WO2008079892A1 - Composition and articles containing cross-liinked polymer matrix and immobilized active liquid, and methods of making same - Google Patents
Composition and articles containing cross-liinked polymer matrix and immobilized active liquid, and methods of making same Download PDFInfo
- Publication number
- WO2008079892A1 WO2008079892A1 PCT/US2007/088178 US2007088178W WO2008079892A1 WO 2008079892 A1 WO2008079892 A1 WO 2008079892A1 US 2007088178 W US2007088178 W US 2007088178W WO 2008079892 A1 WO2008079892 A1 WO 2008079892A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- polyamine
- active liquid
- article
- polymeric matrix
- compound
- Prior art date
Abstract
Description
Claims