WO2006011684A1 - Oxide superconducting film and method of preparing the same - Google Patents
Oxide superconducting film and method of preparing the same Download PDFInfo
- Publication number
- WO2006011684A1 WO2006011684A1 PCT/JP2005/014367 JP2005014367W WO2006011684A1 WO 2006011684 A1 WO2006011684 A1 WO 2006011684A1 JP 2005014367 W JP2005014367 W JP 2005014367W WO 2006011684 A1 WO2006011684 A1 WO 2006011684A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- film
- substrate
- prepare
- solution
- carbon atoms
- Prior art date
Abstract
Description
Claims