WO2006065471A1 - Flame retardant electrical wire - Google Patents
Flame retardant electrical wire Download PDFInfo
- Publication number
- WO2006065471A1 WO2006065471A1 PCT/US2005/042290 US2005042290W WO2006065471A1 WO 2006065471 A1 WO2006065471 A1 WO 2006065471A1 US 2005042290 W US2005042290 W US 2005042290W WO 2006065471 A1 WO2006065471 A1 WO 2006065471A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- polypropylene
- electrical wire
- block copolymer
- amount
- poly
- Prior art date
Abstract
Description
Claims