WO2009012113A1 - Functionalized polymers, articles prepared therefrom, and methods for making the same - Google Patents
Functionalized polymers, articles prepared therefrom, and methods for making the same Download PDFInfo
- Publication number
- WO2009012113A1 WO2009012113A1 PCT/US2008/069639 US2008069639W WO2009012113A1 WO 2009012113 A1 WO2009012113 A1 WO 2009012113A1 US 2008069639 W US2008069639 W US 2008069639W WO 2009012113 A1 WO2009012113 A1 WO 2009012113A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- carbon
- composition
- propylene
- coagent
- double bond
- Prior art date
Abstract
Description
Claims