WO2008064417A1 - Matériau de revêtement - Google Patents

Matériau de revêtement Download PDF

Info

Publication number
WO2008064417A1
WO2008064417A1 PCT/AU2007/001835 AU2007001835W WO2008064417A1 WO 2008064417 A1 WO2008064417 A1 WO 2008064417A1 AU 2007001835 W AU2007001835 W AU 2007001835W WO 2008064417 A1 WO2008064417 A1 WO 2008064417A1
Authority
WO
WIPO (PCT)
Prior art keywords
particles
coating material
polymer matrix
water
coating
Prior art date
Application number
PCT/AU2007/001835
Other languages
English (en)
Inventor
Mark Geoffrey Sceats
Connor James Horley
Original Assignee
Calix Limited
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from AU2006906654A external-priority patent/AU2006906654A0/en
Application filed by Calix Limited filed Critical Calix Limited
Publication of WO2008064417A1 publication Critical patent/WO2008064417A1/fr

Abstract

La présente invention concerne un matériau de revêtement, un matériau composite, et une peinture antisalissure. Le matériau de revêtement une matrice polymère et des inclusions particulaires de dolomite caustique partiellement calcinée ou de magnésite caustique.
PCT/AU2007/001835 2006-11-28 2007-11-28 Matériau de revêtement WO2008064417A1 (fr)

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
AU2006906654A AU2006906654A0 (en) 2006-11-28 An anti-fouling paint
AU2006906654 2006-11-28
AU2007903095A AU2007903095A0 (en) 2007-06-07 A Coating Material
AU2007903095 2007-06-07

Publications (1)

Publication Number Publication Date
WO2008064417A1 true WO2008064417A1 (fr) 2008-06-05

Family

ID=39467352

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/AU2007/001835 WO2008064417A1 (fr) 2006-11-28 2007-11-28 Matériau de revêtement

Country Status (1)

Country Link
WO (1) WO2008064417A1 (fr)

Cited By (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2010049535A1 (fr) * 2008-10-31 2010-05-06 Dsm Ip Assets B.V. Composition de revêtement antisalissure renfermant des nanoparticules fonctionnalisées
AU2012321097A1 (en) * 2012-12-25 2014-07-10 The University Of Melbourne Materials and methods
WO2015100468A1 (fr) * 2014-01-02 2015-07-09 Calix Ltd Produits d'oxyde formés de poudre de carbonate calcinée destinés à être utilisés comme biocide, détoxifiant chimique et produits de support catalytique
CN108752045A (zh) * 2018-05-07 2018-11-06 安徽中鼎美达环保科技有限公司 一种免烧结、自固化、高强度多孔陶瓷保护涂层及其制备方法
CN112408793A (zh) * 2020-11-24 2021-02-26 清远市简一陶瓷有限公司 高透光耐磨熔块及其制备方法、釉料和大理石瓷砖
CN114350197A (zh) * 2021-12-31 2022-04-15 万华化学集团股份有限公司 一种抗菌肤感漆及其制备方法

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB2168984A (en) * 1984-12-03 1986-07-02 Chemopetrol Koncernova Ucelova A powdery filler for plastics
RU1774922C (ru) * 1990-12-21 1992-11-07 Эдуард Петрович Блашкун Способ изготовлени слоистого плиточного материала
RU2096380C1 (ru) * 1995-08-31 1997-11-20 Тульский государственный университет Способ изготовления изделий
JP2001026754A (ja) * 1999-07-14 2001-01-30 Nobuhide Maeda 複合接着剤およびこれを用いてなる複合材料
EP1661460A1 (fr) * 2003-08-12 2006-05-31 Mochigase Electric Technical Co., Ltd. Agent antiviral ainsi que fibres et elements antiviraux pourvus dudit agent

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB2168984A (en) * 1984-12-03 1986-07-02 Chemopetrol Koncernova Ucelova A powdery filler for plastics
RU1774922C (ru) * 1990-12-21 1992-11-07 Эдуард Петрович Блашкун Способ изготовлени слоистого плиточного материала
RU2096380C1 (ru) * 1995-08-31 1997-11-20 Тульский государственный университет Способ изготовления изделий
JP2001026754A (ja) * 1999-07-14 2001-01-30 Nobuhide Maeda 複合接着剤およびこれを用いてなる複合材料
EP1661460A1 (fr) * 2003-08-12 2006-05-31 Mochigase Electric Technical Co., Ltd. Agent antiviral ainsi que fibres et elements antiviraux pourvus dudit agent

Non-Patent Citations (3)

* Cited by examiner, † Cited by third party
Title
DATABASE WPI Week 199348, Derwent World Patents Index; Class P73, AN 1993-383952 *
DATABASE WPI Week 199830, Derwent World Patents Index; Class A93, AN 1998-346027 *
PATENT ABSTRACTS OF JAPAN *

Cited By (17)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2010049535A1 (fr) * 2008-10-31 2010-05-06 Dsm Ip Assets B.V. Composition de revêtement antisalissure renfermant des nanoparticules fonctionnalisées
CN102203195A (zh) * 2008-10-31 2011-09-28 帝斯曼知识产权资产管理有限公司 含有功能纳米颗粒的防污涂料组合物
AU2012321097A1 (en) * 2012-12-25 2014-07-10 The University Of Melbourne Materials and methods
US10421871B2 (en) 2012-12-25 2019-09-24 The University Of Melbourne Materials and methods
EP2938415A4 (fr) * 2012-12-25 2016-05-11 Univ Melbourne Matériaux et procédés
AU2012321097B2 (en) * 2012-12-25 2016-06-30 The University Of Melbourne Materials and methods
AU2014374829B2 (en) * 2014-01-02 2018-01-04 Calix Ltd Oxide products formed from calcined carbonate powder for use as biocide, chemical detoxifier and catalyst support products.
EP3089589A4 (fr) * 2014-01-02 2017-06-14 Calix Ltd Produits d'oxyde formés de poudre de carbonate calcinée destinés à être utilisés comme biocide, détoxifiant chimique et produits de support catalytique
CN105899076A (zh) * 2014-01-02 2016-08-24 卡利有限公司 益生菌和杀生物剂及其生产方法和装置
US9913475B2 (en) 2014-01-02 2018-03-13 Calix Ltd Oxide products formed from calcined carbonate powder for use as biocide, chemical detoxifier and catalyst support products
CN105899076B (zh) * 2014-01-02 2019-07-16 卡利有限公司 益生菌和杀生物剂及其生产方法和装置
EP3530117A1 (fr) * 2014-01-02 2019-08-28 Calix Ltd Produits d'oxyde formés de poudre de carbonate calcinée destinés à être utilisés comme biocide, détoxifiant chimique et produits de support catalytique
WO2015100468A1 (fr) * 2014-01-02 2015-07-09 Calix Ltd Produits d'oxyde formés de poudre de carbonate calcinée destinés à être utilisés comme biocide, détoxifiant chimique et produits de support catalytique
CN108752045A (zh) * 2018-05-07 2018-11-06 安徽中鼎美达环保科技有限公司 一种免烧结、自固化、高强度多孔陶瓷保护涂层及其制备方法
CN112408793A (zh) * 2020-11-24 2021-02-26 清远市简一陶瓷有限公司 高透光耐磨熔块及其制备方法、釉料和大理石瓷砖
CN114350197A (zh) * 2021-12-31 2022-04-15 万华化学集团股份有限公司 一种抗菌肤感漆及其制备方法
CN114350197B (zh) * 2021-12-31 2023-03-28 万华化学集团股份有限公司 一种抗菌肤感漆及其制备方法

Similar Documents

Publication Publication Date Title
EP2215168B1 (fr) Composition antisalissure comprenant un aérogel
KR100880841B1 (ko) 방오 도료 조성물
WO2008064417A1 (fr) Matériau de revêtement
CN1100108C (zh) 防止含羟基吡啶硫酮的涂料组合物变色
US4513029A (en) Sea water antifouling method
EP1497382A1 (fr) Composition antisalissure comprenant une enzyme sans substrat
CN101935493A (zh) 一种水性无毒长效防污涂料及其制备方法
EP1272570A1 (fr) Composition de peinture antisalissures contenant de la colophane et une enzyme
CN111286273A (zh) 一种新型长效广谱抑菌抗菌多功能水性建筑涂料及其制备方法
US20040062807A1 (en) Biocide compositions and a method for their production
CN102190460B (zh) 钢化仿瓷涂料
US5314932A (en) Antifouling coating and method for using same
CA3190989A1 (fr) Formulations de revetement maritime
JP5429453B2 (ja) 石灰を含有する水配合コーティング組成物
EP3033385B1 (fr) Désintégration de films et particules déclenchée par concentration ionique
KR20160017805A (ko) 알리자린을 포함하는 방오제 및 방오도료 조성물
AU2009247593A1 (en) Novel environmental friendly anti-microbial adhesion agents for anti-fouling paints and anti-fouling paints containing them
JPH04120183A (ja) 塗料組成物
KR20000067313A (ko) 액상 규산염을 함유하는 수성 무기 바인더 및 이를 이용한 도료 조성물
WO1992007037A1 (fr) Composition antisalissure
KR20150082273A (ko) Dcoit를 함유한 방출 제어 조성물
JPS58183762A (ja) 船底防汚塗料
US5713987A (en) Method as well as active substance for preventing microbial growth on surfaces, as well as compound for surface coating or finishing
JP2006117894A (ja) 海洋生物付着防止塗料
JP4806769B2 (ja) 防汚性樹脂およびその製造方法、並びに防汚塗料

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 07815635

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

32PN Ep: public notification in the ep bulletin as address of the adressee cannot be established

Free format text: NOTING OF LOSS OF RIGHTS PURSUANT TO RULE 112(1) EPC, 1205A DATED 04.08.09.

122 Ep: pct application non-entry in european phase

Ref document number: 07815635

Country of ref document: EP

Kind code of ref document: A1