WO2007009957A1 - Toughened compositon - Google Patents
Toughened compositon Download PDFInfo
- Publication number
- WO2007009957A1 WO2007009957A1 PCT/EP2006/064283 EP2006064283W WO2007009957A1 WO 2007009957 A1 WO2007009957 A1 WO 2007009957A1 EP 2006064283 W EP2006064283 W EP 2006064283W WO 2007009957 A1 WO2007009957 A1 WO 2007009957A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- epoxy resin
- weight
- composition according
- resin composition
- hardener
- Prior art date
Abstract
Description
Claims