WO2006053777A1 - Crosslinkable poly(oxyalkylene)-containing polyamide prepolymers - Google Patents

Crosslinkable poly(oxyalkylene)-containing polyamide prepolymers Download PDF

Info

Publication number
WO2006053777A1
WO2006053777A1 PCT/EP2005/012438 EP2005012438W WO2006053777A1 WO 2006053777 A1 WO2006053777 A1 WO 2006053777A1 EP 2005012438 W EP2005012438 W EP 2005012438W WO 2006053777 A1 WO2006053777 A1 WO 2006053777A1
Authority
WO
WIPO (PCT)
Prior art keywords
radical
chloride
oxyalkylene
alkylene
poly
Prior art date
Application number
PCT/EP2005/012438
Other languages
French (fr)
Inventor
John Christopher Phelan
Original Assignee
Novartis Ag
Novartis Pharma Gmbh
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Novartis Ag, Novartis Pharma Gmbh filed Critical Novartis Ag
Priority to EP05807368A priority Critical patent/EP1817362B1/en
Priority to CA002577513A priority patent/CA2577513A1/en
Priority to JP2007541811A priority patent/JP2008520781A/en
Priority to AT05807368T priority patent/ATE482248T1/en
Priority to DE602005023768T priority patent/DE602005023768D1/en
Publication of WO2006053777A1 publication Critical patent/WO2006053777A1/en

Abstract

The present invention provides a water-soluble crosslinkable poly(oxyalkylene)­containing prepolymer. The crosslinkable poly(oxyalkylene)-containing copolymer prepolymer of the invention is prepared by reacting an amine-capped poly(oxyalkylene)­containing polyamide with a multifunctional compound having at least one one ethylenically unsaturated group and a function group coreactive with the capping amine groups of the amine-capped poly(oxyalkylene)-containing polyamide. The amine-capped poly(oxyalkylene)-containing polyamide is a copolymerization production of a mixture comprising: (a) at least one poly(oxyalkylene)diamine, (b) optionally at least one organic di­or poly-amine, (c) at least one dicarboxyl derivative, (d) optionally at least one polycarboxyl derivative, and (e) a carbodiimide. The crosslinkable poly(oxyalkylene)-containing prepolymer of the invention can find use in economically producing contact lenses which have improved thermal stability. In addition, the present invention provides method for making a medical device, preferably an ophthalmic device, more preferably a contact lens.

Description

Crosslinkable polv(oxyalkylene)-containinq polvamide prepolvmers
The present invention is related to radiation-curable prepolymers useful for making polymeric articles, preferably ophthalmic device, more preferably soft hydrogel contact lenses. In particular, the present invention is related to water-soluble radiation-curable poly(oxyalkylene)-containing poiyamides.
BACKGROUND
It is well known that contact lenses can be used for cosmetics and the correction of visual acuity. The ideal contact lens is one which is not only comfortable to wear for extended periods of time, but also easily and reproducibly manufactured at minimum cost in time and labor.
Great of efforts have been made to develop fast, highly efficient contact lens manufacturing process. Such processes are described in U.S. Patent Nos. 5,508,317, 5,583,163, 5,789,464 and 5,849,810 describe a fast, highly efficient contact lens manufacturing process, in which contact lenses are cast-molded under a spatial limitation of actinic radiation. A "spatial limitation of actinic radiation" refers to an act or process in which energy radiation in the form of rays is directed by means of, for example, a mask or screen or combinations thereof, to impinge, in a spatially restricted manner, onto an area having a well defined peripheral boundary. In this case, only the lens-forming material, which is in the unmasked area in the mold cavity is crosslinked, whereas the lens-forming material located in the masked area (behind the mask) remains uncrosslinked. The remarkably high accurate edge of the lens can be created without a positive connection between two reusable, precision mold halves. When using a water-soluble photo-crosslinkable prepolymer as a lens-forming material, a finished lens of optical quality can be produced in a mold within a few seconds without the necessity for subsequent extraction or finishing steps to the contact lens. Moreover, following the production of a lens, the reusable molds can be cleaned rapidly and effectively of the uncrosslinked prepolymer and other residues, using water, on account of the water- soluble lens formulations, and can be blown dried with air. With such manufacturing process, contact lenses can be manufactured at considerably low cost.
Various water-soluble crosslinkable prepolymers have been developed, such as, for example, those disclosed in U.S. Patent Nos. 5,508,317, 5,583,163, 5,665,840, 5,712,356, 5,789,464, 5,849,841 , 5,849,810, 6,165,408, 6,221 ,303, 6,303,687, 6,479,587, in U.S. Patent Application Publication No. 2004/0082680A1 , in EP 932,635, and in PCT patent application WO 2000/31150. Contact lenses produced from the above-described water- soluble crosslinkable prepolymers have advantageous properties such as a good compatibility with the human cornea resulting in a high wearing comfort and the absence of irritation and allergenic effects. However, contact lenses made from those water-soluble photo-crosslinkable prepolymers may not always posses combination of most desirable physical/mechanical properties, for example, such as tensile properties (stress at break, elongation at break, and modulus), water contents, biocompatibility, and thermostability, for the intended uses.
Accordingly, there is still a need for a new prepolymer for economically producing durable, thermostable, highly-elastic soft contact lenses with desired physical/mechanical properties.
SUMMARY OF THE INVENTION
In accomplishing the foregoing, there is provided, in accordance with one aspect of the present invention, a water-soluble, actinically-crosslinkable poly(oxyalkylene)-containing prepolymer, which is the reaction product of a poly(oxyalkylene)-containing polyamide having terminal amine groups and a multifunctional compound having at least one ethylenically unsaturated group and a functional group coreactive with the amine groups of the polyamide, wherein the poly(oxyalkylene)-containing polyamide is a copolymerization product of a mixture comprising (a) at least one amine-capped polyalkylene glycol, (b) optionally at least one organic di- or poly-amine, (c) at least one di-carboxyl derivative, (d) optionally at least one polycarboxyl derivative, and (e) optionally a carbodiimide.
In another aspect, the present invention provides a polymer which is a product of actinically- crosslinking of an above-described water-soluble actinically-crosslinkable poly(oxyalkylene)- containing prepolymer of the invention in the presence or preferably in the absence of one or more additional vinylic monomers.
In a further aspect, the present invention provides a medical device, preferably an ophthalmic device, more preferably a contact lens, which is obtained by actinically crosslinking an above-described water-soluble crosslinkable poly(oxyalkylene)-containing prepolymer of the invention in the presence or preferably in the absence of one or more additional vinylic monomers.
In another further aspect, the present invention provides a method for producing an ophthalmic device, the method comprising the steps of: a) introducing an above-described water-soluble crosslinkable poly(oxyalkylene)-containing prepolymer of the invention, which is liquid or readily meltable at room temperature, and which is essentially free from solvents, into a mold, in the presence or preferably in the absence of one or more additional vinylic monomers, and optionally in the presence of a photo-initiator, b) crosslinking by actinic radiation the water-soluble crosslinkable prepolymer, and c) opening the mold so that the article can be removed from the mold.
In a still further aspect, the present invention provides a method for producing an ophthalmic device, the method comprising the steps of: a) introducing an aqueous solution of an above- described water-soluble crosslinkable poly(oxyalkylene)-containing prepolymer of the invention, in the presence or preferably in the absence of one or more additional vinylic monomers, and optionally in the presence of a photo-initiator, into a mold; b) crosslinking by actinic radiation the water-soluble crosslinkable prepolymer, and c) opening the mold so that the article can be removed from the mold.
These and other aspects of the invention will become apparent from the following description of the preferred embodiments taken in conjunction with the following drawings. As would be obvious to one skilled in the art, many variations and modifications of the invention may be effected without departing from the spirit and scope of the novel concepts of the disclosure.
DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS
Reference now will be made in detail to the embodiments of the invention. It will be apparent to those skilled in the art that various modifications and variations can be made in the present invention without departing from the scope or spirit of the invention. For instance, features illustrated or described as part of one embodiment, can be used on another embodiment to yield a still further embodiment. Thus, it is intended that the present invention cover such modifications and variations within the scope of the appended claims and their equivalents. Other objects, features and aspects of the present invention are disclosed in or are obvious from the following detailed description. It is to be understood by - A -
one of ordinary skill in the art that the present discussion is a description of exemplary embodiments only, and is not intended as limiting the broader aspects of the present invention.
Unless defined otherwise, all technical and scientific terms used herein have the same meaning as commonly understood by one of ordinary skill in the art to which this invention belongs. Generally, the nomenclature used herein and the laboratory procedures are well known and commonly employed in the art. Conventional methods are used for these procedures, such as those provided in the art and various general references. Where a term is provided in the singular, the inventors also contemplate the plural of that term. The nomenclature used herein and the laboratory procedures described below are those well known and commonly employed in the art.
In one aspect, the present invention relates to a water-soluble actinically-crosslinkable poly(oxyalkylene)-containing prepolymer, which is obtained by introducing ethylenically unsaturated groups into a poly(oxyalkylene)-containing polyamide with terminal amine groups (or amine-capped poly(oxyalkylene)-containing polyamide).
Exemplary ethylenically unsaturated groups include without limitation acryloyl, methacryloyl, allyl, vinyl, styrenyl, or other C=C containing groups.
A "prepolymer" refers to a starting polymer which can be cured (e.g., crosslinked and/or polymerized) actinically or thermally or chemically to obtain a crosslinked and/or polymerized polymer having a molecular weight much higher than the starting polymer. A "actinically- crosslinkable prepolymer" refers to a starting polymer which can be crosslinked upon actinic radiation to obtain a crosslinked polymer having a molecular weight much higher than the starting polymer. Examples of actinic radiation are UV irradiation, ionized radiation (e.g. gamma ray or X-ray irradiation), microwave irradiation, and the like.
As used herein, "actinically" in reference to curing or polymerizing of a polymerizable composition or material means that the curing (e.g., crosslinked and/or polymerized) is performed by actinic irradiation, such as, for example, UV irradiation, ionized radiation (e.g. gamma ray or X-ray irradiation), and microwave irradiation. In accordance with the present invention, a poly(oxyalkylene)-containing polyamide with terminal amine groups must contain poly(oxyalkylene) segments, each of which is a divalent radical of
-(Ri-O)n-(R2-O)m-(R3 -O)p- in which R1, R2, and R3, independently of one other, are each linear or branched C2-C4- alkylene or hydroxy-substituted C2-C8 alkylene radical, and n, m and p, independently of one another, are each a number from 0 to 500, wherein the sum of (n+m+p) is 5 to 1000. Each
O
Il i poly(oxyalkylene) segment is linked through an amide linkage (or bond) (-C-N — ) to at least one segment in the poly(oxyalkylene)-containing polyamide with terminal amine groups of the invention. It is discovered that a material with amide linkages has improved thermal stability as compared to similar materials containing urea or urethane linkages. The improved thermal stability of a poly(oxyalkylene)-containing polyamide preferably is characterized by its capability to endure repeated sterilization without undergoing significant changes (e.g., more than about 5% of changes) in material properties (e.g., tensile properties, lens diameter, water content, etc.).
Preferably, an amine-capped poly(oxyalkylene)-containing polyamide of the invention is a branched copolymer in which each of its polymeric chains including main and side chains are terminated with one capping group which can be an primary or secondary amine group.
An amine-capped poly(oxyalkylene)-containing polyamide of the invention is a copolymerization product of a mixture comprising (a) at least one amine-capped polyalkylene glycol (or poly(oxyalkylene), (b) optionally at least one organic di- or poly-amine, (c) at least one di-carboxyl derivative, (d) optionally at least one polycarboxyl derivative, and (e) optionally a carbodiimide. Preferably, the amine-capped poly(oxyalkylene)-containing copolymer is a copolymerization product of a mixture comprising (a) at least one poly(oxyalkylene)diamine, (b) at least one organic poly-amine, (c) at least one di-carboxyl derivative, (d) optionally at least one polycarboxyl derivative, and (e) optionally a carbodiimide. More preferably, the amine-capped poly(oxyalkylene)-containing polyamide is a copolymerization product of a mixture comprising (a) at least one poly(oxyalkylene)diamine, (b) at least one organic poly-amine (preferably triamine), (c) at least one di-carboxyl derivative, (d) at least one polycarboxyl derivative (preferably tri- carboxyl derivative), and (e) optionally a carbodiimide. In accordance with the present invention, a "poly(oxyalkylene)diamine" or "amine-capped poly(oxyalkylene)" refers to a compound of formula
CG-(Ri -O)n- (R2-O)m-(R3 -O)p-CG' (1 ) wherein CG and CG' independently of each other are a primary or secondary amino (amine) group, or an amino-Ci-C12 alkyl, R1, R2, and R3, are defined above. The sum of (n+m+p) is preferably from 8 to 200, more preferably from 8 to 100. Examples of preferred compounds of formula (1 ) include the family of poly(oxyalkylene)amines with various average molecular weights, e.g. so-called Jeffamines® having an average molecular weight of, for example, approximately from 200 to 5000.
In accordance with the present invention, an organic diamine is a compound with two amino groups (primary and/or secondary). An organic diamine can be a linear or branched C2-C24 aliphatic diamine, a C5-C24 cycloaliphatic or aliphatic-cycloaliphatic diamine, or a C6-C24 aromatic or alkyl-aromatic diamine. A preferred organic diamine is bis(hydroxyethylene)ethylenediamine (BHEEDA) and isophorone diamine.
In accordance with the present invention, an organic polyamine is a compound of formula
HN- B1 1- NH
R4 R4' (2), wherein R4 and R4 1 independently of each other are hydrogen or unsubstituted or substituted C1-C6 alkyl or together are a direct, ring-forming bond, and B1' is a bivalent aliphatic, cycloaliphatic, aliphatic-cycloaliphatic, aromatic or araliphatic hydrocarbon radical that is interrupted by at least one bivalent amine group ( — NH — ) or has a primary or secondary amine group (such as, e.g., -NH2 or — NHR1 wherein R is C1-C6 alkyl, hydroxy-substituted C1-C6 alkyl or C1-C4 alkoxy-substituted C1-C6 alkyl).
Each of R4 and R4' independently of the other is hydrogen, unsubstituted CrC6alkyl, hydroxy-substituted CrC6alkyl or C1-C4alkoxy-substituted CrCδalkyl. Each of R4 and R4' independently of the other is preferably hydrogen, unsubstituted CrCβalkyl, or hydroxy- substituted CrCialkyl, more preferably hydrogen, CrC2alkyl or hydroxy-CrC2alkyl, and most preferably hydrogen. The radicals R4 and R4' may be different or, preferably, identical. The radical B1' may be, for example, linear or branched C3-C24alkylene or unsubstituted or Ci-C4alkyl-substituted C6-C10arylene, C7-C18aralkylene, Ce-C^arylene-C^alkylene-Ce-Cio- arylene, C3-C8cycloalkylene, Ca-Cβcycloalkylene-d-Cealkylene, C3-C8cycloalkylene-C1-C2- alkylene-C3-C8cycloalkylene or Ci-Cβalkylene-Cs-Cβcycloalkylene-Ci-Cealkylene, each of which is interrupted by at least one, preferably from 1 to 3, more preferably 1 or 2 groups of - NH-.
Examples of polyamines of formula (2) are symmetrical or asymmetrical dialkylenetriamines or trialkylenetetramines or cycloaliphatictriamine. Preferred polyamines include without limitation diethylenetriamine, N-2'-aminoethyl-1 ,3-propylenediamine, N,N-bis(3-aminopropyl)- amine, N,N-bis(6-aminohexyl)amine and triethylenetetramine.
The component (b) can be absent or preferably present in the reaction mixture for preparing an amine-capped poly(oxyalkylene)-containing copolymer. Where the component (b) is present, it comprise preferably at least one organic polyamine and optionally an organic diamine, more preferably at least one triamine and optionally an organic diamine.
In accordance with the invention, a di- or polycarboxyl derivative preferably is an organic
O
Il compound with two or more groups of — C-D, wherein D is halide (i.e., carbonyl chloride or acid chloride group), OH (i.e., carboxylic acid group), or alkoxyl or cycloakoxyl or aralkoxyl (i.e., ester group).
In accordance with the present invention, a dicaboxyl derivative can be a derivative (i.e., carbonyl chloride, carboxylic acid or ester) of a linear or branched C3-C24 aliphatic dicarboxylic acid, a C5-C24 cycloaliphatic or aliphatic-cycloaliphatic dicarboxylic acid, a C6-C24 aromatic or araliphatic dicarboxylic acid, or a dicarboxylic acid which contains amino or imido groups or N-heterocyclic rings. Examples of suitable aliphatic dicarboxylic acids are: malonic acid, dimethylmalonic acid, succinic acid, octadecylsuccinic acid, pimelic acid, adipic acid, trimethyladipic acid, sebacic acid, azelaic acid, and dimeric acids (dimerisation products of unsaturated aliphatic carboxylic acids, such as oleic acid). Examples of suitable cycloaliphatic dicarboxylic acids are: 1 ,3-cyclobutanedicarboxylic acid, 1 ,3- cyclopentanedicarboxylic acid, 1 ,3- and 1 ,4-cyclohexanedicarboxylic acid, 1 ,3- and 1 ,4- dicarboxylmethylcyclohexane, 4,4'-dicyclohexyldicarboxylic acid. Examples of suitable unsaturated dicarboxylic acids are: maleic acid, fumaric acid, methylmaleic acid or itaconic acid. Examples of suitable aromatic dicarboxylic acids are: terephthalic acid, isophthaiic acid, o-phthalic acid, 1 ,3-, 1 ,4-, 2,6- or 2,7-naphthalenedicarboxylic acids, 4,4'- diphenyldicarboxylic acid, 4,4'-diphenylsulphone-dicarboxylic acid, 1 ,1 ,3-trimethyl-5-carboxyl- 3-(p-carboxyphenyl)-indane, 4,4'-diphenyl ether-dicarboxylic acid, bis-p-(carboxylphenyl)- methane.
In accordance with the present invention, a polycarboxyl derivative is a compound comprising at least three carbonyl halide or carboxylic acid or ester groups. A polycarboxyl derivative can be a linear or branched C3-C24 aliphatic polycarboxyl derivative, a C5-C45 cycloaliphatic or aliphatic-cycloaliphatic polycarboxyl derivative, or a C6-C24 aromatic or araliphatic polycarboxyl derivative. Preferably, a polycarboxyl derivative is a C6-C45 cycloaliphatic or aliphatic-cycloaliphatic compound containing 3-6 carbonyl halide or carboxylic acid or ester groups. Most preferably, a polycarboxyl derivative is a C6-C45 cycloaliphatic or aliphatic-cycloaliphatic compound containing 3 carbonyl halide or carboxylic acid or ester groups. Examples of aliphatic tricarboxylic acids are aconitic acid and citric acid. Examples of cycloaliphatic tricarboxylic acids are 1 ,3,5-cyclohexanetricarboxylic acid and 1 ,3,5-trimethyl-1 ,3,5-cyclohexanetricarboxylic acid. Examples of aromatic tricarboxylic acids are 1 ,2,3 benzene tricarboxylic acid, 1 ,2,4 benzene tricarboxylic acid, and 1 ,3,5 benzene tricarboxylic acid (trimesic acid).
Preferred di- or polyacid halides (i.e., di- or polycarbonyl chloride) are triacid chlorides, triacid bromides, diacid chlorides and diacid bromides. Examples of diacid chlorides are fumaryl chloride, suberoyl chloride, succinyl chloride, phthaloyl chloride, isophthaloyl chloride, terephthaloyl chloride, sebacoyl chloride, adipoyl chloride, trimethyladipoyl chloride, azelaoyl chloride, dodecanedioic acid chloride, succinic chloride, glutaric chloride, oxalyl chloride, and dimer acid chloride. Examples of triacid chlorides are trimesoyl chloride, cyclohexane-1 ,3,5- tricarbonyl chloride, trimer acid chloride and the like.
In a preferred embodiment, the di- or polycarboxyl derivative is a di- or polycarbonyl halide (or di- or polyacid halide, or di- or polyacyl halide).
In another preferred embodiment, the di- or polycarboxyl derivative is a di- or polycarboxylic acid. In this preferred embodiment, the reaction mixture for making an amine-capped poly(oxyalkylen)-containing polyamide of the invention preferably comprises a carbodiimide, which can couple carboxyls to amines, resulting in formation of a amide.
When a carbodiimide is used in the coupling of a carboxyl and an amine, no cross-bridge is formed between the molecules being coupled. The carbodiimide facilitates amide formation. Examples of carbodiimides are 1-ethyl-3-(3-dimethylaminopropyl)carbodiimide (EDC), N1N'- dicyclohexylcarbodiimide (DCC), 1-cylcohexyl-3-(2-morpholinoethyl)carbodiimide, diisopropyl carbodiimide, or mixtures thereof. N-hydroxysuccinimide (NHS) or N-hydroxysulfo- succinimide may be desirably included in carbodiimide (e.g., EDC)-mediated coupling reaction to improve coupling (conjugation) efficiency. EDC couples NHS to carboxyls, resulting in an NHS-activated site on a molecule. The formed NHS-ester can react with amines to form amides.
Preferably, a resin-bound carbodiimide is used to coupling carboxyls and amines. The resin- bound reagents are easily removed by filtration or decanting and as such, purification of reaction products is simplified. It is preferably that resin-bound 1 -hydroxybenzotriazole catalyst is used together with a resin-bound carbodiimide for making an amine-capped poly(oxyalkylene)-containing polyamide of the invention.
Where a carbodiimide is present in a reaction mixture for making an amine-capped poly(oxyalkylene)-containing polyamide of the invention, an amino acid can also be added into the reaction mixture.
Ethylenically unsaturated groups can be introduced into an amine-capped poly(oxyalkylene)- containing polyamide by reacting it with a multifunctional compound having at least one ethylenically unsaturated group and a functional group coreactive with capping amine groups, according to any methods known to a person skilled in the art, for example, by reacting it with an acryloyl chloride-containing compound or a methacryloyl chloride- containing compound, or by coupling it with a compound comprising at least one ethylenically unsaturated group and a carboxylic acid group in the presence of a carbodiimide.
One embodiment of a crosslinkable prepolymer of the invention is illustrated in formula (4)
CP-(Q)q (4) wherein q is an integer of 2 or higher, preferably 3 or higher, Q is an organic radical that comprises at least one ethylenically unsaturated group, CP is a multivalent linear or branched copolymer fragment comprising segments A, A1, T, and optionally segments G, wherein:
A is the bivalent radical of — (R-|— O)n- (R2~ O)m— (R3~ O)p~. wherein R1, R2, R3, n, m, and p each are defined above;
G is a linear or branched C3-C24 aliphatic trivalent radical, a C5-C45 cycloaliphatic trivalent radical, a C5-C45 aliphatic-cycloaliphatic trivalent radical, or a C3-C24 aromatic or araliphatic trivalent radical;
A1 is a linear or branched C2-C24 aliphatic bivalent radical, a C5-C24 cycloaliphatic or aliphatic-cycloaliphatic bivalent radical, a C6-C24 araliphatic bivalent radical, or aliphatic-heterocyclic bivalent radical, each of which is interrupted by at least one group of formula — NRm— in which Rm is hydrogen, a radical Q mentioned above or a radical of formula
O it — C-CP1- Q (4') wherein Q is as defined above, and CP' is a bivalent copolymer fragment comprising one or more segments selected from the group consisting of A, A1, T and G; T is a bivalent radical of formula
RA C N
O (5), wherein RA is hydrogen, an unsubstituted C1-C6 alkyl, or a substituted C1-C6 alkyl; provided that in the copolymer fragments CP and CP' a segment A is linked to a segment A1 or G through a segment T; provided that the C atom of -CO— is bonded to a segment A1 or G when Rm is a radical of formula (4'); provided that Q is linked to the copolymer fragment CP or CP' through a segment T.
Q is, for example, an ethylenically unsaturated, copolymerizable radical that is bonded to the copolymer fragment CP in a suitable manner, for example, through a urethane linkage, a urea linkage, preferably an amide linkage. The radical Q corresponds, for example, to a radical R5 which is an olefinically unsaturated copolymerizable radical having 2 to 24 carbon atoms which may be further substituted, or to a radical of formula -(NH )r— Q1 or -Q-Q1, wherein Q1 is a radical of formula
Figure imgf000012_0001
o
Il -Z" — NH-C-R5 (6e), and wherein
Z is linear or branched C2-C12alkylene,
R5 is an olefinically unsaturated copolymerisable radical having from 2 to 24 carbon atoms which may be further substituted,
W is a C2-C12alkylene radical, phenylene radical or C7-C12aralkylene radical, each of R6 and R6' independently of each other is hydrogen, C1-C4BlKyI or halogen,
R7 is a bivalent aliphatic, cycloaliphatic, aliphatic-cycloaliphatic, aromatic or araliphatic hydrocarbon radical,
R8 is hydrogen or CrC4alkyl, each of alk and alk1 independently of the other is a linear or branched CrC12alkylene radical, each of r and s independently of each other is the number 0 or 1 ,
Z" is d-Cealkylene and
P1 and P1' independently of each other are a radical of formula -(NH ^-Q1 Or -O-Q1.
Z is preferably linear or branched C2-C8alkylene, more preferably linear C2-C6alkylene and most preferably linear C2-C4alkylene. In a preferred embodiment of the invention, Z is 1 ,3- propylene or, especially, 1 ,2-ethylene. Suitable substituents on the olefinic C2-C24 radical R5 are, for example, C1-C4BIkOXy, halogen, phenyl or carboxy.
R5 is, for example, a radical of formula
Figure imgf000013_0001
wherein t is the number 0 or 1 , R9 is hydrogen, C1-C4BlKyI or halogen, each of R10 and R11 independently of the other is hydrogen, Ci-C4alkyl, phenyl, carboxy or halogen, and
Z' is linear or branched CrC12alkylene or unsubstituted or CrC4alkyl- or CrC4alkoxy- substituted phenylene or C7-C12aralkylene.
When 71 is a phenylene radical, it is, for example, unsubstituted or methyl- or methoxy- substituted 1 ,2-, 1 ,3- or 1 ,4-phenylene. Preferably, Z' as a phenylene radical is 1 ,3- or 1 ,4- phenylene.
When Z' is an aralkylene radical, it is, for example, unsubstituted or methyl- or methoxy- substituted benzylene, wherein the methylene group is bonded to the amine nitrogen in each case. Preferably, Z as an aralkylene radical is the 1 ,3- or 1 ,4-phenylenemethylene radical, wherein the methylene group is bonded to the amine nitrogen -NH- in each case.
Z' is preferably unsubstituted or methyl- or methoxy-substituted phenylene or phenylene- methylene or C^C^alkylene, more preferably 1 ,3- or 1 ,4-phenylene or CrCealkylene, especially d^alkylene and most preferably methylene. t is the number 1 or, preferably, the number 0.
R9 is preferably hydrogen, methyl or chlorine and most preferably hydrogen or methyl.
Each of R10 and R11 independently of the other is preferably hydrogen, carboxy, chlorine, methyl or phenyl. In a preferred embodiment of the invention, R10 is hydrogen, chlorine, methyl or phenyl and R11 is hydrogen or carboxy. Most preferably, R10 and R11 are each hydrogen. Examples of suitable radicals R5 are vinyl, 2-propenyl, allyl, 2-butenyl, o-, m- or p-vinyl- phenyl, styryl, 2-carboxyvinyl, 2-chloro-2-carboxyvinyl, 1 ,2-dichloro-2-carboxyvinyl, 1 ,2- dimethyl-2-carboxyvinyl and 2-methyl-2-carboxyvinyl.
Especially preferred radicals R5 correspond to formula (7) wherein t is 0, R9 is hydrogen or methyl, R10 is hydrogen, methyl, chlorine or phenyl and Rn is hydrogen or carboxy.
Other especially preferred radicals R5 correspond to the above formula (7) wherein t is 1 , Z' is 1 ,3- or 1 ,4-phenylene or CrC6alkylene, especially CVCalkylene, R9 is hydrogen or methyl and R10 and Rn are each hydrogen. G
Z" is preferably CrC4alkylene, especially methylene or 1 ,1-dimethylmethylene.
One group of suitable radicals Q corresponds to the above formula -(NH ) — Q1 wherein r is 0 and Qi is a radical of the above formula (6a) wherein s is 0 and for R5 the meanings and preferences given above apply.
A second group of suitable radicals Q corresponds to the above formula -(NH Jn-Q1 wherein r is 1 and Q1 is a radical of the above formula (6a) wherein s is 0 and for R5 and Z the meanings and preferences given above apply.
A further group of suitable radicals Q corresponds to the above formula -(NH Jr-Q1 wherein r is 1 and Q1 is a radical of the above formula (6a) wherein s is 1 and for R5 and Z the meanings and preferences given above apply.
A further group of suitable radicals Q corresponds to the above formula -(NH ) — Q1 wherein r is 0 and Q1 is a radical of the above formula (6e) wherein for R5 and Z" the meanings and preferences given above apply.
In formulae (6b) and (6c), W is preferably a C2-C6alkylene radical or a 1 ,3- or 1 ,4-phenylene radical and most preferably a C2-C3alkylene radical. Each of R6 and R6' independently of the other is preferably hydrogen, methyl or chlorine. Most preferably, each of R6 and R6 1 independently of the other is hydrogen or methyl. In formula (6d), R7 is, for example, linear or branched C3-C18alkylene or unsubstituted or C^alkyl- or Ci-C4alkoxy-substituted C6-C10arylene, C7-C18aralkylene, C6-C10arylene- Ci-C2alkylene-C6-C10arylene, C3-C8cycloalkylene, C3-C8cycloalkylene-Ci-C6alkylene, C3-C8cycloalkylene-CrC2alkylene-C3-C8cycloalkylene, CrC6alkylene-C3-C8cycloalkylene- Ci-C6alkylene or an aliphatic-heterocyclic radical comprising at least one hydantoin group.
R7 as alkylene is preferably a linear or branched C3-C14alkylene radical, more preferably a linear or branched C4-C12alkylene radical and most preferably a linear or branched C6-C10- alkylene radical. Some preferred alkylene radicals are 1 ,4-butylene, 2,2-dimethyl-1 ,4- butylene, 1 ,5-pentylene, 2,2-dimethyl-1 ,5-pentylene, 1 ,6-hexylene, 2,2,3- or 2,2,4-trimethyl- 1 ,5-pentylene, 2,2-dimethyl-i ,6-hexylene, 2,2,3- or 2,2,4- or 2,2,5-trimethyl-1 ,6-hexylene, 2,2-dimethyl-1 ,7-heptylene, 2,2,3- or 2,2,4- or 2,2,5- or 2,2,6-trimethyl-1 ,7-heptylene, 1 ,8- octylene, 2,2-dimethyl-1 ,8-octylene and 2,2,3- or 2,2,4- or 2,2,5- or 2,2,6- or 2,2,7-trimethyl- 1 ,8-octylene.
When R7 is arylene, it is, for example, naphthylene or especially phenylene, each of which may be substituted, for example, by d-C4alkyl or by CrC4alkoxy. Preferably, R7 as arylene is 1 ,3- or 1 ,4-phenylene that is substituted by CrC4alkyl or by CrC4alkoxy in the ortho- position to at least one linkage site. Examples of substituted arylene are 1 -methyl-2,4- phenylene, 1 ,5-dimethyl-2,4-phenylene, 1-methoxy-2,4-phenylene and 1-methyl-2,7-naph- thylene.
R7 as aralkylene is preferably naphthylalkylene and most preferably phenylalkylene. The alkylene group in aralkylene contains preferably from 1 to 12, more preferably from 1 to 6 and most preferably from 1 to 4 carbon atoms. Most preferably, the alkylene group in aralkylene is methylene or ethylene. Some examples are 1 ,3- or 1 ,4-benzylene, naphth-2-yl- 7-methylene, 6-methyl-1 ,3- or -1 ,4-benzylene and 6-methoxy-1 ,3- or -1 ,4-benzylene.
When R7 is cycloalkylene, it is preferably C5-C6cycloalkylene and most preferably cyclo- hexylene that is unsubstituted or substituted by methyl. Some examples are 1 ,3-cyclo- butylene, 1 ,3-cyclopentylene, 1 ,3- or 1 ,4-cyclohexylene, 1 ,3- or 1 ,4-cycloheptylene, 1 ,3- or 1 ,4- or 1 ,5-cyclooctylene, 4-methyl-1 ,3-cyclopentylene, 4-methyl-1 ,3-cyclohexylene, 4,4- dimethyl-1 ,3-cyclohexylene, 3-methyl- or 3,3-dimethyl-1 ,4-cyclohexylene, 3,5-dimethyl-1 ,3- cyclohexylene and 2,4-dimethyl-1 ,4-cyclohexylene. When R7 is cycloalkylene-alkylene, it is preferably cyclopentylene-CrC4alkylene and espe¬ cially cyclohexylene-Ci-C4alkylene, each unsubstituted or mono- or poly-substituted by Ci-C4alkyl, especially methyl. More preferably, the group cycloalkylene-alkylene is cyclo- hexylene-ethylene and, most preferably, cyclohexylene-methylene, each unsubstituted or substituted in the cyclohexylene radical by from 1 to 3 methyl groups. Some examples are cyclopent-1 -yl-3-methylene, 3-methyl-cyclopent-1 -yl-3-methylene, 3,4-dimethyl-cyclopent-1 - yl-3-methylene, 3,4,4-trimethyl-cyclopenM -yl-3-methylene, cyclohex-1-yl-3- or -4-methylene, 3- or 4- or S-methyl-cyclohex-i-yl-S- or -4-methylene, 3,4- or S.δ-dimethyl-cyclohex-i-yl-S- or -4-methylene and 3,4,5- or 3,4,4- or S.δ.δ-trimethyl-cyclohex-i-yl-S- or -4-methylene.
When R7 is alkylene-cycloalkylene-alkylene, it is preferably d^alkylene-cyclopentylene-Cr C4alkylene and especially Ci-C4alkylene-cyclohexylene-C1-C4alkylene, each unsubstituted or mono- or poly-substituted by CrC4alkyl, especially methyl. More preferably, the group alkylene-cycloalkylene-alkylene is ethylene-cyclohexylene-ethylene and, most preferably, is methylene-cyclohexylene-methylene, each unsubstituted or substituted in the cyclohexylene radical by from 1 to 3 methyl groups. Some examples are cyclopentane-1 ,3-dimethylene, 3- methyl-cyclopentane-1 ,3-dimethylene, 3,4-dimethyl-cyclopentane-i ,3-dimethylene, 3,4,4-tri- methyl-cyclopentane-1 ,3-dimethylene, cyclohexane-1 ,3- or -1 ,4-dimethylene, 3- or 4- or 5- methyl-cyclohexane-1 ,3- or -1 ,4-dimethylene, 3,4- or 3,5-dimethyl-cyclohexane-1 ,3- or -1 ,4- dimethylene, 3,4,5- or 3,4,4- or 3,5,5-trimethyl-cyclohexane-1 ,3- or -1 ,4-dimethylene.
R7 as Ca-Cacycloalkylene-CrCalkylene-Ca-Cβcycloalkylene or CVdoarylene-CrCsalkylene- C6-Ci0arylene is preferably C5-C6cycloalkylene-methylene-C5-C6cycloalkylene or phenylene- methylene-phenylene, each of which may be unsubstituted or substituted in the cycloalkyl or phenyl ring by one or more methyl groups.
When R7 is an aliphatic-heterocyclic radical containing hydantoin groups, it may correspond, for example, to formula
Figure imgf000016_0001
Figure imgf000017_0001
wherein R12 and R12' are each CrC6alkylene, preferably C2-C4alkylene and especially C2-C3alkylene, R13, R13', R14 and R14' are each independently of the others hydrogen, d-C6alkyl or C5-C7cycloalkyl, preferably are each independently of the others hydrogen or CrC4alkyl and especially are each methyl, R15 is CrCealkylene and preferably C1-C6- alkylene and R16 and R16' are each independently of the other hydrogen or CrC4alkyl and preferably hydrogen or methyl.
The radical R7 in formula (6d) has a symmetrical or, preferably, an asymmetrical structure.
A preferred group of radicals Q1 of formula (6d) comprises those wherein R7 is linear or branched C6-C10alkylene; cyclohexylene-methylene or cyclohexylene-methylene-cyclo- hexylene each unsubstituted or substituted in the cyclohexyl moiety by from 1 to 3 methyl groups; or phenylene or phenylene-methylene-phenylene each unsubstituted or substituted in the phenyl moiety by methyl.
The bivalent radical R7 is derived preferably from a diisocyanate and most preferably from a diisocyanate selected from the group isophorone diisocyanate (IPDI), toluylene-2,4- diisocyanate (TDI), 4,4'-methylenebis(cyclohexyl isocyanate), 1 ,6-diisocyanato-2,2,4- trimethyl-n-hexane (TMHDI), methylenebis(phenyl isocyanate), methylenebis(cyclohexyl-4- isocyanate) and hexamethylene diisocyanate (HMDI).
Each of the radicals alk and alk1 independently of the other is preferably a C2-C8alkylene radical, more preferably a C2-C4alkylene radical and most preferably the 1 ,2-ethylene radical.
R8 is preferably methyl or especially hydrogen.
P1 is a radical of the formula -(NH Jr-Q1 or — O— Q1, wherein Q1 is a radical of the above formula (6a), (6b) or (6c), and wherein for the variables contained therein the meanings and preferences given above apply in each case. P1 is preferably a radical of the formula -(NH ) — Qi or — O— Q1, wherein Q1 is a radical of the above formula (6a), and most preferably is a radical of formula (6') or (6"') given below.
When Q is a radical R5, the meaning and preferences given above for R5 apply in each case. Especially preferred radicals Q correspond to formula H or CH3 C=CH2 (61)
Figure imgf000018_0001
O H or CH3 -NH (CH2)2-4 — 0-C-C=CH2 (6'")
Figure imgf000018_0002
wherein for R7 the meanings and preferences given above apply in each case. Especially preferred as the radical Q are radicals of formula (61) and (6'").
In the bivalent radical of — (R1— O)n— (R2-O)m-(R3-O)p— , R1, R2, and R3, independently of one other, are each linear or branched C2-C4-alkylene or hydroxy-substituted C2-C8 alkylene radical, and n, m and p, independently of one another, are each a number from 0 to 500, wherein the sum of (n+m+p) is 5 to 1000. The sum of (n+m+p) is preferably 8 to 200, more preferably from 8 to 100. A is derived preferably bis-aminoalkylene-polyalkylene glycols of various average molecular weights.
The prepolymers of the invention may have uniform segments A or, alternatively, two or more structurally different segments A, for example, 2 or 3 or, preferably, 2 different segments A.
A1 is preferably derived from an aliphatic, cycloaliphatic, aliphatic-cycloaliphatic, aromatic or araliphatic diamine or dicarboxyl derivative, especially from a C5-C24 cycloaliphatic or aliphatic-cycloaliphatic diamine or dicarboxyl derivative. The prepolymers of the invention may have uniform segments A1 or, alternatively, two or more structurally different segments A1.
The prepolymers of the invention may have uniform segments T or, alternatively, two or more structurally different segments T.
Preferably, at least one segment A1 is a linear or branched C4-C24 alkylene radical that is interrupted by from 1 to 3, preferably 1 or 2, more preferably by one divalent amine groups of — NRm— . More preferably, at least one segment A1 is a linear or branched alkylene having from 3 to 14 carbon atoms that is interrupted by one divalent amine group of formula -NRn,-.
When Rm is a radical Q or a radical of formula (4'), then, for the segments A, A1, T and G contained therein and for the radical Q, the meanings, preferences and conditions given above apply in each case.
One group of preferred radicals A1 corresponds to formula
Figure imgf000020_0001
wherein each of alk*, alk** and alk*** independently of the others is a C2-C12alkylene radical, preferably a C2-C6alkylene radical and most preferably a C2-C4alkylene radical; I is the number 0 or 1 and especially the number 0 and for Rm and Rm' independently the meanings and preferences given above for Rm apply in each case.
The trivalent radical G may be a linear or branched C3-C24 aliphatic trivalent radical, a C5-C45 cycloaliphatic or aliphatic-cycloaliphatic trivalent radical, or a C6-C24 aromatic or araliphatic trivalent radical. Preferably, the trivalent radical G is a C6-C45 cycloaliphatic or aliphatic- cycloaliphatic trivalent radical containing at least one heteroatom selected from the group consisting of oxygen and nitrogen.
The average molecular weight of the polymer fragments CP is, for example, in a range of approximately from 350 to 25 000, preferably from 500 to 15000 and most preferably from 1000 to 10000.
A crosslinkable poly(oxyalkylene)-containing prepolymer of the invention can be prepared in a manner known to person skilled in the art, for example in a two-step process. In the first step, an amine-capped poly(oxyalkylene)-containing polyamide of the invention is prepared by reacting together a mixture comprising (a) at least one amine-capped polyalkylene glycol (or poly(oxyalkylene), (b) optionally at least one organic di- or poly-amine, (c) at least one di- carboxyl derivative, (d) optionally at least one polycarboxyl derivative, and (e) optionally a carbodiimide. In the second step, a multifunctional compound having at least one ethylenically unsaturated group and a functional group coreactive with the capping amine groups of the amine-capped poly(oxyalkylene)-containing polyamide obtained in the first step in the absence or presence of a carbodiimide.
Schemes 1-6 illustrate various possible schemes for synthesizing an ethylenically unsaturated group-capped poly(oxyalkylene)-containing prepolymer. H
H2N PPG-PEG-PPG NH2 ,N.
H2N' "NH2
Jeff amine 800 and 1900
DETA
H
HOEt
"EtOH
BHEEDA
Figure imgf000021_0001
Idealized Structure
Scheme 1
Figure imgf000022_0001
DETA
Figure imgf000022_0002
Idealized Structure
Scheme 2
Figure imgf000023_0001
DETA
or organic
terminated with acryloyl
Figure imgf000023_0002
Idealized Structure
Scheme 3
Figure imgf000024_0001
DETA
de / PS-HOBt
Figure imgf000024_0002
and
Figure imgf000024_0003
Idealized Structure
Scheme 4
Figure imgf000025_0001
and
Figure imgf000025_0002
Idealized Structure
Scheme 5
Figure imgf000026_0001
terminated or of
Figure imgf000026_0002
Idealized Structure
Scheme 6 The first step reaction can be, for example, carried out in an aqueous or aqueous-organic medium or organic solvent (e.g, ethyllactate, THF, isopropanol, or the like). A suitable medium has been found to be especially a mixture of water and a readily water-soluble organic solvent, e.g. an alkanol, such as methanol, ethanol or isopropanol, a cyclic ether, such as tetrahydrofuran (THF), or a ketone, such as acetone. An especially suitable reaction medium is a mixture of water and a readily water-soluble solvent having a boiling point of from 50 to 85°C, preferably from 50 to 7O0C, especially a water/tetrahydrofuran or a water/acetone mixture.
The reaction temperature in the first reaction step of the process is, for example, from -20 to 85°C, preferably from -10 to 5O0C and most preferably from -5 to 3O0C.
The reaction times in the first reaction step of the process may vary within wide limits, a time of approximately from 1 to 10 hours, preferably from 2 to 8 hours and most preferably 2 to 3 hours having proved practicable.
In accordance with a preferred embodiment of the invention, the stoichiometry in the reaction of the components (a), (b), (c), (d), and (e) is advantageously selected in a way such that the number of equivalents of the amino groups contained in the components (a) and (b) is greater than the number of equivalents of the carboxyl derivative groups contained in the components (c) and (d). For example, the number of equivalents of the amine groups in the components (a) and (b) is from 1 to 50, preferably from 1.1 to 20, more preferably from 1.1 to 5 and most preferably from 1.1 to 3 folds of the number of equivalents of the carboxyl derivative groups in the components (c) and (d).
It is furthermore preferred that the component (a) is used in excess in relation to the component (b) if the component (b) is preferably present.
Once the reaction of components (a) and (b) with components (c) and (d) is completed, the obtained amine-capped poly(oxyalkylene)-containing polyamide can be reacted directly with a multifunctional compound having at least one ethylenically unsaturated group and a function group coreactive with the capping amine groups of the amine-capped poly(oxyalkylene)-containing polyamide, to prepare a crosslinkable poly(oxyalkylene)- containing prepolymer of the invention. Optionally, the obtained amine-capped poly(oxyalkylene)-containing polyamide can be purified before reacting with the multifunctional compound.
The isolation and purification of the amine-capped poly(oxyalkylene)-containing polyamide obtained in the first reaction step and/or the crosslinkable poly(oxyalkylene)-containing prepolymer obtained in the second reaction step can be carried out according to known processes, for example extraction, precipitation, crystallization, re-crystallization, ultrafiltration or by chromatographic purification methods.
The prepolymers according to the invention are radiation-curable, but uncrosslinked or at least substantially uncrosslinked; nevertheless, they are stable, i.e. spontaneous crosslinking due to homopolymerization does not take place substantially. The term "radiation-curable" in reference to a prepolymer means that the prepolymer can be crosslinked or polymerized by actinic radiation, including, for example, UV radiation, ionizing radiation such gamma radiation or X-rays, microwave, and the like.
The radiation-curable prepolymers are advantageously liquid or readily meltable or water- soluble; the radiation-curable prepolymers are most preferably water-soluble. The average molecular weight of the radiation-curable prepolymers according to the invention may vary within a broad range. An average molecular weight of e.g. 1000 to 50,000 has proved to be advantageous for the radiation-curable prepolymers according to the invention.
Furthermore, the radiation-curable prepolymers according to the invention may be purified in a manner known per se, for example, by precipitation with an organic solvent, dialysis, or preferably by ultrafiltration. As a result of this purification procedure, the radiation-curable prepolymers according to the invention may be obtained in extremely pure form, e.g. as solvent-free liquids or melts or as concentrated aqueous solutions, which are free from or at least substantially free from reaction products such as salts, and from starting materials or other non-polymeric constituents.
The preferred purifying process for the prepolymers according to the invention, ultrafiltration, may be carried out in a manner known per se. Thus, it is possible to carry out ultrafiltration repeatedly, for example two to ten times. Alternatively, ultrafiltration may also be carried out continuously, until reaching the desired degree of purity. The desired degree of purity may be basically selected at any desired level.
In another aspect, the present invention relates to a polymer which is a product of crosslinking of a radiation-curable prepolymer of the invention (described-above) in the presence or preferably in the absence of one or more additional vinylic monomers. As already mentioned above, the radiation-curable prepolymers according to the invention may be crosslinked in an extremely effective and well-directed manner upon actinic irradiation, in particular by UV irradiation. Crosslinking may take place in the presence or preferably in the absence of an additional vinylic monomer. The resulting crosslinked polymers are insoluble in water.
The polymer of the invention is a hydrogel, and when fully hydrated (i.e. the water content is in equilibrium with a saline solution, typically achieved within 45 minutes for a contact lens- shaped piece of polymer) has a water content of 30-90%, preferably 45-80%, by weight. Preferably, the polymer, when fully hydrated, has an averaged contact angle of 75 degrees or less, more preferably 65 degrees or less.
An "average contact angle " refers to a contact angle of water on a surface of a material (measured by Sessile Drop method), which is obtained by averaging measurements of at least 3 individual samples (e.g., contact lenses). Average contact angles (Sessile Drop) of contact lenses can be measured using a VCA 2500 XE contact angle measurement device from AST, Inc., located in Boston, Massachusetts. This equipment is capable of measuring advancing or receding contact angles or sessile (static) contact angles. The measurements are preferably performed on fully hydrated materials.
Contact angle is a general measure of the surface hydrophilicity of a contact lens or an article (e.g., the cavity surface of a container). In particular, a low contact angle corresponds to more hydrophilic surface.
A "vinylic monomer", as used herein, refers to a low molecular weight compound that has an ethylenically unsaturated group and can be polymerized actinically or thermally. Low molecular weight typically means average molecular weights less than 700 Daltons. Exemplary ethylenically unsaturated groups include without limitation acryloyl, methacryloyl, allyl, vinyl, styrenyl, or other C=C containing groups.
In a further aspect, the present invention provides a medical device, preferably an ophthalmic device, more preferably a contact lens, which is obtained by crosslinking an above-described radiation-curable prepolymer of the invention in the presence of or preferably in the absence of one or more additional vinylic monomers.
A "medical device", as used herein, refers to a device or a part thereof having one or more surfaces that contact tissue, blood, or other bodily fluids of patients in the course of their operation or utility. Exemplary medical devices include: (1) extracorporeal devices for use in surgery such as blood oxygenators, blood pumps, blood sensors, tubing used to carry blood and the like which contact blood which is then returned to the patient; (2) prostheses implanted in a human or animal body such as vascular grafts, stents, pacemaker leads, heart valves, and the like that are implanted in blood vessels or in the heart; (3) devices for temporary intravascular use such as catheters, guide wires, and the like which are placed into blood vessels or the heart for purposes of monitoring or repair; (4) artificial tissues such as artificial skin for burn patients; (5) dentifrices, dental moldings; (6) ophthalmic devices. In a preferred embodiment, medical devices are ophthalmic devices; and (7) cases or containers for storing ophthalmic devices or ophthalmic solutions.
An "ophthalmic device", as used herein, refers to a contact lens (hard or soft), an intraocular lens, a corneal onlay, other ophthalmic devices (e.g., stents, or the like) used on or about the eye or ocular vicinity.
An ophthalmic device is preferably a contact lens which is preferably characterized by having: a water content of from about 30% to about 90%, preferably from about 45% to about 75% by weight; an elongation at break of at least 25%, preferably at least 100%, more preferably at least 150%, and a modulus of from about 0.05 to about 2.0 Mpa, preferably from about 0.2 to about 1.5 MPa, more preferably from about 0.3 to about 1.0 MPa. Preferably, the contact lens, when fully hydrated, has an averaged contact angle of 75 degrees or less, more preferably 65 degrees or less. In the case of photo-crosslinking, a photo-initiator is suitably added which can initiate radical crosslinking. Examples of these are familiar to the person skilled in the art, and suitable photo-initiators which may be mentioned in particular are benzoin-methylether, 1-hydroxy- cyclo-hexyl-phenylketone, Darocure 1173 or lrgacure types. Crosslinking may be commenced by actinic radiation, e.g. UV light, or by ionized radiation, e.g. gamma rays or X- rays.
Photo-crosslinking may also be carried out without adding a solvent, e.g. if the radiation- curable prepolymer is a liquid or readily meltable prepolymer, or it takes place in a suitable solvent. Suitable solvents are basically all solvents that dissolve the radiation-curable prepolymers according to the invention and optionally the additional vinylic monomers, e.g. water, alcohols such as lower alkanols, e.g. ethanol or methanol, furthermore carboxylic acid amides, such as dimethyl-formamide, or dimethyl sulphoxide, and likewise mixtures of suitable solvents, e.g. mixtures of water with an alcohol, such as a water/ethanol or a water/methanol mixture.
Photo-crosslinking is preferably effected whilst solvent-free or essentially solvent-free or directly from an aqueous solution of the prepolymers according to the invention, which may be obtained as the result of the preferred purification step, ultrafiltration, optionally after adding additional vinylic monomers. For example, photo-crosslinking may be undertaken from a 15 to 90% aqueous solution.
The process for the production of the crosslinked polymers according to the invention comprises radiation-crosslinking a radiation-curable prepolymer of the invention and optionally further copolymerizable vinylic monomers, especially in substantially pure form, i.e. for example after ultrafiltration once or several times whilst solvent-free or substantially solvent-free or in solution, especially in aqueous solution, in the presence or preferably in the absence of an additional vinylic monomer, preferably using a photoinitiator.
Water content and mechanical properties of radiation cured prepolymers can be adjusted by adjusing relative ratios of components used in the preparation of the prepolymer. For example, prepolymers that contain a higher ratio of crosslinkable groups are expected to yield lenses with higher modulus. Formulations that are enriched with hydrophobic components (e.g. long chain diacid chloride versus short chain diacid chloride) are expected to result in hydrogels with increased mechanical strength and lower water content. Mechanical strength often increases with molecular weight. Therefore, formulations that contain higher molecular weight Jeffamines are likely to result hydrogels with improved elastic properties.
The vinylic monomer which may be additionally used for photo-crosslinking in accordance with the invention may be hydrophilic, hydrophobic or may be a mixture of a hydrophobic and a hydrophilic vinylic monomer. Suitable vinylic monomers include especially those normally used for the manufacture of contact lenses.
A "vinylic monomer", as used herein, refers to a low molecular weight compound that has an ethylenically unsaturated group and can be polymerized actinically or thermally. Low molecular weight typically means average molecular weights less than 700 Daltons. Exemplary ethylenically unsaturated groups include without limitation acryloyl, methacryloyl, allyl, vinyl, styrenyl, or other C=C containing groups.
A "hydrophilic vinylic monomer" refers to a monomer which as a homopolymer typically yields a polymer that is water-soluble or can absorb at least 10 percent by weight water. A "hydrophobic vinylic monomer" refers to a monomer which as a homopolymer typically yields a polymer that is insoluble in water and can absorb less than 10 percent by weight water.
It is preferable to use a hydrophobic vinylic monomer, or a mixture of a hydrophobic vinylic monomer with a hydrophilic vinylic monomer, whereby this mixture contains at least 50 percent by weight of a hydrophobic vinyl monomer. In this way, the mechanical properties of the polymer may be improved without the water content dropping substantially. Both conventional hydrophobic vinylic monomers and conventional hydrophilic vinylic monomers are suitable for copolymerization with the radiation-curable prepolymers according to the invention.
Suitable hydrophobic vinylic monomers include, without limitation, Ci -C-iβ-alkylacrylates and -methacrylates, C3-C18 alkylacrylamides and -methacrylamides, acrylonitrile, methacrylonitrile, vinyl-Ci-C-|8-alkanoates, C2-C-|8-alkenes, C2-C-|8-halo-alkenes, styrene, C-|-C6-alkylstyrene, vinylalkylethers in which the alkyl moiety has 1 to 6 carbon atoms, C2- Cio-perfluoralkyl-acrylates and -methacrylates or correspondingly partially fluorinated acrylates and methacrylates, C3-Ci2-perfluoralkyl-ethyl-thiocarbonylaminoethyl-acrylates and -methacrylates, acryloxy and methacryloxy-alkylsiloxanes, N-vinylcarbazole, C1-C12- alkylesters of maleic acid, fumaric acid, itaconic acid, mesaconic acid and the like. Preference is given e.g. to C-|-C4-alkylesters of vinylically unsaturated carboxylic acids with 3 to 5 carbon atoms or vinylesters of carboxylic acids with up to 5 carbon atoms.
Examples of suitable hydrophobic vinylic monomers include methylacrylate, ethyl-acrylate, propylacrylate, isopropylacrylate, cyclohexylacrylate, 2-ethylhexylacrylate, methylmethacrylate, ethylmethacrylate, propylmethacrylate, vinyl acetate, vinyl propionate, vinyl butyrate, vinyl valerate, styrene, chloroprene, vinyl chloride, vinylidene chloride, acrylonitrile, 1-butene, butadiene, methacrylonitrile, vinyl toluene, vinyl ethyl ether, perfluorohexylethyl-thio-carbonyl-aminoethyl-methacrylate, isobornyl methacrylate, trifluoroethyl methacrylate, hexafluoro-isopropyl methacrylate, hexafluorobutyl methacrylate, tris-trimethylsilyloxy-silyl-propyl methacrylate, 3-methacryloxypropyl-pentamethyl-disiloxane and bis(methacryloxypropyl)-tetramethyl-disiloxane.
Suitable hydrophilic vinylic monomers include, without limitation, hydroxy-substituted lower alkylacrylates and -methacrylates, acrylamide, methacrylamide, lower alkyl-acrylamides and -methacrylamides, ethoxylated acrylates and methacrylates, hydroxy-substituted lower alkyl- acrylamides and -methacrylamides, hydroxy-substituted lower alkylvinyl-ethers, sodium ethylene sulphonate, sodium styrene sulphonate, 2-acrylamido-2-methyl-propane-sulphonic acid, N-vinyl pyrrole, N-vinyl succinimide, N-vinyl pyrrolidone, 2- or 4-vinyl pyridine, acrylic acid, methacrylic acid, amino- (whereby the term "amino" also includes quaternary ammonium), mono-lower-alkylamino- or di-lower-alkylamino-lower-alkyl-acrylates and - methacrylates, allyl alcohol and the like. Preference is given e.g. to hydroxy-substituted C2-C4-alkyl(meth)acrylates, five- to seven-membered N-vinyl-lactams, N,N-di-C-|-C4-alkyl- methacrylamides and vinylically unsaturated carboxylic acids with a total of 3 to 5 carbon atoms.
Examples of suitable hydrophilic vinylic monomers include hydroxyethyl methacrylate, hydroxyethyl acrylate, acrylamide, methacrylamide, dimethylacrylamide, allyl alcohol, vinyl pyridine, vinyl pyrrolidone, glycerol methacrylate, N-(1 ,1 -dimethyl-3-oxobutyl)acrylamide, and the like. Preferred hydrophobic vinylic monomers are methyl methacrylate, ethylmathacrylate and vinyl acetate. It is understood that acetate groups may be hydrolyzed during autoclave and such hydrolysis process may impart hydrophilic character once converted to PVA units. Preferred hydrophilic vinylic monomers are 2-hydroxyethyl methacrylate, N-vinyl pyrrolidone, N,N-dimethylacrylamide and acrylamide.
The processing according to the invention for molding radiation-curable prepolymers into ophthalmic articles, especially contact lenses, may take place in a manner known per se, for example, photo-crosslinking of the radiation-curable prepolymers according to the invention in an appropriate contact lens mold. Further examples of molded articles according to the invention, apart from contact lenses, are e.g. intra-ocular lenses or eye dressings, furthermore biomedical articles which may be used in surgery, such as heart valves, artificial arteries or the like, also films or membranes, e.g. membranes for diffusion control, photo- structurable films for data storage, or photo resist materials, e.g. membranes or molded articles for etch resist printing or screen resist printing.
In another further aspect, the present invention provides a method for producing an ophthalmic device, the method comprising the steps of: a) introducing an above-described radiation-curable prepolymer of the invention, which is liquid or readily meltable at room temperature, and which is essentially free from solvents, into a mold, in the presence or preferably in the absence of one or more additional vinylic monomers, and optionally in the presence of a photo-initiator, b) crosslinking by actinic radiation the radiation-curable prepolymer, and c) opening the mold so that the device can be removed from the mold.
In a still further aspect, the present invention provides a method for producing an ophthalmic device, the method comprising the steps of: a) introducing an aqueous solution of an above- described radiation-curable prepolymer of the invention, in the presence or preferably in the absence of one or more additional vinylic monomers, and optionally in the presence of a photo-initiator, into a mold; b) crosslinking by actinic radiation the radiation-curable prepolymer, and c) opening the mold so that the device can be removed from the mold.
Preferably the viscosity of the aqueous formulation is 15 to 100000 cps, more preferably 50- 2000 cps, at room temperature. The radiation-curable prepolymers according to the invention may be introduced into a mold by methods known per se, especially conventional dispensing, e.g. dropwise addition. If vinylic monomers are present, the monomers employed are those mentioned above, in desired quantities. Any vinylic monomers that are optionally present are advantageously first of all mixed with the prepolymer according to the invention and then introduced into the mold.
Appropriate molds are made, for example, from polypropylene. Suitable materials for re¬ usable moulds are e.g. quartz, sapphire glass metals or combinations thereof.
If the molded articles to be produced are contact lenses, these may be produced in a manner known per se, e.g. in a conventional "spin-casting mold", as described for example in U.S. Patent No. 3,408,429, or by the so-called full mold process in a static form, as described e.g. in U.S. Patent Nos. 4,347,198, 5,508,317, 5,583,463, 5,789,464, and 5,849,810.
Crosslinking may be initiated in the mold e.g. by means of actinic radiation, such as UV irradiation, ionizing radiation (e.g., gamma or X-ray irradiation).
As already mentioned, photo-crosslinking is advantageously carried out in the presence of a photo-initiator which can initiate radical crosslinking. The photo-initiator is advantageously added to the prepolymers according to the invention prior to introducing them into the mold, preferably by mixing the polymers and the photo-initiator together. The amount of photo- initiator may be selected from a wide range, whereby an amount of up to 0.05 g/g polymer and especially up to 0.003 g/g polymer has proved favorable.
What is notable is that the crosslinking according to the invention may be effected in a very short time, e.g. in < 60 minutes, advantageously in < 20 minutes, preferably in < 10 minutes, most preferably in < 5 minutes, particularly preferably in 1 to 60 seconds and most particularly in 1 to 30 seconds.
What is also notable is that the contact lenses according to the invention can be produced from a radiation-curable prepolymer in a very simple and efficient way compared with the prior art. This is based on many factors. On the one hand, the starting materials may be acquired or produced inexpensively. Secondly, there is the advantage that the prepolymers are surprisingly stable, so that they may undergo a high degree of purification. Therefore, for crosslinking, a polymer may be used which requires practically no more subsequent purification, such as in particular complicated extraction of unpolymerized constituents. Furthermore, crosslinking may take place solvent-free or in aqueous solution, so that a subsequent solvent exchange or the hydration step is not necessary. Finally, photo- polymerization is effected within a short period, so that from this point of view also the production process for the contact lenses according to the invention may be set up in an extremely economic way.
Opening of the mold so that the molded article can be removed from the mold may take place in a manner known per se.
If the molded article produced according to the invention is a contact lens which is produced solvent-free from an already purified prepolymer according to the invention, then after removal of the molded article, it is not normally necessary to follow up with purification steps such as extraction. This is because the prepolymers employed do not contain any undesired constituents of low molecular weight; consequently, the crosslinked product is also free or substantially free from such constituents and subsequent extraction can be dispensed with. Accordingly, the contact lens can be directly transformed in the usual way, by hydration, into a ready-to-use contact lens. Appropriate embodiments of hydration are known to the person skilled in the art, whereby ready-to-use contact lenses with very varied water content may be obtained. The contact lens is expanded, for example, in water, in an aqueous salt solution, especially an aqueous salt solution having an osmolarity of about 200 to 450 milli-osmole in 1000 ml (unit: mθsm/l), preferably about 250 to 350 mθsm/l and especially about 300 mθsm/l, or in a mixture of water or an aqueous salt solution with a physiologically compatible polar organic solvent, e.g. glycerol. Preference is given to expansions of the article in water or in aqueous salt solutions.
The aqueous salt solutions used for hydration are advantageously solutions of physiologically compatible salts, such as buffer salts conventionally used in the field of contact lens care, e.g. phosphate salts, or isotonizing agents conventionally used in the field of contact lens care, such as in particular alkali halides, e.g. sodium chloride, or solutions of mixtures thereof. One example of an especially suitable salt solution is an artificial, preferably buffered lachrymal fluid, which is adapted to natural lachrymal fluid as regards pH value and osmolarity, e.g. an unbuffered or preferably buffered common salt solution, for example buffered by phosphate buffer, whose osmolarity and pH value correspond to the osmolarity and pH value of human lachrymal fluid.
The above-defined hydration fluids are preferably pure, i.e. free or substantially free from undesired constituents. This is most preferably pure water or an artificial lachrymal fluid as described above.
If the molded article produced according to the invention is a contact lens which is produced from an aqueous solution of an already purified prepolymer according to the invention, then the crosslinked product also does not contain any troublesome impurities. It is therefore not necessary to carry out subsequent extraction. Since crosslinking is carried out in an essentially aqueous solution, it is additionally unnecessary to carry out subsequent hydration. The contact lenses obtainable by this process are therefore notable, according to an advantageous embodiment, for the fact that they are suitable for their intended usage without extraction. By intended usage is understood, in this context, that the contact lenses can be used in the human eye.
The contact lenses obtained according to the invention have a wide range of unusual and extremely advantageous properties. One of these properties which may be named is for example its excellent compatibility with the human cornea, which is based on a well-balanced relationship between water content, oxygen permeability and good mechanical properties including elasticity and durability. Moreover, the contact lenses according to the invention have high resistance of shape. No changes in shape can be detected even after autoclaving e.g. at about 1200C. The contact lenses obtained according to the invention can also have a water content of from about 30% to about 90%, an elongation at break of at least 150%, and a modulus of from about 0.3 to about 1.0 Mpa, an enhanced thermal stability and a decreased susceptibility to autoclave-induced change in modulus.
The photo-curable prepolymers of the invention can also find uses as binder polymers in inks for making colored contact lenses. The present invention is also related to a water-based ink comprising a photocurable prepolymer of the invention and a colorant. A "binder polymer" refers to a crosslinkable polymer that can be crosslinked by a crosslinker or upon initiation by a chemical or physical means (e.g., moisture, heating, UV irradiation or the like) to trap or bind colorants onto or into a contact lens such as that term is known in the art.
A "colored contact lens" refers to a contact lens (hard or soft) having a color image printed thereon. A color image can be a cosmetic pattern, for example, iris-like patterns, Wild Eye™ patterns, made-to-order (MTO) patterns, and the like; an inversion mark that allows a user to handle and insert easily a contact lens; a toric rotation mark, or contact lenses stock keeping units (SKUs), for example, either in forms of numbers or as bar codes. A color image can be a single color image or a multi-color image. A color image is preferably a digital image, but it can also be an analog image.
A colored contact lens can be produced by printing a high-quality color image directly on a contact lens by pad printing and/or inkjet printing techniques or by using a print-on-mold process described in U.S. Patent No. 5,034,166 to Rawlings et al. A contact lens can be clear before it is printed upon. Alternatively, a contact lens can be tinted prior to being printed upon. That is, a colorant may have been added to that lens using methods that are well known in the art before that lens is printed upon using any printing methods.
A "colored coat" refers to a coating on an object and having a color image printed therein.
"Colorant" means either a dye or a pigment or a mixture thereof that is used to print a color image on an article.
A "pigment" means a powdered substance that is suspended in a liquid in which it is insoluble. Pigments are used to impart color. Pigments, in general, are more opaque than dyes. They can be conventional or non-pearlescent pigments or pearlescent pigments.
"Dye" means a substance that is soluble in a solvent and that is used to impart color. Dyes are typically translucent and absorb but do not scatter light. Dyes can cover both optical regions of contact lenses and non-optical regions of contact lenses. Nearly any dye can be used in the present invention, so long as it can be used in an apparatus as described below. These dyes include fluorescent dyes, phosphorescent dyes, and conventional dyes. The ink of the invention can also include a thermal initiator or a photoinitiator. The identity of the initiator is not critical and is not part of the present invention. One of ordinary skill in the art will readily recognize the kind and amount of an initiator (photoinitiator or thermoinitiator) that will yield good results in the present invention. Any suitable photoinitiators can be used in the ink formulations. The photoinitiator presently preferred by the inventors is lrgacure 2959, lrgacure 907, lrgacure 500, lrgacure 651 , lrgacure 369, Darocure 1 173, and Darocure 4265. In addition, combinations of initiators can be used.
The inks of the invention can optionally (but preferably do not) include a crosslinker. A "cross linker" refers to a compound comprising two or more functional groups, as they are known in the art. A cross linker molecule can be used to crosslink two or more monomers or polymer molecules. Cross linkers are known in the art and are disclosed in various US Patents. Such crosslinkers may be added to the ink in order to match the physical properties (e.g. modulus) of the cured ink to that of the cured lens to which it is applied.
The inks of the invention can optionally include a surfactant. The term "surfactant," as used herein, refers to a surface-active compound as that term is known in the art, such as, for example, Surfynol 420 and Surfynol 104 (from Air Products), Pluronic F108 and F38 (from BASF). A surfactant can have one ore more of the following functions: to adjust the surface tension of an ink, to defoam, to improve the separation of pigment particles, and to prevent settling or clumping of pigment particles.
The inks of the invention can optionally (but preferably do not) include an antimicrobial compound. Some suitable antimicrobial materials include polyquatemary ammonium compounds, such as those described in U.S. Patent No. 3,931 ,319 to Green et al. (e.g. "POLYQUAT"). Other antimicrobial or antibacterials that can be utilized in the present invention are peptides, other polyquats, mucin, mucin mimics, glycopeptides, glycoproteins, silk proteins, cellulose, dextran or other anti-microbial or anti-bacterial entities.
The ink of the invention can further comprise one or more vinylic monomers or macromers, preferably at least one functionalizing vinylic monomer containing at least one functional group selected from the group consisting of hydroxyl group —OH, amino group -NHR (wherein R is hydrogen or C1 to C8 alkyl), carboxylic group -COOH, epoxy group, amide group — CONHR, and combinations thereof.
The ink of the invention can further comprise one or more components selected from the group consisting of humectants, antioxidant agents, anti-coagulating agents, and other additives known in the art.
The ink of the present invention comprises water as a solvent in an amount sufficient to solubilize the binder polymer and achieve a viscosity above 50 centipoise.
The inks may also (but preferably do not) comprise a solvent in addition to water. The solvent can be any appropriate organic or inorganic solvent. Any known suitable solvents can be used, so long as they do not precipitate the binder polymer, or adversely affect the stability of the colorant. Exemplary solvents include, without limitation, acetone, alcohols (e.g., methanol, ethanol, propanol, isopropanol, etc.), glycols, ketones, esters, cyclopentanone, cyclohexanone, tetrahydrofuran, acetone, methyl-2-pyrrolidone, dimethyl formamide, acetophenone, methylene dichloride, dimethyl sulfoxide, gamma-butyrolactone, ethylene dichloride, isophorone, o-dichlorobenzene, tetrahydrofuran, diacetone alcohol, methyl ethyl ketone, acetone, 2-nitropropane, ethylene glycol monoethyl ether, propylene carbonate, cyclohexanol, chloroform, trichloroethylene, 1 ,4-dioxane, ethyl acetate, ethylene glycol monobutyl ether, chlorobenzene, nitroethane, ethylene glycol monomethyl ether, butyl acetate, 1-butanol, methyl isobutyl ketone, nitromethane, toluene, ethanol, diethylene glycol, benzene, diethyl ether, ethanolamine, carbon tetrachloride, propylene glycol, hexane, ethylene glycol, and formamide.
The viscosity of an ink solution can be as high as about 5,000 centipoise (cps), but is preferably between about 1000 to about 3500 cps. The viscosity is preferably above 100 cps; more preferably above 200 cps. Most preferably, the viscosity of the ink is between 250 and 350 cps. If the viscosity is expressed in terms of natural log viscosity, the most preferred range is between 5.5 and 5.9 log (cps).
The proper concentration of binder polymer and the colorant in water to achieve the preferred ink viscosity can be determined, for example, by a design of experiment by modeling the design as a quadratic D-optimal mixture design. This can be done, for example, with a commercial software program, such as Design Expert (v. 6.0.0, from Stat- Ease of Minneapolis, MN), according to a similar procedure described in U.S. Patent Application Publication No. 2004/0044099A1.
An ink of the invention comprises: water in an amount of from about 30% to 98% by weight, preferably from about 50% to 93% by weight; a water-soluble and actinically-curable binder polymer in an amount of from about 2% to 40% by weight, preferably about 6% to 30%; and a colorant in an amount of from about 0.5% to 30% by weight, preferably about 1.5% to 20%. Preferably, the ink further comprises a photoinitiator in an amount of from about 0.05% to 2.0%.
All the above-mentioned advantages apply not only to contact lenses, but also to other molded articles according to the invention.
The previous disclosure will enable one having ordinary skill in the art to practice the invention. In order to better enable the reader to understand specific embodiments and the advantages thereof, reference to the following non-limiting examples is suggested. However, the following examples should not be read to limit the scope of the invention.
Example 1 : Synthesis of Polv(alkyleneoxide)-containinq Polvamide
A mixture consisting of 61.87 grams of O,O'-bis(2-aminopropyl) polypropylene glycol-block- poly(ethylene glycol-block-polypropylene glycol 800 ("Jeffamine-800), 19.39 grams of O1O'- bis-(2-aminopropyl) polypropylene glycol-block-poly(ethylene glycol-block-polypropylene glycol 1900 ("Jeffamine-1900), 3.738 grams of diethylenetriamine (DETA), 9.89 grams of N,N'-bis(2-hydroxy ethyl)ethylenediamine (BHEEDA), 410 grams of tetrahydrofuran (THF), 800 ml_ of water, and 200 ml_ of 20 percent (wt /vol) of Na2CO3 in water is stirred at about 600 RPM at about 210C. A few drops of this mixture are analyzed by FT-IR. The IR sample is prepared by spreading a few drops of the reaction mixture on a NaCI disk and allowing the resulting film to dry for about 15 minutes at about 6O0C. About 31.34 grams of adipoyl chloride dissolved in about 35 grams of THF is added slowly into the reaction mixture over about 7 minutes. After the addition of adipoyl chloride solution is completed, the temperature of the reaction vessel has been increased to about 280C. About 15 minutes after the addition of adipoyl chloride is completed, a few drops of the reaction mixture were removed and analyzed by FT-IR. The IR sample is prepared as described above. The FT-IR spectrum shows an absorption characteristic of amide linkages at about 1645 cm"1 after the adipoyl chloride addition.
Ethylenicallv functionalization of Polv(alkyleneoxide)-containinq polvamide)
100-mL of 20% Na2CO3 solution is added to the above resultant reaction mixture and immediately followed by adding about 3.0 grams of acryloyl chloride into the reaction mixture. After about 30 minutes, an additional 50 mL of 20% Na2CO3 solution is added to the reaction mixture quickly followed by the addition of about 3.0 grams of acryloyl chloride. After about 30 minutes, a third dose of 50 mL of 20% Na2CO3 solution is added to the reaction mixture quickly followed by the addition of about 3.0 grams of acryloyl chloride. Approximately 60 mg of 4-hydroxy-2,2,6,6,-tetramethyl-1-piperidinyloxy, free radical) (CAS# 2226-96-2) (4-hydroxy TEMPO) is then added to the mixture, which is then concentrated by rotary evaporation (bath temperature ~ 550C) until THF is no longer present. The sample is filtered through a course fritted glass filter and then purified by ultrafiltration. A tangential ultrafiltration membrane cartridge with a 3 kilo dalton cut off is employed. Ultrafiltration is allowed to proceed until the conductivity of the permeate is about 54 microsiemans/cm. The sample is then concentrated by rotary evaporation at about 55 0C until the percentage of water in the solution is about 44 percent. Several drops of the concentrated prepolymer solution are spreaded on a NaCI disk and the resulting film is allowed to dry at about 70 0C for about 15 minutes before being analyzed by FT-IR. GPC analysis shows that the obtained prepolymer has Mw = 3650, Mn= 2670, MJM n = 1.37.
Example 2: Synthesis of Polv(alkyleneoxide)-containinq polvamide A mixture consisting of 60.29 grams of O,0'-bis(2-aminopropyl) polypropylene glycol-block- poly(ethylene glycol-block-polypropylene glycol 800 ("Jeffamine-800), 35.79 grams of 0,0'- bis-(2-aminopropyl) polypropylene glycol-block-poly(ethylene glycol-block-polypropylene glycol 1900 ("Jeffamine-1900), 0.2075 grams of diethylenetriamine (DETA), 1.1039 grams of 2-methylpentamethylenediamine, 500 mL grams of tetrahydrofuran (THF), 400 mL of water, and 200 mL of 20 percent (wt /vol) of Na2CO3 in water is stirred at about 800 RPM at about 200C. About 18.59 grams of sebacyl chloride dissolved in about 30 mL of THF is added the reaction mixture over about 5 minutes. Ethylenicallv functionalization of Polv(alkyleneoxide)-containinα polvamide About 15 minutes after the addition of adipoyl chloride is completed, 50 mL of 20% (wt./vol) of sodium carbonate is added to the reaction mixture quickly followed by the addition of 5 grams of acryloyl chloride. The addition of 20% sodium carbonate followed by acryloyl chloride is repeated two more times. The resultant solution is stabilized with about 60 mg of 4-Hydroxy-TEMPO, vacuum filtered to remove precipitated NaCI and then concentrated by rotary evaporation (bath temp 550C) until THF is no longer present. The aqueous polymer solution is then further purified by ultrafiltration (Millipore Prep Scale tangential flow regenerated cellulose, TTF, 2.5 ft2 membrane. The stainless steel ultrafiltration unit is equipped with an electric pump and pressurized to 5 bar to facilitate liquid flow. Ultrafiltration is continued until the conductivity of the permeate dropped from 4.3 milli-siemans/cm to about 28 micro-siemans/cm. The sample is then concentrated by rotary evaporation until the polymer solution contained about 48% water. The resulting polymer solution is then adjusted to 50% water. FT-IR analysis: A few drops of this solution are spread on an NaCI disk and the resulting film is dried at 7O0C for about 15 minutes. Select FT-IR peaks: 3312, 2868, 1667, 1648, 1540, 1455, 1350, 1302, 1250, 1110, 950, 853 cm"1. GPC analysis: Mw = 9510, Mn= 4790, MvZM n = 1.98
Example 3: Synthesis of Polv(alkyleneoxide)-containinα Polvamide
A mixture consisting of 60.29 grams of O,O'-bis(2-aminopropyl) polypropylene glycol-block- poly(ethylene glycol-block-polypropylene glycol 800 ("Jeffamine-800"), 35.79 grams of O1O'- bis-(2-aminopropyl) polypropylene glycol-block-poly(ethylene glycol-block-polypropylene glycol 1900 ("Jeffamine-1900), 1.9475 grams of diethylenetriamine (DETA), 5.4900 grams of 2-methylpentamethylenediamine, 400 mL of water, 200 mL of 20% sodium carbonate, 400 mL of and methylene chloride is stirred at about 800 RPM at about 60C. About 15.7 grams of sebacyl chloride dissolved in about 35 mL of methylene chloride is added into the reaction mixture over about 3 minutes. Adding about 1500 mL of THF, 1 liter of isopropanol and 200 mL of water breaks up the resulting suspension. Approximately 5 grams of acryloyl chloride and 50 mL of 20% sodium carbonate are added to the reaction mixture. The acryloyl chloride and 20% sodium carbonate additions are repeated two more times and then the reaction mixture is stabilized with 4-HydroxyTEMPO. The reaction mixture is then filtered and then concentrated by rotary evaporation (bath temp ~ 550C) until organic solvents are removed. The resulting aqueous polymer solution is further purified by ultrafiltration. A stainless steel ultrafiltration (UF)unit equipped with an electric pump and a 3 kilodalton regenerated cellulose membrane (2.5 ft2, TTF, tangential flow cartridge) is used in this operation. The UF unit is pressurized to about 5 bar to facilitate liquid flow. The UF process is continued until the conductivity of the permeate is decreased to about 4.96 micro- siemans/cm. The polymer solution is concentrated by ultrafiltration and then by rotary evaporation (bath temp 550C) until the water content of the polymer solution is about 55%. Approximately 82 grams of a 45 percent polymer solution in water are obtained. A sample is prepared for FT-IR analysis by spreading a few drops of the polymer solution on a NaCI disk and drying the resulting film at 7O0C for several minutes. Selected FT-IR peaks: 3305, 2866, 1674, 1644, 1539, 1456, 1349, 1292, 1251 , 1108, 949, 862 cm"1. GPC analysis: Mw = 14100, Mn = 8050, MJM „ = 1.75
Example 4: Preparation of Contact Lenses
Clear hydrogel contact lenses are prepared by filling poly(propylene) molds with aqueous solutions containing an actinically-crosslinkable prepolymer prepared in Examples 1-3, photo-initiator (Irgacure 2959) and irradiating the filled molds with UV light near 300 nm (Grobel Lamp). The composition of each lens formulation is shown in Table 1 , in which all of the percentages are by weight. The Grobel lamp produces UV light near 300 nm. The Grobel unit is equipped with a 305 nm filter designed to produce 50% transmission at 305 nm when the filter thickness is 2mm.
Table 1
Figure imgf000044_0001
3. Prepolymer prepared in Example 3.
Curing conditions are listed in Table 2. Clear hydrogel lenses are obtained and placed in glass vials containing borate buffered saline. The vials are sealed and the thermal stability / autoclave stability of the lenses is evaluated as described below. Table 2
Figure imgf000045_0001
* Having a viscosity of about 424 cps at 25 C.
Thermal Stability Testing
The thermal stability of lenses is evaluated by measuring diameters of lenses that are subjected to autoclave at about 1210C for zero minutes (non-autoclave as control), 45 minutes (autoclave) and 90 minutes (double autoclave). Lens diameters are measured at room temperature in borate buffered saline using a tool makers microscope. Diameter data and water content data is summarized in Tables 3 (lens formulation I) and 4 (lens formulation II). Water content (% by weight) in a Lens is measured gravimetrically using a Sartorius Moisture Analyzer.
Table 3
Figure imgf000045_0002
Figure imgf000046_0001
The diameters of the non-sterilized (autoclave), single sterilized (autoclave) and double sterilized (autoclave) lenses are equivalent.
Contact lenses obtained from formulations I and Il are stable to multiple autoclave treatments as shown in Tables 3 and 4. Diameters of the three lens groups measured at room temperature are found to be equivalent as shown in Tables 3 and 4. In addition, lens water content does not change when lenses are subjected to autoclave treatment.
Although various embodiments of the invention have been described using specific terms, devices, and methods, such description is for illustrative purposes only. The words used are words of description rather than of limitation. It is to be understood that changes and variations may be made by those skilled in the art without departing from the spirit or scope of the present invention, which is set forth in the following claims. In addition, it should be understood that aspects of the various embodiments may be interchanged either in whole or in part. Therefore, the spirit and scope of the appended claims should not be limited to the description of the preferred versions contained therein.

Claims

Claims
1. A crosslinkable poly(oxyalkylene)-containing copolymer prepolymer, which is a reaction product of an amine-capped poly(oxyalkylene)-containing polyamide and a multifunctional compound having at least one ethylenically unsaturated group and a functional group coreactive with the capped amine groups of the amine-capped poly(oxyalkylene)-containing polyamide, wherein the amine-capped poly(oxyalkylene)-containing polyamide is a copolymerization product of a mixture comprising the components of:
(a) at least one aminoalkyl polyalkylene glycol of formula (1) CG-(R1-O)n-(R2-O)1n-(R3 -O)p-CG' (1) wherein CG and CG' independently of each other are a primary or secondary amino group, or an amino-CrC^ alkyl, R1, R2, and R3, independently of one other, are each linear or branched C2-C4-alkylene or hydroxy-substituted C2-C8 alkylene radical, and n, m and p, independently of one another, are each a number from O to 500, wherein the sum of (n+m+p) is 5 to 1000,
(b) optionally at least one organic di- or poly-amine, wherein the organic diamine is a linear or branched C2-C24 aliphatic diamine, a C5-C24 cycloaliphatic or aliphatic-cycloaliphatic diamine, or a C6-C24 aromatic or araliphatic diamine, and wherein the organic poly amine is a compound of formula
HN-B1' — NH
R4 R4' (2), wherein R4 and R4' independently of each other are hydrogen or unsubstituted or substituted C1-C6 alkyl or together are a direct, ring-forming bond, and B1' is a bivalent radical selected from the group consisting of a linear or branched C3-C24alkylene, an unsubstituted C6- C10arylene, a C1-C4 alkyl-substituted C6-C10 arylene, a C7-C18 aralkylene, C6-C10 arylene-Cr C2 alkylene-C6-C10arylene, C3-C8 cycloalkylene, C3-C8 cycloalkylene-C^Ce alkylene, C3-C8 cycloalkylene-CrC2 alkylene-C3-C8 cycloalkylene Or C1-C6 alkylene-C3-C8 cycloalkylene-C,- C6 alkylene, each of which is interrupted by at least one bivalent amine group ( — NH — ) or has a primary or secondary amine group,
(c) at least one dicarboxyl derivative which is an organic compound with two groups of O
Il
— C-D, wherein D is halide, OH, or alkoxyl, cycloakoxyl, or aralkoxyl, wherein the dicarboxyl derivative is derived from a linear or branched C3-C24 aliphatic dicarboxylic acid, a C5-C24 cycloaliphatic or aliphatic-cycloaliphatic dicarboxylic acid, a C6-C24 aromatic or araliphatic dicarboxylic acid, or a dicarboxylic acid which contains amino or imido groups or N- heterocyclic rings,
(d) at least one polycarboxyl derivative which is an organic compound with three or more
O
Il groups of — C-D, wherein D is defined above, and
(e) optionally a carbodiimide.
2. The crosslinkable poly(oxyalkylene)-containing prepolymer of claim 1 , wherein D is halide.
3. The crosslinkable poly(oxyalkylene)-containing prepolymer of claim 2, wherein D is chloride.
4. The crosslinkable poly(oxyalkylene)-containing prepolymer of claim 3, wherein the dicarboxyl derivative is a diacid chloride which is fumaryl chloride, suberoyl chloride, succinyl chloride, phthaloyl chloride, isophthaloyl chloride, terephthaloyl chloride, sebacoyl chloride, adipoyl chloride, trimethyladipoyl chloride, azelaoyl chloride, dodecanedioic acid chloride, succinic chloride, glutaric chloride, oxalyl chloride, cyclobutanedicarbonyl chloride, cyclopentanedicarbonyl chloride, cyclohexanedicarbonyl chloride, methylcyclohexanedicarbonyl chloride, dicyclohexyldicarbonyl chloride, dimer acid chloride, or mixtures thereof.
5. The crosslinkable poly(oxyalkylene)-containing prepolymer of claim 2, wherein the mixture comprises a tricarbonyl halide.
6. The crosslinkable poly(oxyalkylene)-containing prepolymer of claim 5, wherein the tricarbonyl halide is cycloaliphatic tricarbonyl halide, aliphaticcycloaliphatic tricarbonyl chloride, benzene tricarbonyl chloride, or mixtures thereof.
7. The crosslinkable poly(oxyalkylene)-containing prepolymer of claim 6, wherein the tricarbonyl halide is cyclohexane-1 ,3,5-tricarbonyl chloride, 1 ,3,5-trimethyl-1 ,3,5- cyclohexanetricarbonyl chloride, trimesoyl chloride, or mixtures thereof.
8. The crosslinkable poly(oxyalkylene)-containing prepolymer of claim 1 , wherein D is OH, wherein the mixture comprises a carbodiimide.
9. The crosslinkable poly(oxyalkylene)-containing prepolymer of claim 8, wherein the carbodiimide is 1-ethyl-3-(3-dimethylaminopropyl)carbodiimide (EDC), N1N'- dicyclohexylcarbodiimide (DCC), 1-cylcohexyl-3-(2-morpholinoethyl)carbodiimide, diisopropyl carbodiimide, or mixtures thereof.
10. The crosslinkable poly(oxyalkylene)-containing prepolymer of claim 8, wherein the carbodiimide is a resin-bound carbodiimide, wherein the mixture comprises optionally a resin-bound 1 -hydroxybenzotriazole as catalyst.
11. The crosslinkable poly(oxyalkylene)-containing prepolymer of claim 8, wherein the mixture further comprises an amino acid.
12. The crosslinkable poly(oxyalkylene)-containing prepolymer of claim 1 , wherein the multifunctional compound comprises an ethylenically unsaturated group and a carboxylic acid group, wherein the reaction between the multifunctional compound and the amine- capped poly(oxyalkylene)-containing polyamide occurs in the presence of a carbodiimide.
13. The crosslinkable poly(oxyalkylene)-containing prepolymer of claim 12, wherein the carbodiimide is a resin-bound carbodiimide.
14. A crosslinkable poly(oxyalkylene)-containing prepolymer having formula (4)
Figure imgf000049_0001
wherein q is an integer of >3, Q is an organic radical that comprises at least one crosslinkable group, CP is a multivalent linear or branched copolymer fragment comprising comprising segments A, A1, T, and optionally segments G, wherein: A is the bivalent radical of — (R1- O)n- (R2- O)m— (R3- O)p— , wherein R1, R2, and R3, independently of one other, are each linear or branched C2-C4-alkylene or hydroxy- substituted C2-C8 alkylene radical, and n, m and p, independently of one another, are each a number from 0 to 500, wherein the sum of (n+m+p) is 5 to 1000; G is a linear or branched C3-C24 aliphatic trivalent radical, a C5-C45 cycloaliphatic trivalent radical, a C5-C45 aliphatic-cycloaliphatic trivalent radical, or a C3-C24 aromatic or araliphatic trivalent radical; Ai is a linear or branched C2-C24 aliphatic bivalent radical, a C5-C24 cycloaliphatic or aliphatic- cycloaliphatic bivalent radical, a C6-C24 araliphatic bivalent radical, or aliphatic-heterocyclic bivalent radical, each of which is interrupted by at least one group of formula — NRm— in which Rm is hydrogen, a radical Q mentioned above or a radical of formula O
Il — C-CP1- Q (4') wherein Q is as defined above, and CP' is a bivalent copolymer fragment comprising one or more segments selected from the group consisting of A, A1, T and G; T is a bivalent radical of formula
RA C N
O (5), wherein RA is hydrogen, an unsubstituted C1-C6 alkyl, or a substituted C1-C6 alkyl; provided that in the copolymer fragments CP and CP' a segment A is linked to a segment A1 or G through a segment T; provided that the C atom of -CO— is bonded to a segment A1 or G when Rm is a radical of formula (4'); provided that Q is linked to the copolymer fragment CP or CP' through a segment T.
15. The crosslinkable poly(oxyalkylene)-containing copolymer prepolymer of claim 14, wherein Q is
(i) an organic radical R5 which is an olefinically unsaturated copolymerizable radical having 2 to 24 carbon atoms which may be further substituted, or
(ii) a radical of formula -(NH )r— Q1 Or -O-Q1, wherein Q1 is t o Il J hZ-O— C-fj—Rs (6a^
Figure imgf000050_0001
o Il °*c I'Pi V / P1 1' R7-NH-C-O — alk — N— alk'— Nχ
Re (6d), or
O Z"— NH-C-R5 (6e), and wherein
Z is linear or branched C2-C12all<ylene,
W is a C2-C12alkylene radical, phenylene radical or C7-C12aralkylene radical, each of R6 and R6' independently of each other is hydrogen, d-C4alkyl or halogen,
R7 is a bivalent aliphatic, cycloaliphatic, aliphatic-cycloaliphatic, aromatic or araliphatic hydrocarbon radical,
R8 is hydrogen or CrC4alkyl, each of alk and alk' independently of the other is a linear or branched Ci-C12alkylene radical, each of r and s independently of each other is the number 0 or 1 ,
Z" is d-Cealkylene and
P1 and P1' independently of each other are a radical of formula -(NH ^-Q1 or — O— Q1, wherein Q1 is a radical of the above formula (6a), (6b), (6c) or (6e).
16. The crosslinkable poly(oxyalkylene)-containing copolymer prepolymer of claim 15, wherein Q is a radical of formula -(NH Jr-Q1 wherein r is 0 and Q1 is a radical of formula (6a) wherein m is 0, R5 is a radical of formula
Figure imgf000051_0001
wherein t is the number 0 or 1 , R9 is hydrogen, C1-C4SlKyI or halogen, each of R10 and R11 independently of the other is hydrogen, CrC4alkyl, phenyl, carboxy or halogen, and
Z' is linear or branched d-C12alkylene or unsubstituted or d-dalkyl- or CrC4alkoxy- substituted phenylene or C7-C12aralkylene.
17. The crosslinkable poly(oxyalkylene)-containing copolymer prepolymer of claim 15, wherein Q is a radical of formula -(NH Jr-Q1 wherein r is 1 and Q1 is a radical of formula (6a) wherein s is 1 , R5 is a radical of formula
Figure imgf000052_0001
wherein t is 0,
R9 is hydrogen, CrC4alkyl, Ri0 is hydrogen, methyl, chlorine or phenyl, R11 hydrogen or carboxy, and Z' is linear or branched d-C^alkylene.
18. The crosslinkable poly(oxyalkylene)-containing copolymer prepolymer of claim 15, wherein Q is a radical of formula H or CH3
— C=CH2 (6')
Figure imgf000052_0002
O H or CH3 NH — (CH2)2.4 — 0-C-C=CH2 (6"')
Figure imgf000052_0003
Figure imgf000053_0001
wherein for R7 the meanings and preferences given above apply in each case.
19. The crosslinkable poly(oxyalkylene)-containing copolymer prepolymer of claim 18, wherein Q is a radical of formula (6') or (6'").
20. A polymer obtained by crosslinking a crosslinkable poly(oxyalkylene)-containing prepolymer according to any one of claims 1 to 13, in the presence or absence of an additional vinylic monomer.
21. A polymer of claim 20, obtained by crosslinking a crosslinkable poly(oxyalkylene)- containing copolymer prepolymer according to any one of claims 1 to 13, in the absence of an additional vinylic monomer.
22. A polymer obtained by crosslinking a crosslinkable poly(oxyalkylene)-containing prepolymer according to any one of claims 14 to 19, in the presence or absence of an additional vinylic monomer.
23. A medical device, comprising a poly(oxyalkylene)-containing copolymer hydrogel which is an actinically crosslinking product of a crosslinkable poly(oxyalkylene)-containing prepolymer in the absence or presence of an additional vinylic monomer and optionally in the presence of a photo-initiator, wherein the prepolymer is a reaction product of an amine- capped poly(oxyalkylene)-containing polyamide and a multifunctional compound having at least one ethylenically unsaturated group and a function group coreactive with the capping amine groups of the amine-capped poly(oxyalkylene)-containing polyamide, wherein the amine-capped poly(oxyalkylene)-containing polyamide is a copolymerization product of a mixture comprising the components of:
(a) at least one aminoalkyl polyalkylene glycol of formula (1)
CG-(R1-O)n-(R2-O)1n-(R3 -O)P-CG1 (1) wherein CG and CG' independently of each other are a primary or secondary amino group, or an amino-Ci-C12 alkyl, R1, R2, and R3, independently of one other, are each linear or branched C2-C4-alkylene or hydroxy-substituted C2-C8 alkylene radical, and n, m and p, independently of one another, are each a number from 0 to 100, wherein the sum of (n+m+p) is 5 to 1000,
(b) optionally at least one organic di- or poly-amine, wherein the organic diamine is a linear or branched C2-C24 aliphatic diamine, a C5-C24 cycloaliphatic or aliphatic-cycloaliphatic diamine, or a C6-C24 aromatic or araliphatic diamine, and wherein the organic poly amine is a compound of formula
HN- B1 1- NH
R4 R4 1 (2), wherein R4 and R4 1 independently of each other are hydrogen or unsubstituted or substituted C1-C6 alkyl or together are a direct, ring-forming bond, and B1' is a bivalent radical selected from the group consisting of a linear or branched C3-C24alkylene, an unsubstituted C6- C10arylene, a C1-C4 alkyl-substituted C6-C10 arylene, a C7-C18 aralkylene, C6-C10 arylene-Cr C2 alkylene-C6-C10arylene, C3-C8 cycloalkylene, C3-C8 cycloalkylene-CrCe alkylene, C3-C8 cycloalkylene-CrC2 alkylene-C3-C8 cycloalkylene or C1-C6 alkylene-C3-C8 cycloalkylene-Cr C6 alkylene, each of which is interrupted by at least one bivalent amine group ( — NH — ) or has a primary or secondary amine group,
(c) at least one dicarboxyl derivative which is an organic compound with two groups of O
Il
— C-D, wherein D is halide, OH, or alkoxyl, cycloakoxyl, or aralkoxyl, wherein the dicaroxyl derivative is derived from a linear or branched C3-C24 aliphatic dicarboxylic acid, a C5-C24 cycloaliphatic or aliphatic-cycloaliphatic dicarboxylic acid, a C6-C24 aromatic or araliphatic dicarboxylic acid, or a dicarboxylic acid which contains amino or imido groups or N- heterocyclic rings,
(d) at least one polycarboxyl derivative which is an organic compound with three or more
O
Il groups of — C-D1 wherein D is defined above, and
(e) optionally a carbodiimide.
24. The medical device of claim 23, wherein D is halide.
25. The medical device of claim 24, wherein D is chloride.
26. The medical device of claim 25, wherein the dicarboxyl derivative is a diacid chloride which is fumaryl chloride, suberoyl chloride, succinyl chloride, phthaloyl chloride, isophthaloyl chloride, terephthaloyl chloride, sebacoyl chloride, adipoyl chloride, trimethyladipoyl chloride, azelaoyl chloride, dodecanedioic acid chloride, succinic chloride, glutaric chloride, oxalyl chloride, cyclobutanedicarbonyl chloride, cyclopentanedicarbonyl chloride, cyclohexanedicarbonyl chloride, methylcyclohexanedicarbonyl chloride, dicyclohexyldicarbonyl chloride, dimer acid chloride, or mixtures thereof.
27. The medical device of claim 24, wherein the mixture comprises a tricarbonyl halide.
28. The medical device of claim 27, wherein the tricarbonyl halide is cycloaliphatic tricarbonyl halide, aliphaticcycloaliphatic tricarbonyl chloride, benzene tricarbonyl chloride, or mixtures thereof.
29. The medical device of claim 28, wherein the tricarbonyl halide is cyclohexane-1 ,3,5- tricarbonyl chloride, I .S.δ-trimethyl-I .S.δ-cyclohexanetricarbonyl chloride, trimesoyl chloride, or mixtures thereof.
30. The medical device of claim 23, wherein D is OH, wherein the mixture comprises a carbodiimide.
31. The medical device of claim 30, wherein the carbodiimide is a resin-bound carbodiimide, wherein the mixture comprises optionally a resin-bound 1 -hydroxybenzotriazole as catalyst.
32. The medical device of claim 30, wherein the mixture further comprises an amino acid.
33. The medical device of claim 23, wherein the multifunctional compound comprises an ethylenically unsaturated group and a carboxylic acid group, wherein the reaction between the multifunctional compound and the amine-capped poly(oxyalkylene)-containing polyamide occurs in the presence of a carbodiimide.
34. The medical device of claim 33, wherein the carbodiimide is a resin-bound carbodiimide.
35. The medical device of claim 23, wherein the crosslinkable poly(oxyalkylene)-containing prepolymer has formula (4)
CP-(Q)q (4) wherein q is an integer of >3, Q is an organic radical that comprises at least one crosslinkable group, CP is a multivalent linear or branched copolymer fragment comprising comprising segments A, A1, T, and optionally segments G, wherein: A is the bivalent radical of — (R1- O)n- (R2-O)n,- (R3-O)P— , wherein R1, R2, and R3, independently of one other, are each linear or branched C2-C4-alkylene or hydroxy- substituted C2-C8 alkylene radical, and n, m and p, independently of one another, are each a number from 0 to 500, wherein the sum of (n+m+p) is 5 to 1000;
G is a linear or branched C3-C24 aliphatic trivalent radical, a C5-C45 cycloaliphatic trivalent radical, a C5-C45 aliphatic-cycloaliphatic trivalent radical, or a C3-C24 aromatic or araliphatic trivalent radical;
A1 is a linear or branched C2-C24 aliphatic bivalent radical, a C5-C24 cycloaliphatic or aliphatic- cycloaliphatic bivalent radical, a C6-C24 araliphatic bivalent radical, or aliphatic-heterocyclic bivalent radical, each of which is interrupted by at least one group of formula — NRm— in which Rm is hydrogen, a radical Q mentioned above or a radical of formula
O — C-CP'- Q (4') wherein Q is as defined above, and CP' is a bivalent copolymer fragment comprising one or more segments selected from the group consisting of A, A1, T and G; T is a bivalent radical of formula
RA C N
O (5), wherein RA is hydrogen, an unsubstituted CrC6 alkyl, or a substituted C1-C6 alkyl; provided that in the copolymer fragments CP and CP' a segment A is linked to a segment A1 or G through a segment T; provided that the C atom of -CO— is bonded to a segment A1 or G when Rm is a radical of formula (4'); provided that Q is linked to the copolymer fragment CP or CP' through a segment T.
36. The medical device of claim 35, wherein Q is :
(i) an organic radical R5 which is an olefinically unsaturated copolymerizable radical having 2 to 24 carbon atoms which may be further substituted; or
(ii) a radical of formula -(NH Jn-Q1 or — O— Q1, wherein Q1 is a radical of formula
O (-Z-O— C4S-R5 (6a))
Figure imgf000057_0001
O o*c' ^C-P1'
^7 — NH- C— O— alk — N— alk'— N^
(6d), or
O Il -Z" — NH-C- "R5 (6e), and wherein
Z is linear or branched C2-Ci2alkylene,
R5 is an olefinically unsaturated copolymerisable radical having from 2 to 24 carbon atoms which may be further substituted,
W is a C2-Ci2alkylene radical, phenylene radical or C7-C12aralkylene radical, each of R6 and R6' independently of each other is hydrogen, CrC4alkyl or halogen,
R7 is a bivalent aliphatic, cycloaliphatic, aliphatic-cycloaliphatic, aromatic or araliphatic hydrocarbon radical,
R8 is hydrogen or C1-C4alkyl, each of alk and alk1 independently of the other is a linear or branched CrC12alkylene radical, each of r and s independently of each other is the number 0 or 1 ,
Z" is CrC6alkylene and
P1 and P1' independently of each other are a radical of a radical of formula
-(NH ^-Q1 Or -O-Q1.
37. The medical device of claim 19, wherein Q is a radical of formula
H or CH3 C=CH2 (6')
Figure imgf000057_0002
(6") O H or CH3 Il I NH — (CH2)2-4 — 0-C-C=CH2 (6'")
Figure imgf000058_0001
wherein for R7 the meanings and preferences given above apply in each case.
38. The medical device of claim 37, wherein Q is a radical of formula -(NH ^-Q1 wherein r is 0 and Q1 is a radical of formula (6a) wherein m is 0, R5 is a radical of formula
Figure imgf000058_0002
wherein t is the number 0 or 1 , R9 is hydrogen, C1-C4alkyl or halogen, each of R10 and Rn independently of the other is hydrogen, d-C4alkyl, phenyl, carboxy or halogen, and Z' is linear or branched d-C^alkylene or unsubstituted or CrC4alkyl- or C1-C4BIkOXy- substituted phenylene or C7-C12aralkylene.
39. The medical device of claim 37, wherein Q is a radical of formula -(NH ) — Qi wherein r is 1 and Q1 is a radical of formula (6a) wherein s is 1 , R5 is a radical of formula
Figure imgf000059_0001
wherein t is 0,
Rg is hydrogen, CrC4alkyl, R10 is hydrogen, methyl, chlorine or phenyl, Rn hydrogen or carboxy, and Z' is linear or branched C^C^alkylene.
40. The medical device of claim 23, wherein the medical device is a contact lens.
41. A method for making a contact lens, comprising the steps of:
(I) introducing a fluid lens-forming material into a mold, wherein the fluid lens-forming material is (i) a liquid or melt of a crosslinkable poly(oxyalkylene)-containing copolymer prepolymer in the presence or in the absence of one or more additional vinylic comonomers and optionally in the presence of a photo-initiator, or (ii) an aqueous solution of the crosslinkable poly(oxyalkylene)-containing copolymer prepolymer at a concentration of from 30% to 90% by weight, wherein the liquid or melt optionally is essentially free from solvents, wherein the aqueous solution optionally contains one or more compounds selected from the group consisting of physiologically compatible salts, isotonizing agents conventionally used in the field of contact lens care, vinylic comonomers and photo-initiators;
(II) initiating by actinic irradiation crosslinking of the crosslinkable poly(oxyalkylene)- containing copolymer prepolymer; and
(III) opening the mold so that the contact lens is removed from the mold, wherein the prepolymer is a reaction product of an amine-capped poly(oxyalkylene)- containing polyamide and a multifunctional compound having at least one ethylenically unsaturated group and a function group coreactive with the capped amine groups of the amine-capped poly(oxyalkylene)-containing polyamide, wherein the amine-capped poly(oxyalkylene)-containing polyamide is a copolymerization product of a mixture comprising the components of
(a) at least one aminoalkyl polyalkylene glycol of formula (1) CG-(R1-O)n-(R2-O)1n-(R3 -O)p-CG' (1 ) wherein CG and CG' independently of each other are a primary or secondary amino group, or an amino-Ci-C12 alkyl, R1, R2, and R3, independently of one other, are each linear or branched C2-C4-alkylene or hydroxy-substituted C2-C8 alkylene radical, and n, m and p, independently of one another, are each a number from 0 to 100, wherein the sum of (n+m+p) is 5 to 1000,
(b) optionally at least one organic di- or poly-amine, wherein the organic diamine is a linear or branched C2-C24 aliphatic diamine, a C5-C24 cycloaliphatic or aliphatic-cycloaliphatic diamine, or a C6-C24 aromatic or araliphatic diamine, and wherein the organic poly amine is a compound of formula
HN-B1 1 — NH i I
R4 R4 1 (2), wherein R4 and R4' independently of each other are hydrogen or unsubstituted or substituted C1-C6 alkyl or together are a direct, ring-forming bond, and B1' is a bivalent radical selected from the group consisting of a linear or branched C3-C24alkylene, an unsubstituted C6- C10arylene, a C1-C4 alkyl-substituted C6-C10 arylene, a C7-C18 aralkylene, C6-C10 arylene-d- C2 alkylene-C6-C10arylene, C3-C8 cycloalkylene, C3-C8 cycloalkylene-CrCe alkylene, C3-C8 cycloalkylene-d-C alkylene-C3-C8 cycloalkylene or C1-C6 alkylene-C3-C8 cycloalkylene-Cr C6 alkylene, each of which is interrupted by at least one bivalent amine group ( — NH — ) or has a primary or secondary amine group,
(c) at least one dicarboxyl derivative which is an organic compound with two groups of O
Il
— C-D, wherein D is halide, OH, or alkoxyl, cycloakoxyl, or aralkoxyl, wherein the dicaroxyl derivative is derived from a linear or branched C3-C24 aliphatic dicarboxylic acid, a C5-C24 cycloaliphatic or aliphatic-cycloaliphatic dicarboxylic acid, a C6-C24 aromatic or araliphatic dicarboxylic acid, or a dicarboxylic acid which contains amino or imido groups or N- heterocyclic rings,
(d) at least one polycarboxyl derivative which is an organic compound with three or more
O
Il groups of — C-D, wherein D is defined above, and
(e) optionally a carbodiimide.
42. The method of claim 41 , said radiation-curable prepolymer is substantially purified before introducing step.
43. The method of claim 42, wherein the fluid forming material is the aqueous solution, said radiation-curable prepolymer is substantially purified before introducing step.
44. The method of claim 43, wherein said aqueous solution contains buffer salts conventionally used in the field of contact lens care and/or isotonizing agents conventionally used in the field of contact lens care.
45. The method of claim 42, wherein the fluid forming material is the liquid or melt.
46. The method of claim 45, further comprising the step of (IV) hydrating said contact lens in water, in an aqueous salt solution having an osmolarity of about 200 to 450 mOsm/ml, or in a mixture of water or an aqueous salt solution with a physiologically compatible polar organic solvent.
PCT/EP2005/012438 2004-11-22 2005-11-21 Crosslinkable poly(oxyalkylene)-containing polyamide prepolymers WO2006053777A1 (en)