WO2006082166A1 - Functionalized esters, amides or urethanes of perfluorinated alcohols or amines as surface modifiers - Google Patents
Functionalized esters, amides or urethanes of perfluorinated alcohols or amines as surface modifiers Download PDFInfo
- Publication number
- WO2006082166A1 WO2006082166A1 PCT/EP2006/050508 EP2006050508W WO2006082166A1 WO 2006082166 A1 WO2006082166 A1 WO 2006082166A1 EP 2006050508 W EP2006050508 W EP 2006050508W WO 2006082166 A1 WO2006082166 A1 WO 2006082166A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- alkyl
- hydrogen
- tert
- butyl
- crc
- Prior art date
Abstract
Description
Claims