WO2007087675A1 - Improved base metal recovery process from heap leaching - Google Patents
Improved base metal recovery process from heap leaching Download PDFInfo
- Publication number
- WO2007087675A1 WO2007087675A1 PCT/AU2007/000087 AU2007000087W WO2007087675A1 WO 2007087675 A1 WO2007087675 A1 WO 2007087675A1 AU 2007000087 W AU2007000087 W AU 2007000087W WO 2007087675 A1 WO2007087675 A1 WO 2007087675A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- leach solution
- heap
- reducing gas
- pregnant leach
- ore
- Prior art date
Abstract
Description
Claims