WO2009026637A1 - Article for extracting a component from a fluid stream, methods and systems including same - Google Patents
Article for extracting a component from a fluid stream, methods and systems including same Download PDFInfo
- Publication number
- WO2009026637A1 WO2009026637A1 PCT/AU2008/001269 AU2008001269W WO2009026637A1 WO 2009026637 A1 WO2009026637 A1 WO 2009026637A1 AU 2008001269 W AU2008001269 W AU 2008001269W WO 2009026637 A1 WO2009026637 A1 WO 2009026637A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- article
- body portion
- bores
- component
- carbon
- Prior art date
Abstract
Description
Claims