trifluorostyrene, sulphonated copolymers based on α,β,β-triflurostyrene monomer, radiation-grafted membranes. Non-fluorinated membranes include sulphonated poly(phenylquinoxalines), poly (2,6 diphenyl-4-phenylene oxide), poly(arylether sulphone), poly(2,6-diphenylenol); acid-doped polybenzimidazole, sulphonated polyimides; styrene/ethylene- butadiene/styrene triblock copolymers; partially sulphonated polyarylene ether sulphone; partially sulphonated polyether ether ketone (PEEK); and polybenzyl suphonic acid siloxane (PBSS).

In embodiments in which the polymer electrode membrane is anion specific, it is preferred that the catholyte solution have a pH of above 7. In a more preferred embodiment, the catholyte has a pH of above 8.

In some cases it may be desirable for the ion selective polymer electrolyte membrane to comprise a bi-membrane. The bimembrane if present will generally comprise a first cation selective membrane and a second anion selective membrane. Sn this case the bimembrane may comprise an adjacent pairing of oppositely charge selective membranes. For example the bi- membrane may comprise at least two discreet membranes which may be placed side-by-side with an optional gap therebetween. Preferably the size of the gap, if any, is kept to a minimum in the redox cell of the invention. The use of a bi-membrane may be used in the redox fuel cell of the invention to maximise the potential of the cell, by maintaining the potential due to a pH drop between the anode and catholyte solution. Without being limited by theory, in order for this potential to be maintained in the membrane system, at some point in the system, protons must be the dominant charge transfer vehicle. A single cation-selective membrane may not achieve this to the same extent due to the free movement of other cations from the catholyte solution in the membrane.

In this case the cation selective membrane may be positioned on the cathode side of the bimembrane and the anion selective membrane may be positioned on the anode side of the bimembrane. In this case, the cation selective membrane is adapted to allow protons to pass through the membrane from the anode side to the cathode side thereof in operation of the cell. The anion selective membrane is adapted substantially to prevent cationic materials other than protons from passing therethrough from the cathode side to the anode side thereof. In this case protons may pass from anode to cathode.

In a second embodiment of the invention the cation selective membrane is positioned on the anode side of the bimembrane and the anion selective membrane is positioned on the cathode side of the bi-membrane. In this case, the cation selective membrane is adapted to allow protons to pass

- is - through the membrane from the anode side to the cathode side thereof in operation of the cell. In this case, anions can pass from the cathode side into the interstitial space of the bimembrane, and protons will pass from the anode side. It may be desirable in this case to provide means for flushing such protons and anionic materials from the interstitial space of the bimembrane. Such means may comprises one or more perforations in the cation selective membrane, allowing such flushing directly through the membrane. Alternatively means may be provided for channelling flushed materials around the cation selective membrane from the interstitial space to the cathode side of the said membrane.

A representative example of a useful bipolar membrane, the arrangement used with the anionic-selective membrane on the anode side is that sold under the trademark Neosepta(R) BP-1 , available from Tokuyama Corporation.

According to another aspect of the present invention, there is provided a method of operating a ion exchange membrane fuel cell comprising the steps of: a) forming H⁺ ions at an anode situated adjacent to an ion exchange membrane; b) supplying the catholyte of the invention with its modified ferrocene species in an oxidised state to a cathode situated oppositely adjacent to the ion exchange membrane; and c) allowing the modified ferrocene species to become reduced upon contact with the cathode concomitantly with H⁺ ions passing through the membrane to balance charge.

In another embodiment, the catholyte is supplied from a catholyte reservoir.

The method of the above aspect may additionally comprise the step of: d) passing the catholyte from the cathode to a reoxidation zone wherein the modified ferrocene species is reoxidised by the catalyst reacting with the oxidant.

In another embodiment, the method of the above aspect comprises the step of: e) passing the catholyte from the reoxidation zone to the catholyte reservoir.

In this embodiment, the cell is cyclic and the modified ferrocene species in the cathode can be repeatedly oxidised and reduced without having to be replaced.

An electricity loading device configured to load an electric power may also be provided in association with the fuel cell of the invention.

The fuel cell of the invention may comprise a reformer configured to convert available fuel precursor such as LPG, LNG, gasoline or low molecular weight alcohols into a fuel gas (e.g. hydrogen) through a steam reforming reaction. The cell may then comprise a fuel gas supply device configured to supply the reformed fuel gas to the anode chamber.

Preferred fuels include hydrogen; metal hydrides, for example borohydride which may act as a fuel itself or as a provider of hydrogen, low molecular weight alcohols, aldehydes and carboxylic acids, sugars and biofuels as well as LPG, LNG or gasoline.

Preferred oxidants include air, oxygen and peroxides

The anode in the redox fuel cell of the invention may for example be a hydrogen gas anode or a direct methanol anode; other low molecular weight alcohols such as ethanol, propanol, dipropylene glycol; ethylene glycol; also aldehydes formed from these and acid species such as formic acid, ethanoic acid etc. In addition the anode may be formed from a bio-fuel cell type system where a bacterial species consumes a fuel and either produces a mediator which is oxidized at the electrode, or the bacteria themselves are adsorbed at the electrode and directly donate electrons to the anode.

The cathode in the redox fuel cell of the invention may comprise as cathodic material carbon, gold, platinum, nickel, metal oxide species. However, as a result of the advantageous cathoiytβ of the present invention, the use of such cathodes is not necessary to achieve satisfactory power output. Thus, the preferred cathodic materials include carbon, nickel, titanium and other metals

- is - inert in the specific catholyte and metal oxide or sulphide. One preferable material for the cathodes is reticulated vitreous carbon or carbon fibre based electrodes such as carbon felt. Another is nickel foam or mesh, or titanium foam or mesh. The cathodic material may be constructed from a fine dispersion of particulate cathodic material, the particulate dispersion being held together by a suitable adhesive, or by a proton conducting polymeric material. The cathode is designed to create maximum flow of catholyte solution to the cathode surface. Thus it may consist of shaped flow regulators or a three dimensional electrode; the liquid flow may be managed in a flow-by arrangement where there is a liquid channel adjacent to the electrode, or in the case of the three dimensional electrode, where the liquid is forced to flow through the electrode. It is intended that the surface of the electrode is also the electrocatalyst, but it may be beneficial to adhere the electrocatalyst in the form of deposited particles on the surface of the electrode.

The modified ferrocene species flowing in solution in the cathode chamber in operation of the cell is used in the invention as a mediator which acts as an electron sink for electrons formed during the fuel cell reaction. Following this reduction of the mediator, it is reoxidised by the catalyst reacting with the oxidant.

The modified ferrocene species, and any catalyst redox couple, utilised in the fuel cell of the invention should be non-volatile, and be preferably soluble in aqueous solvent. Preferred catalyst couple species should react with the oxidant at a rate effective to generate a useful current in the electrical circuit of the fuel cell, and react with the oxidant such that water is the ultimate end product of the reaction.

The fuel cell of the invention requires the presence of at least about 0.0001 M of a modified ferrocene species in the catholyte solution. However, catalyst redox couples should be included in the catholyte solution in addition to the modified ferrocene species. There are many suitable examples of such catalyst redox couples, including ligated transition metal complexes and polyoxometallate species. Specific examples of polyoxometallate catalyst species which are useful in the fuel cell of the present invention are disclosed in the co-pending UK patent application, GB 0605878.8. Specific examples of suitable transition metals ions which can form such complexes include manganese (Il - V), iron (I - IV), copper (I - III), cobalt (I - III), nickel (I - III), chromium (Il - VII), titanium (Il - IV), tungsten (IV - Vl), vanadium (Il - V) and molybdenum (Il - Vl). Ligands for ligated transition metal complexes can contain carbon, hydrogen, oxygen, nitrogen, sulphur, halides and/or phosphorus.

Alternative catalysts which may be useful in the present invention are complexes of multidentate N-donor ligands. Such ligands are described in PCT/GB2007/050421 and in our co-pending applications GB (P509433GB and P509434GB) filed 23 January 2008., and may be coordinated with any suitable metal or metals, for example transition metals. Examples of such N- donor iigands can be selected from N4Py and derivatives thereof, pydien or derivatives thereof, and trilen and tpen and derivatives thereof. Iron complexes of these example N-donors are found to be effective catalysts for the oxidation of redox mediators in fuel cell systems.

Various aspects of the present invention will now be more particularly described with reference to the following figure which illustrate embodiments of the present invention:

Figure 1 illustrates a schematic view of the cathode compartment of a fuel cell in accordance with the present invention. Figure 2 shows a reaction scheme for the synthesis of a selection of bridged ferrocene species of the present invention.

Figure 3 shows a cyclic voltammogram of the bridged ferrocene species

1 '-3,3'-[3₂]-ferrocenophane-4,5'-disulfonic acid.

Figure 4 shows a UV-Vis spectrum of 1 ,1'-bis(sulphonato)-ferrocene diammonium salt.

Figure 5 shows a UV-Vis spectrum of I'-S.S'-ISaj-ferrocenophane^.S'- disulfonic acid.

Figure 6 shows a polarization curve of a catholyte solution in accordance with the present invention.

Referring to Fig. 1 , there is shown the cathode side of fuel cell 1 in accordance with the invention comprising a polymer electrolyte membrane 2 separating an anode (not shown) from cathode 3. Cathode 3 comprises in this diagram reticulated carbon and is therefore porous. Polymer electrolyte membrane 2 comprises cation selective Nafion 112 membrane through which protons generated by the (optionally catalytic) oxidation of fuel gas (in this case hydrogen) in the anode chamber pass in operation of the cell. Electrons 11 generated at the anode by the oxidation of fuel gas flow in an electrical circuit (not shown) and are returned to cathode 3. Fuel gas (in this case hydrogen) is supplied to the fuel gas passage of the anode chamber (not shown), while the oxidant (in this case air) is supplied to oxidant inlet 4 of cathode gas reaction chamber 5, Cathode gas reaction chamber 5 (the catalyst reoxidation zone) is provided with exhaust 6, through which the byproducts of the fuel cell reaction (eg water and heat) can be discharged.

A catholyte solution comprising a catalyst and the oxidised form of the modified ferrocene species is supplied in operation of the cell from catholyte reservoir 7 into the cathode inlet channel 8. The catholyte passes into reticulated carbon cathode 3, which is situated adjacent membrane 2. As the catholyte passes through cathode 3, the modified ferrocene species and catalyst are reduced and are then returned to cathode gas reaction chamber 5 via cathode outlet channel 9.

Due to the advantageous composition of the catholyte of the present invention, reoxidation of the modified ferrocene species and the catalyst occurs very rapidly, which allows the fuel cell to produce a higher sustainable current than with catholytes of the prior art.

The following non-limiting examples describe the synthesis of a selection of bridged ferrocenes.

. ^o . Example 1

General Synthesis of [3_n]-Ferrocenophanes

p_roce^_{ure re}p_Ortecj by j Q Turbitt and W. E. Watts in J. Organomet. Chem. 1972, 46, 109.

(a) Synthesis of [3_n]-ferrocenophan-1-ones

Ferrocene derivative (1 equiv.) was dissolved in anhydrous DCM and cooled to -78°C. Once at temperature the mixture was treated with AiCb (1 equiv.) in small additions. Acryloyl chloride (1 equiv.) was dissolved in anhydrous DCM and added dropwise to the ferrocene mixture over 1 hr, maintaining the temperature at -78°C. The mixture was stirred at this temperature for a further 4-6 hrs before being quenched with ice-water, before being treated with TiCI₃ (12% in HCI) and extracted with DCM. The organic extracts were combined, dried over MgSO₄, filtered and the solvent removed in vacuo yielding a dark solid. Purification was performed on silica gel, elution with ligroin recovers starting material, whilst elution with ligroin/EtaO (3/1 v/v) recovers the ferrocene-ketone product.

(b) Reduction of [3_n]-ferrocenophan-1-ones to form [3_n]-ferrocenophanes

LiAIH₄ (2 equiv.) under nitrogen was suspended in anhydrous Et₂O and cooled to O⁰C before AICI₃ (2 equiv.) was added stepwise, maintaining the temperature. The mixture was then treated dropwise with ferrocenophan-1- one derivative (1 equiv.) dissolved in anhydrous DCM. The mixture was stirred at room temperature until consumption of the starting material was confirmed by tic, typically 30-60 mins. The mixture was slowly quenched with ice water and filtered through celite to remove inorganic residues, before the product was extracted with Et₂θ. The organic layers were combined, dried over MgSO₄, filtered and the solvent removed in vacuo typically yielding a bright yellow solid. If necessary the product was purified on silica gel eluted with ligroin.

Example 2

General Procedure for the Sulfonation of [3_n]-Ferrocenophanes

Synthetic protocol based on previously reported synthetic procedures in J.

Am. Chem. Soc, 1958, 692.

The ferrocene derivative (1 equiv.) was suspended in acetic anhydride and treated dropwise with chlorosulfonic acid (2.1 equiv.). Addition of the chlorosulfonic acid causes an elevation of reaction temperature to around 40⁰C, The mixture was allowed to stir at RT, for a minimum of overnight, visibly changing colour to a dark green slurry. The mixture was quenched over ice before being neutralized with NaOH and the aqueous solution washed with Et₂O until the washings were colourless. The mixture was acidified with H₂SO₄ until all sodium acetate had been consumed forming acetic acid, ca. pH 3. Any solids were removed by filtration and discarded. The product was extracted into CH₃CN (sodium sulfate in solution creates a biphasic layer with acetonitrile and water which are usually miscible). The solvent was removed in vacuo yielding a dark yellow solid. Treatment with Ba(OH)₂ followed by passing through celite and a cation exchange column can be performed to remove traces of sodium sulfate.

Example 3 Synthesis of [3i]-Ferrocenophan-1-one, 1

Following the general procedure in Example 1(a) and referring to Fig. 2. Ferrocene (20O g, 1.05 moles) in DCM (4 L), treated with AICI₃ (144 g, 1.06 moles) and arcyloyl chloride (100 g, 1.06 moles) yielded 1 (138 g, 55%) as a red/orange solid. ¹H NMR (200 MHz, CDCI₃): δ 4.90 (2H, broad, H²- Cp¹), 4.65 (2H, broad, H²-Cp²), 4.40 (2H, boad, H²-Cp 1), 4.05 (2H, broad, H³- Cp²), 3.00 (4H, broad, -CH₂-α, y). MSES⁺: m/z 240.0 [M]⁺.

Example 4

Synthesis of [3i]-Ferrocenophane, 2 Following the general procedure in Example 1(b) and referring to Fig. 2.

1 (150 g, 0.56 moles) treated with AICI₃ (110 g, 0.81 moles) and LiAIH₄ (32 g, 0.83 motes) in Et₂O (2 L) yielded 2 (125 g, 98%). ¹H NMR (500 MHz₁ CDCI₃): δ 3.90 (4H, d, H³-Cp), 3.85 (4H, d, H²-Cp), 1.90 (2H, m, β-CH₂), 1.80 (4H, m, α/γ-CH₂). MSES⁺: m/z 226.1 [M]⁺.

Example 5

Synthesis of [3i]-Ferrocenophane Disulfonic Acid, 3

Following the general procedure in Example 2 and referring to Fig. 2.

2 (1.75 g, 7.7 mmoi) treated with chlorosulfonic acid (1.1 mL, 16.5 mmol) in acetic anhydride (35 mL) yielded a crude mixture of multiple α/α'-α/β'-efc- isomers. Similar results have been previously reported in J. Am. Chem, Soc, 1957, 79, 2748.

Example 6 5 Synthesis of i.i'-PiJ-Ferrocenophane-S.S'-trimethyl-i-one, 4

Following the general procedure in Example 1(a) and referring to Fig. 2. 2 (200 g, 0.88 moles) in DCM (4 L) was treated with AICI₃ (120 g, 0.88 motes) and acryloyl chloride (98 g, 1.04 moles) recovered 2 (50%) as well as yielding 4 (100 g, 40%) as an orange oily solid. ¹H NMR (500 MHz, CDCI₃): δ 4.85 io (1 H, s, H²-Cp¹), 4.60 (1 H, s, H²-Cp²), 4.55 (1 H, d, H⁵-Cp¹), 4.45 (1 H, d, H⁴- Cp¹), 4.20 (1 H, d, H⁵-Cp²), 3.75 (1 H, d, H⁴-Cp²), 3.20 - 1.60 (10H, multiple signals, H-alkyl). R f = 0.4 (silica gel; Et₂O/ligoin, 1/1 , v/v). MSES⁺: m/z 303.0 [M + Na]⁺; 335.0 [M + Na + MeOH]⁺; 582.7 [2M + Na]⁺. R_f = 0.16 (silica gel; ligroin/Et₂O 75/25).

15

Example 7

Synthesis of 1,1'-3,3'-[3₂]-Ferrocenophane, 5

Following the general procedure in Example 1(b) and referring to Fig. 2. 4 (2.5 g, 9.0 mmol) in anhydrous Et₂O (20O mL) treated with AICI₃ (1.2 g, 20 9.0 mmol) and LiAIH₄ (350 mg, 9.0 mmol) yielding 5 a yellow/orange solid (2.4 g, 99%). ¹H NMR (500 MHz, CDCI₃): δ 3.90 (4H, s, H⁴-Cp, H⁵-Cp), 3.80 (2H₁ s, H²-Cp), 2.00 (4H₁ broad, CH₂-β), 1.70 (8H, broad, CH₂-αγ). R_f = 0.9 (silica gel; Et₂G/ligoin, 1/1 , v/v). MSES⁺: m/z 266.1 [M]⁺.

^ r Example 8 Synthesis of 1,1^*-3,3'-[3₂]-Ferrocenophane-4,5^!-disuIfonic Acid, 6

Following the general procedure in Example 2 and referring to Fig. 2. 5 (20O g, 0.76 moles) with chlorosulfonic acid (189 g, 1.6 moles) in acetic acnhydride (2.5 L) gave 6 (100 g, 31%). ¹H NMR (300 MHz, D₂O): δ 4.50 (2H, s, H⁴-Cp¹ , H⁵-Cp²), 4.15 (2H, H²-Cp¹ , H²-Cp²), 2.20 (8H, m, alkyl), 1.70 (4H, m, alkyl). MSES^': m/z 212.3 [M - 2Hf; 424.9 [M - 2H]-; 447 [M - 2H + Na]^".

Example 9 Synthesis of 1 ,1 '-S.S'-Pal-Ferrpcenophane-^'-trimethyM -one, 7

Following the general procedure in Example 1(a) and referring to Fig. 2. 5 (2.0 g, 7.5 mmol) was dissolved in anhydrous DCM (150 ml_) and cooled to - 78°C. The mixture was treated with AICb (1.0 g, 7.5 mmol) followed by dropwise addition over 1 hr of acyloyl chloride (0.6 ml_, 7.6 mmol) dissolved in anhydrous DCM (30 ml_). The mixture was stirred vigorously at -78°C for a further 6 hrs. The mixture was allowed to warm to ambient temperature before being quenched with water. The crude material was extracted into DCM with treating of the separation phases with TiCI₃ (1 - 2 mL of 12% in HCI). The organic phase was retained, dried over MgSO₄, filtered and the solvent removed in vacuo. Purification was performed on silica gel; gradient elution from ligroin to ligroin/diethyl ether (75/25 v/v). The product 7 was isolated as an orange solid (260 mg, 11%) along with a substantial quantity of 5 (558 mg, 28%). ¹H NMR (500 MHz, CDCl₃); δ 4.20 (1 H₁ s, H¹-Cp¹), 3.85 (I H, s, H²~Cp¹), 3.65 (2H, m, H¹-Cp², H²-Cp²), 2.00 (16H, broad multiplet, H^ alkyl). R_f = 0.2 (silica gel; Iigroin/Et₂O 75/25).

. ^*>7 . Example 10

Synthesis of [3₃]-Ferrocenophane, 8

Following the general procedure in Example 1(b) and referring to Fig. 2. 7 (260 mg, 0.81 mmol) was treated with AICI₃ (220 mg, 1.65 mmol) and LiAIH₄ (60 mg, 1.57 mmol) in anhydrous diethyl ether (11O mL) yielding a bright yellow solid 8 (187 mg, 76%). R_f = 0.9 (silica gel; Iigroin/Et₂θ 4/1 v/v).

Example 11 Synthesis of [3i]-Ferrocenophan-1-ol, 9

1 (200 mg, 0.85 mmol) was dissolved in anhydrous Et₂θ (30 mL) and cooled to 0⁰C. The mixture was then treated with LiAIH₄ (52 mg, 1.37 mmol) at 0⁰C and allowed to slowly warm to ambient temperature. The mixture is visibly observed to change colour. After 1 hour the mixture was quenched with distilled water [Caution! LiAIH₄ reacts violently with water liberating extremely flammable gases.]. The product 9 was extracted into Et₂O, dried over MgSO₄, filtered and the solvent evaporated in vacuo yielding a bright yellow solid (187 mg, 97%). MS(ES+): m/z 242.1 [M]⁺.

The performance of the catholyte of the present invention is described in the following examples.

Example 12

A standard three electrode ceϋ having (a) a 0.5 cm² glassy carbon electrode, (b) a reference calomel electrode (SCE) with a luggin capillary placed with the end about 2 mm away from the electrode, and (c) a platinum counter electrode was set up.

A solution of 0.01 M I'-S.S'-tSaHerrocenophane-^δ'-disulfonic acid in 0.1 M H₂SO₄ZNa₂SO₄ at pH 2.5 was prepared. A cyclic voltammogram was recorded over 500 continuous cycles at 0.1 V/s whilst the solution was heated to at 75⁰C. During this time there was no decrease in current indicating that the ferrocene species is stable under these conditions. Furthermore, the CV displays reversible electrochemistry with a peak separation of 70 mV. Figure 3 shows an example voltammogram containing 100 sweeps with potentials given relative to the standard calomel reference electrode.

Example 13

The relative stabilities of acidic solutions of the unbridged ferrocene species 1 ,1 '-bis(sulphonato)-ferrocene diammonium salt and the bridged ferrocene species 1 '-3,3'-[3₂]-ferrocenophane-4,5'-disulfonic acid were examined using UV-Vis spectroscopy. A 1cm quartz cuvette was used in a double beam instrument using water in the reference cuvette.

A 2.O mM solution of 1 ,1'-bis(sulphonato)-ferrocene diammonium salt was prepared in 0.1 IvI glycine buffer solution at pH 2.5. A UV-Vis spectrum was recorded before and after an aliquot of this solution was allowed to stand in light at room temperature for a period of 50 minutes. A substantial decrease in absorbance was observed after this 50 minute period indicating that this unbridged ferrocene is unstable in this environment (Fig. 4). A 1.1 mM solution of 1'-3,3'-[32]-ferrocenophane-4,5'-disulfonic acid was prepared in 0.1 M Na₂SO₄/H₂SO₄ buffer solution at pH 2.5. A UV-Vis spectrum was recorded before and after an aliquot of this solution was allowed to stand in light at room temperature for a period of 1 week. Even after this extended period of time, there was very little change in the recorded UV-Vis spectrum (Fig. 5), indicating that the introduction of bridging units greatly increase the stability of the ferrocene species under these conditions.

Example 14

A catholyte solution of the present invention was prepared and its performance assessed using a redox cathode and a hydrogen anode. A commercial anode was used with a platinised gas diffusion layer from E-TEK (De Nora Deutschland), ¹/4 MEA from Ion Power lnc using a 0.05 mm NafionRTM 25 (DuPont) membrane. A reticulated vitreous carbon (RVC) electrode was used for the cathode. The catholyte solution was pumped through this electrode before passing to a reservoir from where it was recircuiated. The total liquid volume was 100 mL.

The catholyte solution tested contained 0.01 M 1'-3,3'-[3₂]-ferrocenophane- 4,5'-disulfonic acid in 0.1 M H₂SO₄. The solution was partially oxidized in the fuel cell by applying a potential of 0.75 V for a period of 10 minutes. A polarization curve was then recorded and is shown in Fig. 6.

Claims

1. A redox fuel cell comprising an anode and a cathode separated by an ion selective polymer electrolyte membrane; means for supplying a fuel to the anode region of the cell; means for supplying an oxidant to the cathode region of the cell; means for providing an electrical circuit between the anode and the cathode; a catholyte solution comprising at least one non-volatile catholyte component flowing in fluid communication with the cathode, the catholyte solution comprising a modified ferrocene species comprising at least one bridging unit between the cyclopentadienyl rings, the modified ferrocene species being at least partially reduced at the cathode in operation of the cell, and at least partially regenerated by reaction with the oxidant after such reduction at the cathode by direct reaction with the oxidant or by indirect reaction therewith using a redox catalyst catalysing the regeneration of the ferrocene mediator.

2. A fuel cell according to claim 1 wherein the modified ferrocene species is represented by the formula

wherein:

A-(B)n-C together comprise a divalent heteroannular bridging group; n is from 1 to 6; and each B (B^1"6) may be the same or different.

3. A fuel cell according to claim 2 wherein the divalent heteroannular bridging group is selected from optionally substituted straight or branched chain Ci-C₂O alkylidene, C2-C20 alkenylidene, C₃-C₂O cycloalkylidene, Ce-C₂Q arylidene, C₇-C₂₀ alkylarylidene, or a C₇-C₂₀ arylalkylidene radicals, optionally containing one or more heteroatoms.

4. A fuel cell according to claim 3 wherein the or each heteroatom present is selected from oxygen, nitrogen, phosphorus and sulphur.

5. A fuel cell according to any one of claims 2 to 4 wherein A, B¹ - B⁶ and C are independently selected from carbon, sulphur, oxygen, nitrogen and phosphorus and from functional groups comprising one or more of those atoms.

6. A fuel cell according to any one of claims 2 to 5 wherein the number of bridging units (A-(B)_n-C) between the cyclopentadienyl rings is from 1 to 5 and the bridging units may be the same or different.

7. A fuel cell according to claim any one of claims 2 to 6 wherein n is from 1 to 3

8. A fuel cell according to claim 7 wherein n is from 1 to 2.

9. A fuel cell according to any one of claims 2 to 8 wherein the or each bridging unit A-(B)_n-C may be the same or different, and -A-, -B¹-, -B²-, -B³-, -B⁴-, -B⁵-, -B⁶- and -C- are preferably independently selected from compatible combinations of substituted and unsubstituted, branched- and straight-chain -(CH₂)-, -CH(alkyl)-, - C(alkyl)₂-, -CH(alkenyl)-, -C(alkenyl)₂-, -CH(alkynyl)-, -C(alkynyl)₂-, -CH(aryl)-, -CH(heteroaryl)-, - O-, -S-, -(NH)-, -N(alkyl)-, -CH(OH)-, -CH(O-alkyl)-, -C(=O)-, -C-O-C(=O)- or -O-C(=O)-OR-C(=O)-O-.

10. A fuel ceil according to any one of claims 2 to 9 wherein the ferrocene bridging units A, B, and C, may carry further substituent groups which are independently selected from hydrogen and from functional groups comprising halogen, hydroxy, amino, protonated amino, imino, nitro, cyano, acyl, acyloxy, sulphate, sulphonyl, sulphinyl, alkylamino, protonated alkylamino, quaternary alkylammonium, carboxy, carboxylic acid, ester, ether, amido, sulphonate, sulphonic acid, sulphonamide, phosphonic acid, phosphonate, phosphate, alkylsulphonyl, arylsulphonyl, alkoxycarbonyl, alkylsulphinyl, alkylthio, arylthio, alkyl, alkoxy, oxyester, oxyamido, aryl, arylamino, aryloxy, heterocycloalkyl, heteroaryl, (C2-C5)alkenyl, (C2-C5)alkynyl, azido, phenylsulphonyloxy o amino acid conjugates having the formula - CO-W-OH, where W is an amino acid , and from alkyl, alkenyl, aryl, cycioalkyl, alkaryl, alkenaryl, aralkyl, aralkenyl groups substituted with one ore more of the aforesaid functional groups.

11. A fuel cell according to any one of claims 2 to 10 wherein the or each bridging unit is further branched and/or extended at any bridging atom on any bridge by any suitable number of spacer and/or functional groups,

12. A fuel cell according to claim 11 wherein the or each spacer group is independently selected from straight or branched chain, substituted or unsubstituted alkyl, alkenyl, aryl, heteroaryl, cycioalkyl, alkaryl, alkenaryl, acetylene, and suitable _combjnations of the aforesaid units.

13. A fuel cell according to any one of claims 2 to 12 wherein at least one ferrocene sites without a bridging substituent is independently substituted with hydrogen or with functional groups comprising halogen, hydroxy, amino, imino, nitro, cyano, acyl, acyloxy, sulphate, sulphonyl, sulphinyl, alkylamino, carboxy, carboxylic acid, ester, ether, amido, sulphonate, sulphonic acid, sulphonamide, phosphonic acid, phosphonate, phosphonic acid, phosphate, alkylsulphonyl, aryisulphonyf, alkoxycarbonyl, alkylsulphinyl, arylsulphinyi, aikylthio, aryithio, alkyl, alkoxy, oxyester, oxyamido, aryl, arylamino, aryloxy, heterocycloalkyl, heteroaryl, (C₂-C₅)aikenyl, (C₂-C-₅)alkynyl, azido phenylsulphonyloxy or amino acid conjugates having the formula - CO-W-OH, where W is an amino acid, and from alkyl, alkenyl, aryl, cycloalkyl, alkaryl alkenaryl, aralkyl, aralkenyl groups substituted with one or more of the aforesaid functional groups.

14. A fuel cell according to any one of claims 1 to 13 wherein the modified ferrocene species is selected from::

15. A redox fuel cell according to claims 1-14 wherein the ion selective polymer electrode membrane is cation and/or proton selective.

16. A redox fuel cell according to any one of claims 1 to 15 wherein the catholyte is acidic.

17. A redox fuel cell according to claim 16 wherein the modified ferrocene species is non-ionic or anionic in its oxidised form.

18. A redox fuel cell according to claim 17 wherein the modified ferrocene species is anionic in its oxidised form.

19. A redox fuel cell according to any one of Claims 1 to 14 wherein the ion selective polymer electrode membrane is anion selective.

20. A redox fuel cell according to Claim 19 wherein the catholyte is alkali.

21. A redox fuel cell according to Claim 20 wherein the modified ferrocene species is non-ionic or cationic in its reduced form.

22.A redox fuel cell according to any one of claims 1 to 14 wherein the ion selective polymer electrode membrane is a bi-membrane,

23.A redox fuel cell according to any one of claims 1 to 22 wherein the modified ferrocene species is present in the catholyte at a concentration of at least 0.0001 M.

24.A redox fuel cell according to any one of claims 1 to 23 wherein the modified ferrocene species is present in the catholyte at a concentration of at least 0.005M.

25.A redox fuel cell according to any one of claims 1 to 24 wherein the modified ferrocene species is present in the catholyte at a concentration of at least 0,001 M.

26.A redox fuel cell according to any one of claims 1 to 25 wherein the catholyte additionally comprises a catalyst redox species.

27.A redox fuel cell according to claim 26 wherein the catalyst redox species is selected from ligated transition metal complexes, polyoxometallate species, and combinations thereof.

28.A redox fuel cell according to claim 27 wherein the transition metal(s) in the transition metal complexes are selected from manganese (Il - V), iron (I - IV), copper (I - III), cobalt (I - III), nickel (I - III), chromium (Il - VII), titanium (Il - IV), tungsten (IV - Vl), vanadium (Il - V) and molybdenum (Il - V!).

29.A redox fuel cell according to claim 26 wherein the catalyst redox species comprises a multidentate N-donor ligand.

30. A redox fuel cell according to claim 29 wherein the N-donor ligand comprises one or more pyridine substituents.

31. A redox fuel cell according to claim 30 wherein the catalyst redox species is an iron complex of N4Py, pydien, trilen or derivatives thereof.

32.A catholyte solution for use in a redox fuel cell according to any one of Claims 1 to 31.