WO2006047746A1 - Water-borne dispersions of oil modified urethane polymers - Google Patents
Water-borne dispersions of oil modified urethane polymers Download PDFInfo
- Publication number
- WO2006047746A1 WO2006047746A1 PCT/US2005/038983 US2005038983W WO2006047746A1 WO 2006047746 A1 WO2006047746 A1 WO 2006047746A1 US 2005038983 W US2005038983 W US 2005038983W WO 2006047746 A1 WO2006047746 A1 WO 2006047746A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- acid
- component
- polyol
- polyurethane prepolymer
- mixtures
- Prior art date
Abstract
Description
Claims