WO2008000917A1 - Fiber-reinforced composites and method for the manufacture thereof - Google Patents
Fiber-reinforced composites and method for the manufacture thereof Download PDFInfo
- Publication number
- WO2008000917A1 WO2008000917A1 PCT/FI2007/050404 FI2007050404W WO2008000917A1 WO 2008000917 A1 WO2008000917 A1 WO 2008000917A1 FI 2007050404 W FI2007050404 W FI 2007050404W WO 2008000917 A1 WO2008000917 A1 WO 2008000917A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- fibers
- fiber
- filler
- dimethacrylate
- fillers
- Prior art date
Abstract
Description
Claims