WO2008112061A1 - Method of building three-dimensional objects with modified abs materials - Google Patents
Method of building three-dimensional objects with modified abs materials Download PDFInfo
- Publication number
- WO2008112061A1 WO2008112061A1 PCT/US2008/002021 US2008002021W WO2008112061A1 WO 2008112061 A1 WO2008112061 A1 WO 2008112061A1 US 2008002021 W US2008002021 W US 2008002021W WO 2008112061 A1 WO2008112061 A1 WO 2008112061A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- extrusion
- modified abs
- abs material
- modified
- build
- Prior art date
Abstract
Description
Claims