WO2008110602A1 - Polyisocyanate-based adhesive - Google Patents
Polyisocyanate-based adhesive Download PDFInfo
- Publication number
- WO2008110602A1 WO2008110602A1 PCT/EP2008/053015 EP2008053015W WO2008110602A1 WO 2008110602 A1 WO2008110602 A1 WO 2008110602A1 EP 2008053015 W EP2008053015 W EP 2008053015W WO 2008110602 A1 WO2008110602 A1 WO 2008110602A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- adhesive
- polyisocyanate
- reaction mixture
- hydrogen atoms
- reactive hydrogen
- Prior art date
Abstract
Description
Claims