WO2007130058A1 - Procédé de séchage de bois d'œuvre et appareil associé - Google Patents

Procédé de séchage de bois d'œuvre et appareil associé Download PDF

Info

Publication number
WO2007130058A1
WO2007130058A1 PCT/US2006/017805 US2006017805W WO2007130058A1 WO 2007130058 A1 WO2007130058 A1 WO 2007130058A1 US 2006017805 W US2006017805 W US 2006017805W WO 2007130058 A1 WO2007130058 A1 WO 2007130058A1
Authority
WO
WIPO (PCT)
Prior art keywords
timber
chamber
pressure
moisture
heated platens
Prior art date
Application number
PCT/US2006/017805
Other languages
English (en)
Inventor
Dennis Richard Socling
Original Assignee
Pcs Wood Technologies, Llc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Pcs Wood Technologies, Llc filed Critical Pcs Wood Technologies, Llc
Priority to PCT/US2006/017805 priority Critical patent/WO2007130058A1/fr
Publication of WO2007130058A1 publication Critical patent/WO2007130058A1/fr

Abstract

La présente invention concerne un appareil (100) et un procédé de séchage de bois d'œuvre. Le bois d'œuvre disposé en couches avec des plateaux (106) à l'intérieur d'une chambre (120) est pratiquement chauffé uniformément avec les plateaux (106) jusqu'à une température associée à une tension de vapeur de l'humidité présente à l'intérieur du bois d'œuvre. La chambre (120) est exposée à une première condition de pression, dans laquelle une pression sub-atmosphérique supérieure à la tension de vapeur correspondant à la température enlève l'humidité non fixée du bois d'œuvre, pendant qu'une première humidité relative maintenue à l'intérieur de la chambre (120) minimise un gradient d'humidité à l'intérieur du bois d'œuvre. La chambre (120) est ensuite exposée à une deuxième condition de pression, dans laquelle un cycle entre une première limite de pression inférieure à la pression atmosphérique et une deuxième limite de pression autour de la tension de vapeur correspondant à la température enlève l'humidité non fixée du bois d'œuvre, pendant qu'une deuxième humidité relative choisie maintenue à l'intérieur de la chambre (120) maintient l'humidité autour d'une surface, et minimise les défauts de surface, du bois d'œuvre alors que le bois d'œuvre est séché.
PCT/US2006/017805 2006-05-09 2006-05-09 Procédé de séchage de bois d'œuvre et appareil associé WO2007130058A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
PCT/US2006/017805 WO2007130058A1 (fr) 2006-05-09 2006-05-09 Procédé de séchage de bois d'œuvre et appareil associé

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/US2006/017805 WO2007130058A1 (fr) 2006-05-09 2006-05-09 Procédé de séchage de bois d'œuvre et appareil associé

Publications (1)

Publication Number Publication Date
WO2007130058A1 true WO2007130058A1 (fr) 2007-11-15

Family

ID=37560763

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2006/017805 WO2007130058A1 (fr) 2006-05-09 2006-05-09 Procédé de séchage de bois d'œuvre et appareil associé

Country Status (1)

Country Link
WO (1) WO2007130058A1 (fr)

Cited By (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
ITGE20090075A1 (it) * 2009-10-06 2011-04-07 Sergio Ninchi " la conduzione tecnologica dell'essiccazione sotto vuoto con il nuovo sistema termoguidato per rovere e la tifoglie eseguito con termoregolatori "
ITGE20090081A1 (it) * 2009-10-28 2011-04-29 Sergio Ninchi Nuovo sistema di essicazione sotto vuoto con la conduzione a cicli termoguidati della temperatura per abete di forte spessore, legni di facile evaporazione e travi.
US7963048B2 (en) * 2005-05-23 2011-06-21 Pollard Levi A Dual path kiln
US8201501B2 (en) 2009-09-04 2012-06-19 Tinsley Douglas M Dual path kiln improvement
EP3093596A1 (fr) * 2015-05-11 2016-11-16 Coldbay AB Procédé pour déterminer une action
US10619921B2 (en) 2018-01-29 2020-04-14 Norev Dpk, Llc Dual path kiln and method of operating a dual path kiln to continuously dry lumber
CN109442916B (zh) * 2018-10-25 2021-02-26 老河口市天和科技有限公司 一种2-氯烟酸湿品干燥工艺及其干燥设备
US20210207886A1 (en) * 2018-07-02 2021-07-08 Green Mountain Mechanical Design, Inc. Vacuum drying kilns and control systems therefore

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3521373A (en) * 1967-07-20 1970-07-21 Vincenzo Pagnozzi Process and plant for the vacuum drying of wood in the form of planks or laths
US4620373A (en) * 1984-07-23 1986-11-04 Laskowski Donald R Dry kiln and method
US20050220924A1 (en) * 2004-03-23 2005-10-06 Apollo Hardwoods Company Heating panel
WO2006028388A1 (fr) * 2004-09-10 2006-03-16 Pcs Wood Technologies Limited Systeme procede et dispositif de sechage de bois d'oeuvre

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3521373A (en) * 1967-07-20 1970-07-21 Vincenzo Pagnozzi Process and plant for the vacuum drying of wood in the form of planks or laths
US4620373A (en) * 1984-07-23 1986-11-04 Laskowski Donald R Dry kiln and method
US20050220924A1 (en) * 2004-03-23 2005-10-06 Apollo Hardwoods Company Heating panel
WO2006028388A1 (fr) * 2004-09-10 2006-03-16 Pcs Wood Technologies Limited Systeme procede et dispositif de sechage de bois d'oeuvre

Cited By (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US7963048B2 (en) * 2005-05-23 2011-06-21 Pollard Levi A Dual path kiln
US8201501B2 (en) 2009-09-04 2012-06-19 Tinsley Douglas M Dual path kiln improvement
US8342102B2 (en) 2009-09-04 2013-01-01 Douglas M Tinsley Dual path kiln improvement
ITGE20090075A1 (it) * 2009-10-06 2011-04-07 Sergio Ninchi " la conduzione tecnologica dell'essiccazione sotto vuoto con il nuovo sistema termoguidato per rovere e la tifoglie eseguito con termoregolatori "
ITGE20090081A1 (it) * 2009-10-28 2011-04-29 Sergio Ninchi Nuovo sistema di essicazione sotto vuoto con la conduzione a cicli termoguidati della temperatura per abete di forte spessore, legni di facile evaporazione e travi.
EP3093596A1 (fr) * 2015-05-11 2016-11-16 Coldbay AB Procédé pour déterminer une action
US10619921B2 (en) 2018-01-29 2020-04-14 Norev Dpk, Llc Dual path kiln and method of operating a dual path kiln to continuously dry lumber
US20210207886A1 (en) * 2018-07-02 2021-07-08 Green Mountain Mechanical Design, Inc. Vacuum drying kilns and control systems therefore
US11624557B2 (en) 2018-07-02 2023-04-11 Green Mountain Mechanical Design, Inc. Vacuum drying kilns and control systems therefore
CN109442916B (zh) * 2018-10-25 2021-02-26 老河口市天和科技有限公司 一种2-氯烟酸湿品干燥工艺及其干燥设备

Similar Documents

Publication Publication Date Title
WO2007130058A1 (fr) Procédé de séchage de bois d'œuvre et appareil associé
FI87691B (fi) Foerfarande foer torkning av trae och traebaserade produkter
US4182048A (en) Method of drying lumber
Liu et al. Radio-frequency/vacuum drying of softwoods: drying of thick western red cedar with constant electrode voltage
CN105387691B (zh) 一种控制木材皱缩的干燥方法
JP2002086407A (ja) 木材の人工乾燥方法および木材乾燥装置
US6857201B2 (en) Method for treating and drying of wood
CN107036394B (zh) 一种楠木板材的真空干燥方法
JP2008106959A (ja) 木材乾燥装置及び木材乾燥方法
WO2006028388A1 (fr) Systeme procede et dispositif de sechage de bois d'oeuvre
US11624557B2 (en) Vacuum drying kilns and control systems therefore
KR20120009972A (ko) 반건시 제조장치 및 제조방법
AT409421B (de) Verfahren und vorrichtung zum trocknen von feuchtigkeit enthaltenden produkten
JP5900793B2 (ja) 木材の乾燥方法、および木材用の乾燥装置
EP2959247B1 (fr) Procédé de séchage de matériau hygroscopique et et appareil de séchage de matériau hygroscopique
RU2110026C1 (ru) Способ, устройство и нагреватель для сушки древесины
JP2009085542A (ja) 木材乾燥方法
CN2345927Y (zh) 木材干燥机
Begloua et al. EffEct of drying mEthods on wood strEngth
JP3320057B2 (ja) 木材の乾燥方法および乾燥装置
WO2002065038A1 (fr) Procede et dispositif pour le sechage du bois
CN1719228A (zh) 木材真空过热蒸汽干燥实验装置及检测方法
JP2019184097A (ja) 木材の乾燥方法
RU2277682C2 (ru) Способ сушки пиломатериала (варианты) и сушилка для его осуществления
FI110891B (fi) Menetelmä ja laitteisto puumateriaalin kuivaamiseksi ja/tai lämpökäsittelemiseksi

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 06759360

Country of ref document: EP

Kind code of ref document: A1

DPE1 Request for preliminary examination filed after expiration of 19th month from priority date (pct application filed from 20040101)
NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 06759360

Country of ref document: EP

Kind code of ref document: A1