WO2005111145A1 - Scratch resistant propylene polymer composition - Google Patents
Scratch resistant propylene polymer composition Download PDFInfo
- Publication number
- WO2005111145A1 WO2005111145A1 PCT/US2005/011825 US2005011825W WO2005111145A1 WO 2005111145 A1 WO2005111145 A1 WO 2005111145A1 US 2005011825 W US2005011825 W US 2005011825W WO 2005111145 A1 WO2005111145 A1 WO 2005111145A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- polymer
- weight
- parts
- wax
- composition
- Prior art date
Abstract
Description
Claims