WO2006017433A2 - Reactivity drift and catalyst degradation in polyurethane foam - Google Patents
Reactivity drift and catalyst degradation in polyurethane foam Download PDFInfo
- Publication number
- WO2006017433A2 WO2006017433A2 PCT/US2005/027244 US2005027244W WO2006017433A2 WO 2006017433 A2 WO2006017433 A2 WO 2006017433A2 US 2005027244 W US2005027244 W US 2005027244W WO 2006017433 A2 WO2006017433 A2 WO 2006017433A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- acid
- catalyst
- component
- blowing agent
- molar equivalent
- Prior art date
Abstract
Description
Claims