WO2007003507A1 - Sulphonium salt initiators - Google Patents
Sulphonium salt initiators Download PDFInfo
- Publication number
- WO2007003507A1 WO2007003507A1 PCT/EP2006/063378 EP2006063378W WO2007003507A1 WO 2007003507 A1 WO2007003507 A1 WO 2007003507A1 EP 2006063378 W EP2006063378 W EP 2006063378W WO 2007003507 A1 WO2007003507 A1 WO 2007003507A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- acid
- alkyl
- compounds
- phenyl
- groups
- Prior art date
Abstract
Description
Claims