WO2008063931A2 - Bituminous emulsions - Google Patents
Bituminous emulsions Download PDFInfo
- Publication number
- WO2008063931A2 WO2008063931A2 PCT/US2007/084319 US2007084319W WO2008063931A2 WO 2008063931 A2 WO2008063931 A2 WO 2008063931A2 US 2007084319 W US2007084319 W US 2007084319W WO 2008063931 A2 WO2008063931 A2 WO 2008063931A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- molecular weight
- block
- peak molecular
- conjugated diene
- block copolymer
- Prior art date
Abstract
Description
Claims