WO2006028666A2 - Light weight fire-blocking insulation blanket with improved durability and handleability - Google Patents
Light weight fire-blocking insulation blanket with improved durability and handleability Download PDFInfo
- Publication number
- WO2006028666A2 WO2006028666A2 PCT/US2005/029129 US2005029129W WO2006028666A2 WO 2006028666 A2 WO2006028666 A2 WO 2006028666A2 US 2005029129 W US2005029129 W US 2005029129W WO 2006028666 A2 WO2006028666 A2 WO 2006028666A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- fire
- insulation blanket
- batting
- blocking material
- insulation
- Prior art date
Abstract
Description
Claims