WO2007019063A1 - Polyurethanes made from hydroxyl-containing fatty acid amides - Google Patents

Abstract

Polyurethanes, and rigid polyurethane foams in particular, are made using certain amides of modified fatty acids. The fatty acid groups are substituted hydroxymethyl, N-hydroxyalkyl aminoalkyl or hydroxy-substituted ester groups. The amide portion of the molecule contains hydroxyalkyl or other hydroxyl-substituted organic groups bonded to the amide nitrogen.

Description

POLYURETHANES MADE FROM HYDROXYL-CONTAINING PATTY ACID AMIDES

This application claims benefit of United States Provisional Application No. 60/705,086, filed 3 August 2005.

This invention relates to polyurethane polymers and methods for making such polymers.

Polyurethanes are produced by the reaction of polyisocyanates and polyols.

One type of polyurethane, rigid polyurethane foam, is widely used in thermal insulation and structural applications. The starting materials used to make these rigid polyurethane foams tend to be low equivalent weight, high functionality polyols and high functionality polyisocyanates, as these materials provide a densely crosslinked polymeric structure. The polyols are most typically polyethers and polyesters that are derived from petroleum feedstocks. Rigid polyurethane foams have been made with castor oil or castor oil byproducts.

Polyols for rigid foam applications must meet several demands. They provide the needed crosslinking to the polymer structure and to form a foam, having the necessary mechanical attributes. The polyols must react with the other components in the formulation to form a foam having a fine and uniform cell structure. This is especially the case when the foam is used in thermal insulating applications. To accomplish this, the polyols must be reasonably compatible with the other components in the formulation, in particular water and the polyisocyanate. It is especially desirable that the polyol can be used with readily available surfactants and catalyst packages. The polyols should be reactive enough that the foam rises and cures quickly without the need for very high levels of catalysts, while still providing for good processing and yielding a high quality foam.

Because of unpredictable crude oil pricing and a growing desire to find alternative feedstocks for making commodity chemicals, there is an interest in replacing conventional polyols with newer materials that are made using renewable feedstocks such as vegetable oils or animal fats.

One approach to creating vegetable oil-based polyols is described in EP 0 106 491A2. Certain fatty acid mixtures are hydroxymethylated, and esters are formed by reacting the hydroxymethylated material with a polyhydroxyl initiator. More recently, higher functionality versions of these materials have been developed, as

and WO 04/096883A. These polyols are described as being useful in flexible foam and other elastomeric polyurethane applications.

Amides of hydroxymethylated fatty acids with alkanolamines have been described for use in making rigid polyurethane foam. See Khoe et al., "Polyurethane Foams form Hydroxymethylated Fatty Diethanolamides", J. Amer. Oil Chemists' Society 50:331-333 (1973). The foam described therein was made using Freon 11 as a blowing agent. Khoe et al. report that in such a formulation, the amide compound produced foam with inadequate dimensional stability when used as the sole polyol.

Other vegetable oil-based polyols are described, for example in GB1248919. These polyols are prepared in the reaction of a vegetable oil with an alkanolamine (such as triethanolamine) to form a mixture of monoglycerides, diglycerides, and reaction products of the alkanolamine and fatty acid groups from the vegetable oil. These materials have free hydroxyl groups on the glycerine and alkanolamine portions of the molecules. The free hydroxyl groups are ethoxylated to increase reactivity and to provide a somewhat more hydrophilic character. This makes the product more compatible with a foam formulation containing water as a blowing agent. These products tend to have hydroxyl numbers in the range of from 185 to 200, which corresponds to a hydroxyl equivalent weight in the range of about 280 to 305, and a functionality of about 2.3. The equivalent weights tend to be higher than preferred and the functionalities are lower than needed for producing good quality rigid polyurethane foam.

It would be desirable to provide a polyol that is based on annually renewable feedstocks such as vegetable oils, which can be used to make good quality rigid polyurethane foams. It would be desirable to provide a polyurethane foam that is made using a significant proportion of raw materials derived from an annual renewable feedstock.

In one aspect, this invention is a process for preparing a polyurethane, comprising (a) forming a reaction mixture by mixing a polyol or mixture thereof with a polyisocyanate compound, wherein the polyol or polyol mixture includes one or more compounds having (1) an amide group having at least one hydroxyl-containing organic group bonded to the nitrogen atom of the amide group and (2) a branched or straight chain C7-23 hydrocarbon group bonded directly to the carbonyl carbon of the amide group or ester group, wherein the C7.23 hydrocarbon group is substituted with at least one (i) (N-hydroxyalkyl) amino alkyl group or (ϋ) hydroxyl-containing ester group; and ^r(b) "sύBjecϊϊng '"the" "reacϊibn mixture to conditions such that it cures to form a polyurethane.

In a second aspect, this invention is a process for preparing a polyurethane, comprising (a) forming a reaction mixture by mixing a polyol or mixture thereof with a polyisocyanate compound, wherein the polyol or polyol mixture includes (I) one or more compounds having (1) an amide group having at least one hydroxyl-containing organic group bonded to the nitrogen atom of the amide group and (2) a branched or straight chain C7-23 hydrocarbon group bonded directly to the carbonyl carbon of the amide group or ester group, wherein the C7-23 hydrocarbon group is substituted with at least one (i) hydroxymethyl group, (ii) (N-hydroxyalkyl) amino alkyl group or (iϋ) hydroxyl-containing ester group and (II) at least one part by weight water per 100 parts by weight polyol or polyol mixture; and (b) subjecting the reaction mixture to conditions such that it cures to form a polyurethane.

In another aspect, this invention is a polyurethane made by either of the foregoing processes. In a preferred such process, the polyurethane is a rigid polyurethane foam, the reaction mixture includes a blowing agent and a surfactant, and polyol or mixture thereof has an average hydroxyl equivalent weight of from 100 to 350 and an average hydroxyl functionality of at least 2.5.

In another aspect, the invention is a rigid polyurethane foam made by either of the foregoing processes.

In yet another aspect, this invention is a polyol which is useful in making a polyurethane, and in particular a rigid polyurethane, in accordance with the invention. The polyol is a compound that includes (1) an amide group having at least one hydroxyalkyl group bonded to the nitrogen atom of the amide group, and (2) a branched or straight chain C7-23 hydrocarbon group bonded directly to the carbonyl carbon of the amide group. At least one hydroxyl-containing ester group is bonded to the U7-23 hydrocarbon group. The polyol of the invention can be prepared in alternative ways as described more below.

In making a polyurethane in accordance with the invention, a polyol or polyol mixture is reacted with an organic polyisocyanate. In embodiments of particular interest, the polyurethane is a rigid foam, and the polyol or polyol mixture has an average hydroxyl equivalent weight of from 100 to 350, preferably from 100 to 250 and especially from 110 to 150. For rigid foam applications, the polyol or polyol mixture Cbiϊt'kϊM"" bM 'or '^;;ιhϊdr' &' "jϊolyols that in the aggregate have an average hydroxyl functionality of at least 2.5, especially from 2.8 to 6 and most preferably from 3.0 to 4.5.

In one aspect of the invention, at least one polyol used in making the polyurethane is an amide compound having at least one amide (>N-C(O)-) group. This amide compound has at least one hydroxyl-containing organic group bonded to the nitrogen atom of the amide group. The compound further has a branched or straight chain C7-23 hydrocarbon group bonded directly to the carbonyl carbon of the amide group. The C7-23 hydrocarbon group is substituted with at least one hydroxymethyl group, N-hydroxyalkyl aminoalkyl group or hydroxyl-containing ester group. These amide compounds are conveniently prepared in several steps using vegetable oils or animal fats, or unsaturated fatty acids obtained from vegetable oils or animal fats, as a starting material.

The amide compound will typically be a mixture of materials having on average from one to eight or more hydroxyl groups per molecule. A preferred mixture of amide compounds contains on average at least two, especially at least 2.5 hydroxyl groups/molecule. A mixture of amide compounds having on average from 3 to 6 hydroxyl groups/molecule is especially preferred.

Hvdroxymethyl- group containing amide or ester compounds

Amide compounds having hydroxymethyl groups are conveniently described as an amide of (1) a primary or secondary amine compound that contains at least one hydroxyl group with (2) a fatty acid that contains at least one hydroxymethyl group. This type of amide has at least one hydroxyl-substituted organic group bonded to the amide nitrogen. A C7-23 hydrocarbon group is bonded to the carbonyl carbon of the amide group. The C7-23 hydrocarbon group is itself substituted with at least one hydroxymethyl group.

This type of amide compound is conveniently made using a vegetable oil or animal fat in a series of reactions. The vegetable oil or animal fat is typically a glyceride of one or more fatty acids having from 8 to 26 carbon atoms, more typically from 14 to 22 carbon atoms. At least a portion of the constituent fatty acids of the starting oil or fat has carbon-carbon double bonds in the fatty acid chain. It is preferred that at least 50 mole-% of the constituent fatty acids are unsaturated in this manner. The fatty acid may contain more than one carbon-carbon double bond, but in such cases the multiple carbon-carbon double bonds are preferably not conjugated. StoCablfe~fatfe"^|lέe-icl^ι"¹bils include, for example, chicken fat, canola oil, citrus seed oil, cocoa butter, corn oil, cottonseed oil, lard, linseed oil, oat oil, olive oil, palm oil, peanut oil, rapeseed oil, rice bran oil, saffLower oil, sesame oil, soybean oil, sunflower oil, or beef tallow. Fats and oils having a higher proportion of unsaturated constituent fatty acids are preferred.

Fatty acids can be obtained in the form of a lower alkyl ester from the starting fat or oil, by blending the starting fat or oil with a lower alkanol, preferably methanol or ethanol, and heating in the presence of a transesterification catalyst. The resulting fatty acid esters will contain fatty acid groups in the proportions in which those fatty acids occur naturally in the particular fat or oil that is used as the starting material. The mixture will in most instances include a quantity of saturated fatty acid esters. It is generally not necessary to separate the saturated fatty acids from the mixture, provided that the saturated materials constitute no more than about 50 mole%, especially no more than about 30 mole% of the fatty acid mixture. If a more defined or more highly purified fatty acid is desired, it is possible to separate the components of the fatty acid mixture or to use a starting fat or oil that contains a high proportion of a single constituent fatty acid. For example, purified fatty acid esters having from 1 to 3 preferably non-conjugated carbon-carbon double bonds in the fatty acid chain can be used as the starting material. Examples of these fatty acid esters include esters of linoleic acid, oleic acid, linolenic acid, and the like. Mixtures of two or more of these, or of one or more of these with a saturated fatty acid (or ester), can be used. This may be desirable to "tailor" the functionality (number of hydroxymethyl groups/molecule) or other characteristic of the product.

Using a more defined fatty acid has the advantage of producing a more defined amide product with a narrow molecular weight range and more controlled functionality. However, in most applications the benefits of obtaining the more defined product do not justify the higher cost.

The number of hydroxymethyl groups in the product is determined in part by the number of carbon-carbon double bonds in the starting fatty acid. The fatty acid ester is hydroformylated and then reduced to introduce hydroxymethyl groups. Hydroformylation is achieved by reaction with carbon monoxide and hydrogen. This introduces aldehyde (-CHO) groups onto the fatty acid chain at the site of carbon-carbon unsaturation. Suitable hydroformylation methods are described in U. S. Patent Nos. 4,731,486 and 4,633,021, for example, and in WO 04/096882 and WO 04/096883. A subsequent hydrogenation step converts the -CHO #rd%d' ''tb'''"'Kydϊ'ό^yW^til71 (-CH2OH) groups while hydrogenating residual carbon- carbon bonds to remove essentially all carbon-carbon unsaturation. The proportion of materials having 2 and 3 hydroxymethyl groups is typically somewhat lower than the proportion of starting fatty acids (or esters) containing 2 and 3 carbon-carbon double bonds, as the hydroformylation reaction often does not take place across all the carbon-carbon double bonds unless stringent reaction conditions are used. Carbon- carbon double bonds that are not hydroformylated generally become hydrogenated.

It is preferred that the resulting hydroxymethyl-containing fatty acid ester composition contains an average of at least 0.5, more preferably at least 0.8 and even more preferably at least 1.0 hydroxymethyl group per molecule. This is controlled through the selection of starting fatty acid composition and hydroformylation conditions. A preferred hydroxymethyl group-containing fatty acid is methyl- or ethyl 9(10)-hydroxymethylstearate, which is formed by hydroformylating and hydrogenating oleic acid or a fatty acid or ester mixture containing oleic acid (such as is prepared in the above-described transesterification reaction).

The amide compound is then formed by reacting the hydroxymethyl-containing fatty acid ester with an amine compound. The amine compound can be any primary or secondary amine that contains a hydroxy-substituted organic group. The hydroxyl- substituted organic group is preferably an alkanol group having form 2 to 8 carbon atoms, such as an ethanol (hydroxyethyl) or propanol (2- or 3-hydroxypropyl) group. The hydroxyl-substituted organic group may be bonded directly or indirectly to the nitrogen atom of the primary or secondary amino group.

The primary or secondary amine compounds of most interest are mono- and dialkanol amines, in which the alkanol group contains from 2 to 8, especially 2 to 4 carbon atoms. Dialkanolamines provide the amide compound with a higher hydroxyl functionality and may be more desirable on that basis. Commonly available alkanolamines such as monoethanolamine, diethanolamine, mono-2-propanolamine, di-2-propanolamine, and the like are conveniently used. Mono- and di-ethanolamine are especially preferred. Aminoalkyl alkanolamines (such as aminoethyl ethanolamine, for example) are also useful.

It is within the scope of the invention to use commercially available mixtures of alkanolamines, especially ethanolamine mixtures. Such ethanolamine mixtures include varying proportions of monoethanolamine, diethanolamine, triethanolamine, and aminoethylethanolamine as well as other ethanol-containing species. These mixtures can be used directly without separation into the various constituent species. (Jdmpϋn'ents" tftatW'rrøreontain amine hydrogens (such as triethanolamine) will form an ester, rather than an amide, with the fatty acid ester starting material. In addition, a small proportion of the alkanolamines that do contain amine hydrogen atoms may react through one of the hydroxyl groups to form esters, rather than amides, with the hydroxymethyl-containing fatty acid ester.

The reaction of the amine compound and hydroxymethyl-containing fatty acid ester is conveniently conducted by heating the mixture to a temperature of from 50 to 100⁰C. The reaction time may vary and will typically be on the order of minutes, hours or tens of hours, depending on the choice of catalyst and other process variables. If the starting materials are not volatile, reaction by-products (water or alcohols such as ethanol or methanol) can be removed during the course of the reaction by applying heat or vacuum. The reaction may be conducted in the presence of a base, such as an alkali metal hydroxide, or otherwise at high pH conditions. The reaction may be conducted neat, or in the presence of a solvent or diluent. It is also possible to use a hydroxymethyl-containing fatty acid as a reactant in the amide-forming reaction, rather than the lower alkyl ester.

The resulting product is typically a mixture of materials having amide groups. As mentioned before, if the amine compound contains some tertiary amine impurities, the produce will contain a corresponding proportion of esters of that tertiary amine and fatty acid. In addition, some esters may be formed even when the amine compound is devoid of tertiary amine species. The amide compounds have one or more hydroxyl-substituted organic groups (typically an alkanol group) bonded directly or indirectly to the amide nitrogen atom. The amide carbonyl group is bonded to a C7-23 hydrocarbon group. At least a portion of those C7-23 hydrocarbon groups is substituted with one or more hydroxymethyl groups.

The amide of this embodiment preferably has an average hydroxyl functionality of at least 2.5, especially at least 2.8 and more preferably at least 3.0.

Amide compounds containing at least one (N-hvdroxyalkyl) aminoalkyl group substituted onto a fatty acid chain

This type of amide compound is conveniently described as an amide of a fatty acid (or ester) and a hydroxyl-containing primary or secondary amine, in which the fatty acid group has been modified to introduce one or more (N-hydroxyalkyl) aminoalkyl groups. These materials can be prepared from vegetable or oils or animal fats in a sequence of reactions, as follows. JW^teslktϋMtfeftf fatty acid ester, or mixture thereof with other saturated or unsaturated fatty acid esters, is used as a starting material. These can be produced from the vegetable oil or animal fat in the manner described before. As before, at least 50 mole% and more preferably at least 80 mole% of the fatty acids contains at least one site of carbon-carbon unsaturation. As before, the fatty acids may contain two or more of such sites, in which case those sites preferably are not conjugated.

An amide is prepared from the fatty acid ester by reacting it with a primary or secondary amine compound that contains at least one hydroxyl-containing organic group. Suitable conditions for conducting this reaction are described before. Suitable amine compounds are those described earlier with respect to the hydroxymethyl group-containing amide compounds.

N-hydroxyalkylamino groups can be introduced onto the fatty acid chain of the resulting amide at sites of carbon-carbon unsaturation, via a reaction with a mono- or dialkanolamine in the presence of carbon monoxide and hydrogen gas. Synthetic methods for performing such a reductive animation reaction are described, for example, in Science 2002, 297, 1676-1678 and in United States Provisional Application No. 60/565781, filed April 27, 2005. Preferred alkanolamines for use in this reductive amination step include diethanolamine, monoethanolamine, di(isopropanol)amine, monoisopropanolamine, and the like. Dialkanolamines are generally more preferred as they result in a higher functionality product. Mixtures of dialkanolamines or of monoalkanolamines with dialkanolamines may also be used.

In a preferred method, as described in United States Provisional Application No. 60/565781, the reductive amination is conducted in the presence of a neutral rhodium-monodentate phosphite ligand complex. The neutral rhodium-monodentate phosphite ligand complex is conveniently prepared by contacting a neutral rhodium procatalyst with a stoichiometric excess of a monodentate phosphite ligand in the presence of a solvent such as dioxane, THF, cyclohexane, toluene, acetone, or o-xylene. The monodentate phosphite ligand can be characterized by the general formula P(OR)3, where each R is independently a carbon-containing substituent. Preferably, each R independently includes an alkyl, aryl, arylalkyl, arylalkoxy, or carbonylaryl group. Examples of representative monodentate phosphites include triphenylphosphite, tris(2,4-di-t-butylphenyl)phosphite, tri-o-tolylphosphite, tri-p- tolylphosphite, trimethylphosphite, triethylphosphite, tri-n-propylphosphite, tri-n-butylphosphite, tri-t-butylphosphite, tri-1-naρhthylphosphite, tri-2- naβ'Mn5>'Iβ'nόs^Jb[ite;^ι"^rif2;';¹-i^'biphenolphenylphosphite_J 2,2',4,4'-tetra-t-butyl-2,2^l-biphenol

2,4-di-t-butylphenylphosphite, and tribenzylphosphite.

The neutral rhodium procatalyst is a rhodium (I) catalyst precursor characterized by having its positive charge balanced by the negative charge of supporting bound ligands. For example, rhodium dicarbonyl acetonylacetate is a neutral rhodium procatalyst and, therefore, suitable. Other suitable examples of neutral rhodium procatalysts useful in preparing the complex include [Rh4(CO)i2], [Rh2(OAc)4], [RhXCaBUMacac)], [Rh(cyclooctadiene)(acac)], [(Rh(norbornene)2(acac)], [(Rh(norbornadiene)(acac)], and [Rh(acac)3] procatalysts. The amide, alkanolamine and catalyst complex are advantageously saturated with a stoichiometric excess of a mixture of CO and Bb and subject to an elevated temperature and pressure. The mole-to-mole ratio of CO:IΪ2 is suitably from about 1:1 to about 4:1. The reaction is carried out at a pressure of not less than 200 psi (1380 kPa) to as high as 3000 psi (20700 kPa). A preferred reaction temperature is from 20 to 120⁰C.

This reaction product contains a mono- or di(hydroxyalkyl)-substituted aminomethyl group at a site of carbon-carbon unsaturation in the fatty acid chain. If the fatty acid material contains more than one site of carbon-carbon unsaturation, multiple such aminomethyl groups are usually introduced. In addition, the amide will contain one or more alkanol groups attached to the amide nitrogen atom. Amides of this type advantageously have an average hydroxyl functionality of at least 2.5, especially at least 2.8 and more preferably at least 3.0.

Amide compounds having pendant hydroxyl-substituted ester groups. This type of amide compound is conveniently prepared by (1) forming an amide of an unsaturated fatty acid and a hydroxyl-containing primary or secondary amine, (2) epoxidizing the unsaturated fatty acid group and then (3) reacting the resulting epoxy group with a hydroxy acid or a hydroxy acid precursor. A hydroxyl-substituted group is formed, which is bound to the fatty acid chain through an ester linkage. The hydroxyl-containing primary or secondary amine is as described before.

The unsaturated fatty acid is preferably used in the form of a lower alkyl ester, which is conveniently prepared from vegetable oils or animal fats as described before. As before, mixtures of unsaturated fatty acids or of unsaturated fatty acids with saturated fatty acids can be used if desired. Conditions for the amide-forming reaction are suitably as described before. SIfS¹S¹OfCaI⁹WH-CaI¹¹IDOn unsaturation in the fatty acid chain are then epoxidized.

Conditions for epoxidizing carbon-carbon double bonds are well known, and commonly include the use of organic peresters, organic peracids or organic peroxides as reagents. It is preferred to epoxidize at least 50%, especially at least 80% and most preferably at least 95% of the carbon-carbon double bonds in the fatty acid groups.

The epoxide group is then reacted with a hydroxy acid or hydroxy acid precursor to introduce a hydroxy-substituted ester group onto the fatty acid chain. The ester group will be introduced at the locus of the epoxy group(s). The size of the pendant ester group will depend on the selection of the hydroxy acid. The pendant ester group preferably contains from 3 to 10, especially from 3 to 6 carbon atoms. Suitable hydroxy acids and esters include lactic acid, glycolic acid, 2,2- dimethylolprop ionic acid and the like. A hydroxy acid precursor that produces the hydroxy acid under the conditions of the reaction can be used instead or in conjunction with the hydroxy acid. Examples of such precursors are cyclic dianhydride dimers of the hydroxy acid, such as lactide and glycolide. These materials can be reacted with epoxy groups on the fatty acid amide using a wide range of catalysts and conditions as are commonly used in esterification reactions. Those conditions generally include an elevated temperature, suitably of from 80 to 200⁰C. Suitable catalysts include a wide range of acid and strong Lewis acid compounds, as these favor the ring-opening reaction of the hydroxyacid with the epoxide. When a hydroxy-substituted acid is used as a starting material, it may be desirable to conduct the reaction under a reduced pressure, to remove water as it forms during the condensation reaction.

This reaction product contains one or hydroxy-substituted ester groups pendant from the fatty acid portion of the amide. In addition, the product amide compound will contain one or more alkanol groups attached to the amide nitrogen atom. Amide compounds of this type advantageously have an average hydroxyl functionality of at least 2.0, especially at least 2.5 and more preferably at least 2.8.

Polyurethanes, especially rigid polyurethane foams, made using the foregoing amides The foregoing amide compounds are capable of reacting with an organic polyisocyanate to form a variety of polyurethanes. The types of polyurethane that can be prepared include rigid foam, flexible foam, molded elastomers, adhesives, sealants, and the like. The amide compound may be used as the sole polyol in the polyurethane- producing reaction, or may be combined with other polyols to achieve a desired set of properties in the polyurethane. The amide compound may be used as already "'dd'sfcriWff:"'¹ AKefSMf Slyϊ its equivalent weight may be increased by alkoxylating the hydroxyl groups with an alkylene oxide such as ethylene oxide, propylene oxide, butylene oxide or tetrahydrofuran.

Rigid polyurethane foam is an application of particular interest, as the amide compound of the invention can be prepared with a high hydroxyl functionality. In addition, the presence of nitrogen atoms in the amide causes it to be somewhat auto- catalytic, which is often a desirable trait for rigid foam polyols.

Rigid polyurethane foam is prepared using the amide compounds described above by forming a polyol component containing the amide compound, and contacting the polyol component with at least one polyisocyanate compound in the presence of a blowing agent and a surfactant. The resulting reaction mixture is subjected to conditions at which the polyol(s) react with the polyisocyanate and a gas is generated to expand the reacting mixture and form a foam.

The polyol component includes at least one amide compound as described. The amide compound may constitute the sole polyol in the polyol component. Alternatively, other polyols may be used in combination with the amide compound in order to achieve a desired reactivity or level of crosslinking, or otherwise to achieve a particular set of properties in the foam. When the amide compound is used with other polyols, the amide compound can constitute as Little as one percent by weight of the polyols. Preferably, the amide compound constitutes from 10 to 100% of the polyols (by weight), such as from 30 to 100%, from 50 to 100% or from 75 to 100% thereof.

Suitable polyols (other than the amide compound) are compounds having at least two isocyanate-reactive hydroxyl groups per molecule. The functionality of the individual polyols preferably ranges from about 2 to about 12, more preferably from about 2 to about 8. The hydroxyl equivalent weight of the individual polyols may range from about 31 to about 2000 or more. However, for preparing rigid polyurethanes, the equivalent weight of the polyols is selected in conjunction with that of the amide compound so the polyol component as a whole has an equivalent weight is from about 100 to 150, preferably from about 100 to 250 and especially from about 110 to about 150. Preferably, the hydroxyl equivalent weight of the individual polyols is from about 31 to about 500, more preferably from about 31 to about 250, even more preferably from about 31 to about 200.

Suitable additional polyols include compounds such as alkylene glycols (e.g., ethylene glycol, propylene glycol, 1,4-butane diol, 1,6-hexanediol and the like), glycol ethers (such as diethylene glycol, triethylene glycol, dipropylene glycol, tripropylene

"giy^:®eruie, trimethylolpropane, tertiary amine-containing polyols such as triethanolamine, triisopropanolamine, and ethylene oxide and/or propylene oxide adducts of ethylene diamine, toluene diamine and the like, polyether polyols, polyester polyols, and the like. Among the suitable polyether polyols are polymers of alkylene oxides such as ethylene oxide, propylene oxide and 1,2-butylene oxide or mixtures of such alkylene oxides. Preferred polyethers are polypropylene oxides or polymers of a mixture of propylene oxide and a small amount (up to about 12 weight percent) ethylene oxide. These preferred polyethers can be capped with up to about 30% by weight ethylene oxide. Polyester polyols are also suitable additional polyols. These polyester polyols include reaction products of polyols, preferably diols, with polycarboxylic acids or their anhydrides, preferably dicarboxylic acids or dicarboxylic acid anhydrides. The polycarboxylic acids or anhydrides may be aliphatic, cycloaliphatic, aromatic and/or heterocyclic and may be substituted, such as with halogen atoms. The polycarboxylic acids may be unsaturated. Examples of these polycarboxylic acids include succinic acid, adipic acid, terephthalic acid, isophthalic acid, trimellitic anhydride, phthalic anhydride, maleic acid, maleic acid anhydride and fumaric acid. The polyols used in making the polyester polyols preferably have an equivalent weight of about 150 or less, especially 75 or less, and include ethylene glycol, 1,2- and 1,3-propylene glycol, 1,4- and 2,3-butane diol, 1,6-hexane diol, 1,8-octane diol, neopentyl glycol, cyclohexane dimethanol, 2-methyl-l,3-propane diol, glycerine, trimethylol propane, 1,2,6-hexane triol, 1,2,4-butane triol, trimethylolethane, pentaerythritol, quinitol, mannitol, sorbitol, methyl glycoside, diethylene glycol, triethylene glycol, tetraethylene glycol, dipropylene glycol, dibutylene glycol and the like. Polycaprolactone polyols such as those sold by The Dow Chemical Company under the trade name "Tone" are also useful.

Preferred additional polyols are alkylene glycols, glycol ethers of up to about 75 equivalent weight, glycerine, trimethylolpropane, triethanolamine, triisopropanolamine, and poly (propylene oxide) polyols of up to about 200 equivalent weight.

The additional polyol (when used) may include a tertiary amine-containing polyol and/or an amine-functional compound. Such tertiary amine-containing polyols include, for example, triisopropanol amine, triethanolamine and ethylene and/or propylene oxide adducts of ethylene diamine, toluene diamine or aminoethylpiperazine having a molecular weight of up to about 800, preferably up to about 400. Tlϊe'"!kⁱήii^lae-ϊ«ellΘiϋal compound is a compound having at least two isocyanate- reactive groups, of which at least one is a primary or secondary amine group. Among these are monoethanolamine, diethanolamine, monoisopropanol amine, diisopropanol amine and the like, and aliphatic polyamines such as aminoethylpiperazine. Also included among these compounds are the so-called aminated polyethers in which all or a portion of the hydroxyl groups of a polyether polyol are converted to primary or secondary amine groups. Suitable such aminated polyethers are sold by Huntsman Chemicals under the trade name JEFFAMINE®. Typical conversions of hydroxyl to amine groups for these commercial materials range from 70 to 95%, and thus these commercial products contain some residual hydroxyl groups in addition to the amine groups. Preferred among the aminated polyethers are those having a weight per isocyanate-reactive group from 100 to 1700, especially from 100 to 250, and having from 2 to 4 isocyanate-reactive groups per molecule.

In order to impart toughness to the foam, a minor amount of a high (i.e. 800 or higher, preferably from 1500 to 3000) equivalent weight polyol may be added to the polyol component. This high equivalent weight polyol is preferably a polyether polyol having two to three hydroxyl groups per molecule. It more preferably is a poly(propylene oxide) that may be end-capped with up to 30% (by weight of the polyol) of poly (ethylene oxide). The high equivalent weight polyol may contain dispersed polymer particles. These materials are commercially known and are commonly referred to as "polymer polyols" (or, sometimes "copolymer polyols"). The dispersed polymer particles may be, for example, polymers of a vinyl monomer (such as styrene, acrylonitrile or styrene-acrylonitrile particles), polyurea particles or polyurethane particles. Polymer or copolymer polyols containing from about 2 to about 50% or more by weight dispersed polymer particles are suitable. When used, this polymer or copolymer polyol may constitute up to about 45%, preferably from about 5 to about 40%, of the weight of all isocyanate-reactive materials in the polyol component.

Suitable polyisocyanates include aromatic, cycloaliphatic and aliphatic isocyanates. Exemplary polyisocyanates include m-phenylene diisocyanate, toluene-2- 4- diisocyanate, toluene-2-6-diisocyanate, isophorone diisocyanate, 1,3- and/or 1,4- bis(isocyanatomethyl)cyclohexane (including cis- or trans-isomers of either), hexamethylene-l,6-diisocyanate, tetramethylene-l,4-dϋsocyanate, cyclohexane-1,4- dϋsocyanate, hexahydrotoluene diisocyanate, methylene bis(cyclohexaneisocyanate) (H12MDI), naphthylene-l,5-diisocyanate, methoxyphenyl-2,4-diisocyanate, diphenylmethane-4,4'-diisocyanate, 4,4'-biphenylene diisocyanate, 3,3'-dimethoxy-4,4'- bipΕe'riyf 'fllifiol^aa&^/δ^'-dimetihyl-^^-biphenyl dϋsocyanate, 3,3'-dimethyldiphenyl methane-4,4'-diisocyanate, 4,4',4"-triphenyl methane trϋsocyanate, a polymethylene polyphenylisocyanate (PMDI), toluene-2,4,6-trϋsocyanate and 4,4'- dimethyldiphenylmethane-2,2',5,5'-tetraisocyanate. Preferably the polyisocyanate is diphenylmethane-4,4'-dϋsocyanate, diphenylmethane-2,4'-dϋsocyanate, PMDI, toluene-2-4-diisocyanate, toluene-2-6-dϋsocyanate or mixtures thereof. Diphenylmethane-4,4'-dϋsocyanate, diphenylmethane-2,4'-dϋsocyanate and mixtures thereof are generically referred to as MDI, and all can be used. Toluene-2,4- dϋsocyanate, toluene-2,6-diisocyanate and mixtures thereof are generically referred to as TDI, and all can be used.

Derivatives of any of the foregoing polyisocyanate groups that contain biuret, urea, carbodiimide, allophonate and/or isocyanurate groups can also be used. These derivatives often have increased isocyanate functionalities and are desirably used when a more highly crosslinked product is desired. Suitable blowing agents include physical blowing agents such as various low- boiling chlorofluorocarbons, fruorocarbons, hydrocarbons and the like. Fluorocarbons and hydrocarbons having low or zero global warming and ozone-depletion potentials are preferred among the physical blowing agents. Chemical blowing agents that decompose or react under the conditions of the polyurethane-forming reaction are also useful.

By far the most preferred chemical blowing agent is water, which reacts with isocyanate groups to liberate carbon dioxide and form urea linkages. Water is preferably used as the sole blowing agent, in which case from 1 to 7, especially from 1.5 to 5 parts by weight water are typically used per 100 parts by weight of isocyanate- reactive materials (exclusive of water). Water may also be used in combination with a physical blowing agent, particularly a fluorocarbon or hydrocarbon blowing agent. In addition, a gas such as carbon dioxide, air, nitrogen or argon may be used as the blowing agent in a frothing process. It has been found that when the blowing agent includes at least one part of water per 100 parts by weight of isocyanate-reactive materials (exclusive of water), dimensionally stable foams can be produced even when the amide compound constitutes a high proportion, such as from 80 to 100% or from 90 to 100% by weight, of the isocyanate-reactive materials (exclusive of water).

A wide variety of silicone surfactants as are commonly used in making polyurethane foams can be used in making the foams in accordance with this invention. Examples of such silicone surfactants are commercially available under the •tr&ae»M?s^/ 'Feg*¹bttW^Th. Goldschmidt and Co.), Niax™ (GE OSi Silicones) and

Dabco™ (Air Products and Chemicals).

The reaction mixture may contain a wide variety of other additives as are conventionally used in making polyurethanes of various types. These include, for example, catalysts, blowing agents, surfactants, cell openers, fillers such as calcium carbonate; pigments and/or colorants such as titanium dioxide, iron oxide, chromium oxide, azo/diazo dyes, phthalocyanines, dioxazines and carbon black; reinforcing agents such as fiber glass, carbon fibers, flaked glass, mica, talc and the like, biocides, preservatives, antioxidants, flame retardants, and the like. Catalysts are particularly preferred additives, as are blowing agents and surfactants in cases where a cellular polyurethane is desired.

A catalyst is often used to promote the polyurethane-forming reaction. The selection of a particular catalyst package will vary somewhat with the particular application, the particular polyol(s) being used, and the other ingredients in the formulation. The catalyst may catalyze the "gelling" reaction between the polyol(s) and the polyisocyanate and/or, in many polyurethane foam formulation(s), the water/polyisocyanate (blowing) reaction which generates urea linkages and free carbon dioxide to expand the foam.

A wide variety of materials are known to catalyze polyurethane forming reactions, including tertiary amines, tertiary phosphines, various metal chelates, acid metal salts, strong bases, various metal alcoholates and phenolates and metal salts of organic acids. Catalysts of most importance are tertiary amine catalysts and organotin catalysts. Examples of tertiary amine catalysts include trimethylamine, triethylamine, N-methylmorpholine, N-ethylmorpholine, N,N-dimethylbenzylamine, N,N-dimethylethanolamine, N,N,N',N'-tetramethyl-l,4-butanediamine, N,N- dimethylpiperazine, l,4-diazobicyclo-2,2,2-octane, bis(dimethylaminoethyl)ether, trie thylene diamine and dimethylalkylamines where the alkyl group contains from 4 to 18 carbon atoms. Mixtures of these tertiary amine catalysts are often used. Examples of suitably commercially available surfactants include Niax™ Al (bis(dimethylaminoethyl)ether in propylene glycol available from GE OSi Silicones), Niax™ B9 (N,N-dimethylpiperazine and N-N- dime thylhexadecylamine in a polyalkylene oxide polyol, available from GE OSi Silicones), Dabco™ 8264 (a mixture of bis(dimethylaminoethyl)ether, triethylenediamine and dimethylhydroxyethyl amine in dipropylene glycol, available from Air Products and Chemicals), and Dabco™ 33LV (triethylene diamine in dipropylene glycol, available from Air Products and .

ILLΪ.:ιLlL.-«Jtc;ii .AiSi'^fJra (a proprietary tertiary amine/carboxylic salt and bis (2- dimethylaminoethy)ether in water and a proprietary hydroxyl compound, available from GE OSi Silicones); Niax™ A-300 (a proprietary tertiary amine/carboxylic salt and triethylenediamine in water, available from GE OSi Specialties Co.); Polycat™ 58 (a proprietary amine catalyst available from Air Products and Chemicals), Polycat™ 5 (pentamethyl diethylene triamine, available from Air Products and Chemicals) and Polycat™ 8 (N,N-dimethyl cyclohexylamine, available from Air Products and Chemicals).

Examples of organotin catalysts are stannic chloride, stannous chloride, stannous octoate, stannous oleate, dimethyltin dilaurate, dibutyltin dilaurate, other organotin compounds of the formula SnR_n(OR)4-n, wherein R is alkyl or aryl and n is 0- 2, and the like. Commercially available organotin catalysts of interest include Dabco™ T- 9 and T-95 catalysts (both stannous octoate compositions available from Air Products and Chemicals). Catalysts are typically used in small amounts, for example, each catalyst being employed from about 0.0015 to about 5% by weight of the high equivalent weight polyol.

A polyurethane is formed by bringing the components of the reaction mixture together under conditions that they react and form a polyurethane polymer. These reactions usually occur spontaneously upon mixing the polyisocyanate with the polyol component at room temperature or an elevated temperature. Accordingly, no special conditions are needed in most cases to form a polyurethane foam having good properties. The amount of polyisocyanate used is sufficient to provide an isocyanate index, i.e., 100 times the ratio of NCO groups to isocyanate-reactive groups in the reaction mixture (including those provided by water if used as a blowing agent), of from 85 to 300, especially from 95 to 150. The use of an isocyanate index above about 150 favors the formation of isocyanurate groups in the polymer.

The polyurethane foam may be formed as foam-in-place insulation, such as for refrigerators, freezers, coolers, ship hulls and the like. It can also be formed as boardstock foam.

The urethane-forming reactions (as well as the water-isocyanate reaction) often proceed well even at room temperature, and are usually exothermic enough to drive the polyurethane-forming reactions nearly to completion. ⁱThfe^l|;follό'wϊϊϊ¹g-^lfe'!s&iϊϊples are provided to illustrate the invention, but are not intended to limit the scope thereof. All parts and percentages are by weight unless otherwise indicated.

Example IA: Preparation of Amide Compound 9(10)-hydroxymethylstearate (400 parts by weight), diethanolamine (361.5 parts) and an 85% solution of potassium hydroxide in water (0.832 part) are placed in a vessel equipped with stirrer, nitrogen purge and condenser. The flask is heated to 85⁰C for 22 hours. The reaction mixture is cooled to 27⁰C and toluene is added to dissolve the amide product. The resulting toluene solution is washed three times with a 2% sodium bicarbonate solution in water. The toluene layer is then dried with anhydrous sodium sulfate and filtered. The dried toluene layer is evaporated under vacuum to remove the toluene. The resulting liquid product is stirred with methanol and filtered, followed by distillation of the methanol from the solution. 467 parts of a product (N,N-bis(hydroxyethyl) hydroxymethylstear amide) containing 12.16% by weight hydroxyl groups (~140 hydroxyl equivalent weight) is obtained. Example IB: Preparation of Rigid Polvurethane Foam

73.95 parts of N,N-bis(hydroxyethyl) hydroxymethylstear amide (from Example IA) are blended with 2.96 parts of a catalyst mixture, 1.59 parts of Niax™L-6900 silicone surfactant (GE silicones), 1.91 parts of water and 19.6 parts of HCFC-141b. The catalyst mixture includes pentamethylene diamine (Polycat™5 from Air Products and Chemicals), dimethylcyclohexyl amine (Polycat™8 from Air Products and Chemicals), and a potassium salt in diethylene glycol (PolyCat™46, from Air Products and Chemicals). The resulting mixture is combined at room temperature with 143.23 parts (1.15 index) of a polymeric MDI having a functionality of 2.7 and an isocyanate equivalent weight of 134, and allowed to rise freely and cure.

Gel time, measured from the time the polyol and polyisocyanate components are mixed until such time as the mixture forms strings when a spatula is touched to the mixture and pulled away, is 22 seconds. Tack free time is 23 seconds. Free rise density, measured on a 4" X 4" X 4" (10 cm X 10 cm X 10 cm) cube cut from the center of the cured foam, is 1.1 pounds/cubic foot (-17.6 kg/m³).

For comparison, a foam is made using the same formulation, except a 360-OH number poly(propylene oxide) polyol (Voranol® 360 from Dow Chemical) is used in replace of the polyol from Example IA. The gel time is 41 seconds and the tack time is 60 seconds, indicating a somewhat higher reactivity in the formulation of the invention. Density is 1.51 lb/ft³ (-24 kg/m³).

Claims

-WHRTIB^' Gmi'MKmS'f '

1. A process for preparing a polyurethane, comprising

(a) forming a reaction mixture by mixing a polyol or mixture thereof with a polyisocyanate compound, wherein the polyol or polyol mixture includes one or more compounds having (1) an amide group having at least one hydroxyl-containing organic group bonded to the nitrogen atom of the amide group and (2) a branched or straight chain C7-23 hydrocarbon group bonded directly to the carbonyl carbon of the amide group or ester group, wherein the C7-23 hydrocarbon group is substituted with at least one (i) (N-hydroxyalkyl) amino alkyl group or (ii) hydroxyl-containing ester group; and

(b) subjecting the reaction mixture to conditions such that it cures to form a polyurethane.

2. A polyurethane made by the process of claim 1.

3. The process of claim 1, wherein the reaction mixture further comprises a blowing agent and a surfactant, the polyol or mixture thereof has an average hydroxyl equivalent weight from 100 to 350 and an average hydroxyl functionality of at least 2.5, and the polyurethane is a rigid polyurethane foam.

4. The process of claim 3, wherein the C7-23 hydrocarbon group is substituted with at least one (N-hydroxyalkyl) aminoalkyl group.

5. The process of claim 4, wherein at least one hydroxyalkyl group is bonded to the nitrogen atom of the amide group.

6. The process of claim 5, wherein the hydroxyalkyl group bonded to the nitrogen atom of the amide group is a hydroxyethyl group.

7. The process of claim 6, wherein the N- (hydroxyalkyl) aminoalkyl group is an N- (hydroxy alkyl) aminomethyl group.

8. The process of claim 7, wherein the N-hydroxyalkyl aminomethyl group is a N- (hydroxyethyl) aminomethyl group or an N,N-bis(hydroxyethyl) aminomethyl group. ^ity.; iw-φrofee s^weiaim a, wherein two nyαroxyetnyi groups are oonαeα to tne nitrogen atom of the amide group.

10. The process of claim 9, wherein the amide compound is formed by first reacting an unsaturated fatty acid or ester thereof with an alkanolamine mixture containing diethanolamine and monoethanolamine to form an amide compound, and then reacting the amide compound with diethanolamine in the presence of carbon monoxide and hydrogen.

11. The process of claim 3, wherein the C7.23 hydrocarbon group is substituted with at least one hydroxyl-containing ester group.

12. The process of claim 11, wherein the amide compound is formed by reacting an epoxidized fatty acid or ester thereof with an aminoalcohol to form an amide compound containing at least one epoxide group, and then reacting a hydroxy acid or hydroxy acid precursor with at least one epoxide group of the amide compound to form the hydroxyl-containing ester group.

13. The process of claim 12, wherein the aminoalcohol is monoethanolamine, diethanolamine or a mixture of mono- and diethanolamine.

14. The process of claim 13 wherein the hydroxy acid or hydroxy acid precursor is one or more of lactic acid, glycolic acid, or 2,2-dimethylolpropionic acid.

15. A rigid polyurethane foam made according to the process of claim 1.

16. A process for preparing a rigid polyurethane foam, comprising (a) forming a reaction mixture by mixing a polyol or mixture thereof with a polyisocyanate compound, wherein the polyol or polyol mixture includes (I) one or more compounds having (1) an amide group having at least one hydroxyl-containing organic group bonded to the nitrogen atom of the amide group and (2) a branched or straight chain C7.23 hydrocarbon group bonded directly to the carbonyl carbon of the amide group or ester group, wherein the C7-23 hydrocarbon group is substituted with at least one (i) hydroxymethyl group, (ii) (N-hydroxyalkyl) amino alkyl group or (iii) hfdWxfT-βόήtaihiήi'^mr^t'gTovLp- and (II) at least one part by weight water per 100 parts by weight polyol or polyol mixture; and

(b) subjecting the reaction mixture to conditions such that it cures to form a rigid polyurethane foam.

17. The process of claim 16, wherein the C7-23 hydrocarbon group is substituted with at least one hydroxymethyl group.

18. The process of claim 17, wherein at least one hydroxyalkyl group is bonded to the nitrogen atom of the amide group.

19. The process of claim 18, wherein the hydroxyalkyl group bonded to the nitrogen atom of the amide group is a hydroxyethyl group.

20. The process of claim 19, wherein two hydroxyethyl groups are bonded to the nitrogen atom of the amide group.

21. The process of claim 20, wherein the amide compound is the reaction product of diethanolamine with a fatty acid or ester containing one or more hydroxymethyl groups.

22. A hydroxyl-containing amide compound that includes (1) an amide group having at least one hydroxyalkyl group bonded to the nitrogen atom of the amide group, and (2) a branched or straight chain C7-23 hydrocarbon group bonded directly to the carbonyl carbon of the amide group, wherein at least one hydroxyl-containing ester group is bonded to the C7-23 hydrocarbon group.

23. The amide compound of claim 22 which has an average of at least 3 hydroxyl groups per molecule.

24. A process for preparing a polyol compound having an amide group, comprising (a) forming an amide of (i) a primary or secondary amine compound having at least one hydroxyl-substituted organic group bonded directly or indirectly to the primary or secondary amino nitrogen and (ii) a fatty acid or ester thereof having at least one site of carbon-carbon unsaturation on the fatty acid chain; (b) epoxidizing at least one of saiα sites ot car Doii-eaFbϋn unsaturation to torm an epoxide group and (c) reacting the epoxide group with a hydroxy acid or hydroxy acid precursor to from a pendant, hydroxyl-substituted ester group.