WO2005106417A2 - Strain sensors based on nanowire piezoresistor wires and arrays - Google Patents

Strain sensors based on nanowire piezoresistor wires and arrays Download PDF

Info

Publication number
WO2005106417A2
WO2005106417A2 PCT/US2004/039302 US2004039302W WO2005106417A2 WO 2005106417 A2 WO2005106417 A2 WO 2005106417A2 US 2004039302 W US2004039302 W US 2004039302W WO 2005106417 A2 WO2005106417 A2 WO 2005106417A2
Authority
WO
WIPO (PCT)
Prior art keywords
nanowire
piezoresistive
strain gauge
providing
piezoresistive wire
Prior art date
Application number
PCT/US2004/039302
Other languages
French (fr)
Other versions
WO2005106417A3 (en
Inventor
Hongxing Tang
Michael L. Roukes
Original Assignee
California Institute Of Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by California Institute Of Technology filed Critical California Institute Of Technology
Publication of WO2005106417A2 publication Critical patent/WO2005106417A2/en
Publication of WO2005106417A3 publication Critical patent/WO2005106417A3/en

Abstract

A highly sensitive and ultra-high density array of electromechanical nanowires is fabricated. Nanowires are extremely sensitive to the strain induced by the attachment of biological and chemical species. Real-time detection is realized through piezoresistive transduction from the specially designed materials that form the nanowires. These specially designed materials include doped silicon or germanium, doped III-V semiconductors such as GaAs, GaN and InAs systems, and ultra-thin metal films.

Description

STRAIN SENSORS BASED ON NANOWIRE PIEZORESISTOR WIRES AND ARRAYS
U.S. Provisional Patent Application Serial No. 60/468,452, filed on May 7, 2003, and PCT Patent Applications Serial Nos. PCT/US03/14566, PCT/US03/14284, and PCT/US03/14286, all filed on May 7, 2003, are incorporated herein by reference in their entirety.
Background of the Invention
1. Field of the Invention The invention is directed to the field of electromechanical piezoresistive nanowire arrays, and in particular nanowire arrays fabricated with doped silicon or germanium, doped lll-V semiconductors such as GaAs, GaN and InAs systems, and ultra-thin metal films and used for real-time detection of biological and chemical analytes.
2. Description of the Prior art Quantification of Piezoresistors Fundamentally, all strain gauges are designed to convert mechanical
motion into an electronic signal. A piezoresistor is basically a device which changes its resistance when strained. The change in resistance is proportional to the strain experienced by the sensor. The strain sensitivity, which is also called the gage factor (GF), is given by:
(1 )
Figure imgf000004_0001
where R is the resistance, and L the length of the piezoresistor. There are two components of the piezoresistive effect in most materials: (1) the geometric component and (2) the resistivity components. When a conducting wire is stretched, it becomes longer and thinner. Its resistance increases according to the Ohm's law. A good example of geometric effect is the liquid strain gauge, such as those made of mercury. When compressed, a tube of mercury becomes shorter in length and larger in diameter to maintain a constant volume. The resistance of such a strain gauge is given by pL pJx R (2) A V where p is the resistivity, A is the cross sectional area, L is the length and V the volume of the strain gauge. Therefore,
Figure imgf000004_0002
This means that all liquid gauges have a gauge factor of 2, since essentially all liquid medium is incompressible. Before replaced by solid stage strain gauge instruments, liquid gauges were extensively used in hospitals to monitor the fluctuations in blood pressure. Metal wires can also be used as strain gauges. Normally metal cannot be treated as incompressible nor is its resistivity constant. The gauge factors can be expressed by following Ohm's law:
R=pL/A dR/R=dp/ p + dLIL -dAIA (4) G =_-^=1+2v+χχ dLIL dLIL
dA/ A
In the above, v is defined as Poisson's ratio . For different metals, this 2dL.lL quantity depends on the material mechanical properties as well as the conduction mechanism. In general metals have. gauge factors between 2 and 4.
In equation (3) above, the first component of the gauge factor is a pure geometrical mechanism, but piezoresistive sensing usually refers specifically to strain gauges in semiconductors, whose conducting band changes in response to stress. Some doped semiconductors have a gauge factor over 100 times greater than those attributable to geometric changes alone. Gat-iqe Facto Q Msϊal Foi 1 to 5 ϋ:K,ι' ri Th:.fi-fiiϋ;m metal 2 Gr = Semiconductor 80 to ISO dL L Diffused Serτiι£ύ3 du;Ctcr .80 So 200
Brief Summary of the Invention The invention is shown in the illustrated embodiment as a nanowire strain gauge comprising a piezoresistive wire having a cross sectional area of the order of 100 nm x 100nm or less and a means for measuring resistance change in the piezoresistive wire in response to a transverse force applied to the piezoresistive wire. In one embodiment the piezoresistive wire comprises a free standing nanowire clamped at opposing ends. The nanowire strain gauge may further comprise a biofunctionaiized element suspended by and connected to the free standing nanowire. In another embodiment the nanowire strain gauge further comprises a flexure element and the piezoresistive wire comprises an embedded piezoresistive wire in the fiexure element. The flexure element comprises in one illustrated embodiment at least one arm in a notched nanocantilevers and preferably in a pair of such parallel, arms. The piezoresistive wire may further comprise an array of piezoresistive wires embedded in the flexure element. In a . first example the piezoresistive wire comprises a thin metal film with a thickness of the order of tens of nanometers or less or of such thickness that it comprises a discontinuous metal island structure. Examples of such thin metal films comprise a pure metal selected from the group consisting of Au, Cr, Ag, Pd, Ni, Pt, n and alloys, Au-Ni, NiCr, Bi-Sb, Ag-NI, Cu-Ni, and Pt-Cr. The piezoresistive wire may also comprise a thin metal film included in a bimorph structure comprised of a top layer comprised of the thin metal film and a bottom layer comprised of a higher resistive metal layer than the top layer, a semiconductor layer or an insulating layer. Still further the piezoresistive wire is composed at least in part of doped crystalline silicon, doped silicon carbide, doped GaAs, doped GaxAiι.xAs, where 0 < x < 1 or a doped AIGaN/GaN, AlN/GaN/lnN or GaN/AIN/GaN heterostructure. The invention further comprises a method of manufacturing the nanowire strain gauge described above and the method of measuring stresses and strains at nanoscale dimensions. While the apparatus and method has or will be described for the sake of grammatical fluidity with functional explanations, it is to be expressly understood that the claims, unless expressly formulated under 35 USC 112, are not to be construed as necessarily limited in any way by the construction of "means" or "steps" limitations, but are to be accorded the full scope of the meaning and equivalents of the definition provided by the claims under the judicial doctrine of equivalents, and in the case where the claims are expressly formulated under 35 USC 1 12 are to be accorded full statutory equivalents under 35 USC 112. The invention can be better visualized by turning now to the following drawings wherein like elements are referenced by like numerals.
Brief Description of the Drawings Fig. 1 is a microphotograph of a suspended nanowire with a circular element provided for carrying a biofunctionalized material. Fig. 2 is an array of piezoresistive nanowires.
Fig. 3a is a microphotograph of a notched silicon cantilever that can be used to detect piconanoscale biological forces. Fig. 3b is a sketch of and integrated cantilever system with integrated nanowire piezoresistor array at its base. Fig. 4a is a diagram of a measurement circuit for integrated nanowire strain sensor. Fig. 4b is a schematic for an equivalent sensing circuit that is comprised of the nanowire resistance (Rs) and amplifier input resistance (R0). The piezoresistive ac signal Vs = lb *GF*RS is divided by the resistance network before amplification. Fig. 5a is an equivalent circuit of an ultra-thin metal film nanowire strain sensor. Fig. 5b is a graph of the Impedance I Z I vs frequency for a thin gold film of thickness of 5 nm. Fig. 5c is a graph of the phase angle vs frequency for a thin gold film of
thickness of 5 nm. Fig. 6. Typical bimorph structure that is required for the construction of nanowire sensors.
Fig. 7 is a polar graph of the room temperature piezoresistive coefficients of p-type and n-type silicon on the (100) plane. Fig. 8 is a polar graph of the room temperature piezoresistive coefficients of p-type and n-type Germanium on the (100) plane. Fig. 9 is a polar graph of the absolute value of the piezoresistive constants of p-GaAs and n-GaAs for longitudinal piezoresistive coefficient π in the (001) plane. The unit is 10"11 Pa"1. . Fig. 10 is a scanning electron microscopic photograph of an array of nanovyvires fabricated according to the invention in . which- the resonant frequencies of 18 different wires are measured and indicated. Figs. 1 1 a - 11f is a process diagram of the method whereby the array of Fig. 10 can be made. Fig. 12 is a magnified scanning electron microscopic photograph of an array of nanowires fabricated according to the invention. Fig. 13 is a diagram showing the means by which the measure of the resonant frequencies of the nanowires in the array are individually measured using an electron beam. Figs. 14a and 14b are graphs of thermal response verses frequency showing the resonant spectrum of two different nanowires in the array. Fig. 15 is a graph of thermal response verses frequency showing measurement of higher harmonic modes of a nanowire in an array.
Figs. 16a and 16b are conceptual diagrams illustrating the discontinuous grain or island structure in an unstressed and stressed very thin metal film, respectively, which can be exploited in nanowire arrays to provide substantially enhance gauge factors. The invention and its various embodiments can now be better understood by turning to the following detailed description of the preferred embodiments which are presented as illustrated examples of the invention defined in the claims. It is expressly„understood that the invention as defined by the claims may be broader than the illustrated embodiments described below.
Detai.e Description of the Preferred Embodiments Nanowire Piezoresistor Sensor Design If we were to sense a longitudinal force applied along the piezoresistor, the fractional change in resistance is,
AR / R = GF * F / EA (5)
where E is the Young's modulus, and F is the force applied along the piezoresistor. Clearly, in order to have a large change in resistance, we generally try to choose small diameters, a small Young's modulus and a large gauge factor when possible. In this sense, nanowire piezoresistors, having a cross sectional area of the order 100 nm2 in contrast to that of 106 nm2 in a commercial piezoresistor, wiil have an enhanced resistance change by a factor of
10,000.
In illustrated embodiment, we address a strain gauge 10 that is sensitive to a transverse force. The expression for the resistance change with a transverse force load, F, is generally different from Eq. 5 above. We will consider two classes of nanowire devices: (1 ) free standing nanowires and (2) embedded nanowires.
a. Free Standing Nanowires
The free standing nanowires 12 are extremely small doubly clamped nanobeams as shown in Fig. 1. The analysis of a beam, which is fixed at both opposing ends, is similar to that of cantilever, which is fixed only at one end. For a bimorph beam of dimension I x w x t comprised of a layer of piezoresistor 14 of thickness ts, best illustrated in Fig. 8, a point force load at the center of the beam causes a resistance change of,
Figure imgf000011_0001
Here ττ\ is the piezoresistive coefficient of the sensing material and is closely related to the gauge factor. A simple comparison between Eq. (6) and Eq. (5) shows that for freestanding nanowires 12, the piezoresistive sensitivity can be further improved to a factor of 106.
A demonstrated version of these suspended beams or nanowires 12 has
been fabricated by the inventors. A photograph of nanowires 12 is shown in Fig. 1. The center circular ring 16 is designed as a biological trap to which biological species can be attached after proper biofunctionalization.
The nanowires 12 shown in Fig. 1 are fabricated by the use of electron beam lithography. The achievable size of the beam or nanowire 12 is around 50 nm wide. By using conventional superlattice nanowire pattern transfer technique as described byN. A. Melosh, et.al. Science 300, 112, (2003) suspended beams or nanowires 12 less than 10 nm size can be realized. Fig. 2 is a photograph of an interdigitated nanowire array 18 fabricated by electron beam lithography. In a nanowire piezoresistor array 18, the metal wires 12 are replaced by piezoresistive materials, such as doped Si, GaAs and or other piezoresistive materials.
b. Embedded Nanowires
Due to the difficulty of maintaining a finite conductivity in a nanoscale suspended semiconductor, we also propose a second type sensor design based on nanowire piezoresistors. In PCT Patent Applications serial no. PCT/US03/14566, PCT/US03/14284, and PCT/US03/14286, incorporated herein by reference, we have demonstrated a biofunctionized nanomechanical device that can realize ultra-sensitive and ultra-fast biochemical analysis. A notched cantilever 22 is used to detect biological forces applied on the biofunctionaiized cantilever surface, i.e. a surface coated with a material which selectively binds to a biological analyte. An example of such a device is' shown in Fig. 3a.
The scheme of embedded nanowire piezoresistor array 20 is illustrated in
Fig. 3b, where arrays of nanowires are patterned above two arms 24 of the cantilever 22. The arms 24 of the cantilevers 22 act as an efficient strain concentrator and amplify the torque induced by biological species. The nanowires 12 can be laid out in parallel circuit as shown in Fig. 3b at the base of the cantilever 22 or in a serpentine serial circuit as shown in the inset in Fig. 3b. The above mentioned stress changes can be picked up in the integrated piezoresistor. The relative change in resistance can be written as,
AR / R = -4 GF σs I Et (8) where E is Young's modulus for the piezoresistive material, t is the thickness of the piezoresistive material and σs is the surface stress applied to a flexure element in which the wire is embedded.
Nanowire fabrication - An example
To provide a simple example how the nanowire array 18 is fabricated, an example is presented below. It is to be understood that many variations in the method described here can be practiced without departing from the principle of the disclosed invention.
Fig. 0 is a perspective SEM image of nanowire array 18 fabricated by means of top-down electron beam lithography. The wires 12 are made of Cr/Au and have a dimension of 20μm long, 50nm wide and 50nm thick. A cross sectional view of the nanowire fabrication process is sketched in Figs. 11a - 11f. In Fig. 11a a bare silicon wafer 40 is provided. A layer 42 of Cr/Au is first evaporated on a silicon wafer 40 as shown in Fig. 11b. A FOX resist 44 is then spun on top of Cr/Au surface 42, followed by electron beam exposure of nanowire patterns to provide the patterned deposition of the resist as shown in Fig. 11 c. After the development, the remaining FOX pattern 44 is employed as etch mask in an ion-milling instrument to remove Cr/Au 42 exposed between resist elements 44.. The pattern in FOX is therefore transferred in to Cr/Au layer 42 and partially defined into wafer 40 as shown in Fig. 11d. FOX resist 44 is then removed in the step of Fig. 11e and a final isotropic silicon etch is used as shown in Fig. 11f to suspend Cr/Au beams 42 as wires 12. Fig. 12 is a SEM photograph of the top view of nanowire array 18 fabricated according to the method illustrated in Figs. 11 a - 11f in which array 18 is shown as an 8μm long array.
In-situ Electron Beam characterization of nanowire resonator It should be clear that stresses and strains are not merely measured statically using nanowires 12, but also dynamically as a function of time. Hence, various types of nanostructures may incorporate or be coupled to the nanowires 12 of the invention and the piezoresistivity of nanowires 12 may be measured as a function of time, namely frequency spectrums of the piezoresistivity are obtained. For example, the scale of nanowires 12 is such that thermal fluctuations or thermal molecular motions in the gaseous or fluidic environment in which nanowires 12 are immersed are large enough to osculate or displace nanowires 12. The nanowires 12, being the equivalent of mechanical strings, or taking on the mechanical characteristics of whatever nanostructure in which they are incorporated or to which they are coupled, will have one or more resonant frequencies responsive to the thermal fluctuations or thermal molecular motions, or to whatever other force may be present. In order to explore the piezoresistivity of nanowires 12, it is important to know the resonant frequency of the nanowires 12 through other methods. This will provide a narrow frequency range to search for the resonant peak when piezoresistive detection is employed. An in-situ electron beam detection has been proved to be very useful for this purpose. The measurements are performed at room temperature within a conventional, commercially available scanning electron beam microscope (SEM) as diagrammatically depicted in Fig. 13. Thermal excitation of nanowires 12 will drive them in motion at their respective resonant frequencies. An electron beam is focused on the edge of the target nanowire 12. When the electron beam is focused on a spot on the nanowire 12, the motion of the nanowire 12 will affect the signal detected in a secondary electron detector 46 (SE) or backscatter electron detector 46 (BSE). This signal can be detected by a spectrum analyzer 48 or an oscilloscope equipped fast Fourier transform (FFT) program. The video signal - from detector 46 has a band width greater than 10MHz in most commercial SEM. Therefore, a resonant frequency more than 10MHz can be detected. In Fig. 14a, which is a graph of the thermal response in atomic units verses frequency, a resonant frequency 50 as high as 11 MHz is observed for wire 12, for example a second wire in 8μm long nanowire array 18. Fig. 14b is a graph of the thermal response in atomic units verses frequency, which shows the thermal resonant peak 52 of a wire 12 which is the twentieth wire in the same array 18 of nanowires 12. The inset of Fig. 14b illustrates the resonance peak 52 in a magnified view. The quality factor is about 1800. Due to the intrinsic high resolution of this method, higher harmonic modes of thermal mechanical motion can be measured. Data is shown in Fig. 15 which is a graph of the thermal response in atomic units verses frequency, and which is the measured result for the 18th wire 12 in a 20μm long nanowire array 18, showing a resonant peak 56 and two higher harmonic peaks 58 and 60. This in-situ measurement can measure the resonant frequency of each individual wire 12 in a nanowire array 18 individually. Therefore it is extremely useful for characterizing a large array 18 of nanowires 12. Electrical connection to each individual wire 12 is not required for such a method. Fig. 10 lists the resonant frequencies of different wires 12 in the array 18 depicted there. This electron beam spectroscopy of a nanomechanical resonator can be applied to detect dynamic motion or static motion of a nanomechanical system of other configurations and geometries as well.
Material Aspect Of Making Nanowire Piezoresistor Arrays
Consider now the materials that can be appropriately used to construct piezoresistive nanowires 12. Generally speaking, all conducting materials are piezoresistive, as we have explained above. We will discuss two categories of pie∑oresistors: (1) piezoresistors of geometrical effect and (2) piezoresistors with
varying piezoresistivity. (1) a. Metal thin film piezoresistor
Geometrical effect piezoresistors normally provide a smaller gauge factor, nevertheless they represent a significant amount materials used in commercial gauge sensors. These materials are mostly highly, conductive thin metal films with very low resistivity. To obtain a- larger change in the absolute value of resistance, a lot of effort has been expended to increase the resistance of the sensors. However, for high frequency applications, it is beneficial to maintain a low sensor resistance in order to match the resistance of the sensor with that of the measurement circuit, which is typically 50 Ω. Fig. 4a shows a representative measurement diagram. The signal appear at the input of the network analyzer or lock-in amplifiers is,
'0 s + Kn 0 (9)
where R0 is the input impedance of the measurement amplifier as shown in Fig. 4b and Rs is thin film or nanowire resistance, and Vs is the ac signal (lb x GF x Rs) applied signal across the thin film with lb the bias current applied to the nanowire 12. The maximum signal power spectrum is transferred only when Rs = R0. In this way, the transducer signal will not be significantly degraded. Normally the sheet resistance of semiconducting thin fiim is on the order of 102 Ω to 103 Ω. The two- terminal DC resistance of a high aspect ratio nanowire 12 could be 106 Ω. This makes semiconducting nanowires 12 extremely difficult to be used as a sensing unit in high frequency mechanical resonator. On the other hand, the resistance of metal films can be easily trimmed to specific values by tuning the thickness of the film. On the other hand, comparing to the resistive wires, the Johnson noise, vn ~ Λj4πkTRs t where k is the Boltzman constant, can be reduced by a factor of about 40. Therefore, the signal-to-noise ratio can be compensated even though the gauge factor is about 50 times weaker than for Si wires. The fact that metallic nanowires 12 can work at high frequencies offers another benefit: The drop of 1/f noise that is present in most low frequency strain gages.
Comparing to semiconductor gauges, metal films usually have lower temperature coefficient of resistivity (TCR), and lower temperature coefficient of gauge factor (TCGF). (See table 2.)
Figure imgf000018_0001
Metal thin film sensors can be operated under harsh circumstances, such as high temperatures and high pressure. They are also readily scalable without the depletion limit that exists in most doped semiconductors. The minimum dimension for a semiconductor to be conducting varies from a few nanometers to hundreds of nanometers, depending on the carrier density of the semiconductor. This problem becomes even more severe when dny etching damage is present. Such a process generally becomes obligatory at nanometer length scale.
The invention thus contemplates the use of thin and ultra-thin metal films for strain sensors. The very thin-films typically have thicknesses in the range of tens of nanometers and are characterized by a discontinuous metal island structure as shown in Figs. 16a and 16b. A sketch of such a discontinuous metal island structure of the grains is shown in Fig. 16a when unstressed. The grain structure under stress is illustrated in Fig. 16b where the gap 54 in the grain structure has been widened by the stress applied to the film. This especially true when these metals are used in a nanowire geometry. The discontinuous type of gold thin film has demonstrated a gauge factor from 24 to 48, a much higher value than that of the continuous type which is about 2.6. For ultra thin films, it is not the thickness of thin metal film that determines the sensitivity of the
discontinuous type of ultrathin film.
Pure metal such as Au, Cr, Ag, Pd, Ni, Pt, Mn and alloys, Au-Mi, NiCr, Bi- Sb, Ag-Ni, Cu-Ni, and Pt-Cr are used as materials of metal thin-film-type strain gauges. Their simplicity, reliability and ability to perform in a wide range of environmental conditions have made these gauges available in may shapes, patterns and configurations. The Table below summarizes the gauge factors of
thin metal films that have been explored in literature.
Figure imgf000019_0001
Figure imgf000020_0001
However, constructed at a comparably large scale, they have a lower sensitivity than nanowires 12 implemented according to the invention.
Our choice of thin film metallic materials to construct nanowires 12 is largely dependent on the actual fabrication process and the conductivity of the metal. Many methods of deposition methods can be employed: evaporation, sputtering, CVD etc. For embedded metal wires, the design is straightforward in the sense that only the surface strain is required to be measured. In the case of free-standing metal nanowires, the fabrication is not trivial. Usually a bimorph
structure has to be incorporated to avoid the compensation of tensile strain and compressive strain at the top surface 26 and bottom surface 28 of the suspended beam or wire 12 as shown in Fig. 8. The bottom layer 28 of the bimorph structure is usually insulating or has higher resistivity than the piezoresistor so that most of the current flows through the piezoresistor to gain maximum strain sensitivity. For thin film metal piezoresistors, the bottom layer 28 could be simply another higher resistive metal layer such as Au/Cr. or a semiconductor such as Metal/Si, Metal/SIC, Metal/GaAs etc, or an insulating layer such as Jvletal/S.02, Metal/SiN, Metal/SiNO etc.
b. Si Based Nanowire Piezosensors
It is well known that piezoresistance of silicon can be used as a sensing element for mechanical sensors, such as diaphragm type pressure sensors. This is due to the excellent electrical and mechanical properties of silicon. and due to the availability of integrated circuit compatible fabrication processes. First consider the mechanical properties of silicon. For single crystal silicon of cubic structure, the Young's modulus E depends on the crystal orientation,
E~1 = s11 - 2(511 - s12 - f s r (10)
where r = γι2 y2 2 + Y22 Y32 + Y32 y-i2 and γ1 ( γ2 and γ3 are the direction cosines, and S11, Si2 and s 4 are the matrix elements in the strain tensor. The resulting Young's moduli for silicon in the predominant crystallographic directions are
given in Table 4. Si Si Si <100> <110> <111> E (GPa) 166 170 190 P (kg/m3) 2333 2333 2333
In most case, the mechanical anisotropy of silicon is not significant and can be ignored in the sensor design. Piezoresistive coefficients are frequently used in semiconductor strain gauges. A piezoresistor responds to stress σ as,
Δ π(σ (11) P
Where TΠ, is the longitudinal piezoresistive coefficient. There also exists a transverse piezoresistive coefficient, usually denoted as ττt. Analogously to the modulus of elasticity, the piezoresistive coefficients are determined by "rrii. πi^an
πt = ττιι — 2(ττιι — ττι2 - τr44)r (12)
Coefficients for p-type and n-type silicon is given in the table below. [1011 m2/N] [10 1 m2/N] [1011 m2/N] n-Si (11.7 Dcm) -102.2 53.4 -13.6 p-Si (7.8.7 Dcm) 6.6 -1.1 138.1 n-Ge (9.9 Dcm) -4.7 -5.0 -137.9 p-Ge (15 Dcm) -10.6 5.0 46.5
Fig. 7 is a graph which shows the room temperature piezoresistive coefficients of both p-type and n-type silicon in the (100) plane. It can be seen that p-type silicon has its maximum piezoresistive coefficient of -72 x 10"11 m2/N in the <110> direction; while n-type silicon has its maximum of -103 x 10"11 m2/N in the <100> direction. Although n-type silicon can achieve piezoresistive coeffecients much higher than that of p-type silicon, all piezoresistive sensors fabricated to date, including pressure sensors, accelerometers, and AFM cantilevers are doped p-type. This is partially for historical reasons. Traditional MEMS devices rely on wet etching of Si, such as TMAH and KOH etchants, which etch silicon preferentially to expose the (111) plane. Therefore the membrane edge on the front side is always in parallel to <110> direction, where p silicon has maximum piezoresistive coefficient while n silicon has minimum piezocoefficient. B y using a deep reactive ion etching DRIE technique, nanowires or nanocantilevers 12 can be easily patterned and released along any chosen crystal orientation, therefore improving the piezoresistivity.
The difficulty in making ohmic contacts between metal and n-type silicon is
another concern. But this limitation can be also overcome with current fabrication techniques, for example, Al' contact deposition followed by ion-cleaning of the contact windows.
Both p-type and n-type germanium can be used as strain sensor. The piezocoefπcients are listed in the Table above and plotted in Fig. 8. germanium wires have the benefits of higher' conductivity and ease in making ohmic contacts.
c. SiC Piezoresistor
Silicon carbide has long been viewed as a potentially useful semiconductor for high-temperature applications due to its excellent electrical characteristics. Its wide bandgap (-3.0 eV), high-breakdown electric field (2.5x106Vcrτf1) and high electron saturation velocity (2x107cm/s) make it a superior candidate for electronic applications in a harsh environment. Added to these, SiC 'exhibits excellent thermal and mechanical properties at high temperatures and fairly high piezoresistive coefficients, a combination which makes it suitable for use as an electromechanical sensor.
d. Groups lll-V Based Semiconductor Nanowire Piezosensors
I. The piezoresistive effect of GaAs andAlGaAs
It is generally known that GaAs electronic circuits have a higher tolerance in high temperature and high radiation environments than that in silicon integrated circuits. On the other hand, GaAs membranes can be easily obtained by selectively etching the GaAs/AIGaAs heterostructures. In addition, GaAs
?? nanowires are compatible with integrated high electron mobility transistor (HEMT) amplifiers. This becomes extremely important when the impedance of the piezoresistive wires are significantly larger than the input resistance of the measurement circuits.
As discussed above, it has been well established that the piezoresistive effect of silicon is due to a directional dependent modulation of the average mobility in response to a uniaxially applied stress. But unlike Si, GaAs is a direct band semiconductor. This effect is not as high. Fig. 9 shows the a typical plot of the piezoresistive coefficients of p-type GaAs.
In addition to the effect of mobility changes, nonuniform stress distribution introduced into GaAs can produce piezoelectric charge densities and effectively shift the free charge densities originally established by doping. This effect becomes dominant for low doping level GaAs.
GaxAlq.xAs with x lying between 25 and 40% can be used to develop highiy sensitive strain gauges. Deep impurity states (DX centers) play a dominant role in the electrical conduction band. In contrast to shallow impurity states, which exhibit a relatively small pressure coefficient, the energy of DX states compared to the T minimum of the conduction band decreases at a rate of 10meV/kbar. As a consequence, one could observe a significant piezoresisitvity effect. In one embodiment, a device containing an optimized AlxGaι_xAs layer with thickness in the micrometer range, grown on semi-insulating GaAs substrate showed a gauge factor as high as 60.
ID //. The piezoresistive effect ofAIGaN based materials
Solids with a large bandgap such as diamond or gallium nitride are prime candidates for a variety of sensor applications, particularly at high temperatures and in harsh environments. On the one hand; the large band gap ensures minimal problems due to unwanted optical or thermal generation of charge carriers. On the other hand, the strong chemical bonding between the constiuent atoms not only widens the forbidden gaps in the electronic density of states, but at the same time gives rise to a quite favorable mechanical, thermal and chemical stability of this class of materials. Strong piezoelectricity provides unique possibilities for utilizing AIN-GaN materials in an emerging field of high temperature piezoeiectronics. The piezoelectric effect plays an important role in GaN layers, AIGaN-GaN, AIN-GaN- InN heterostructures and quantum wells. Strain-induced electric fields can significantly modify the electrical properties of GaN-based devices by affecting the free carrier concentration. High dynamic piezoresistive effect with a gauge factor of about 70 has been' reported in n-type GaN layers. A large static gauge factor of about 50 was measured in GaN/AIN/GaN semiconductor-insulator-semiconductor structures. In AIN-GaN short range superlattices, it has been demonstrated that GF can reach 90, which is close to GFs of silicon diaphragms.
The piezoresistivity of AixGa-ι-xN layers with different Al contents and electron concentration have been investigated in the prior art. A strong increase
of the gauge factor with increasing Al content is observed. The corresponding value is negative and its absolute value increases from 3.5 to 25.8 if the Al concentration is increased from x = 0 to 0.35. In addition, a remarkably high gauge factor of -85 is observed for modulation doped AlGaN/GaN high electron mobility transistors containing a polarization induced two-dimensional electron gas.
Many alterations and modifications may be made by those having ordinary skill in the art without departing from the spirit and scope of the invention. Therefore, it must be understood that the illustrated embodiment has been set forth only for the purposes of example and that it should not be taken as limiting the invention as defined by the following claims. For example, notwithstanding the fact that the elements of a claim are set forth below in a certain combination, it must be expressly understood that the invention includes other combinations of fewer, more or different elements, which are disclosed in above even when not initially claimed in such combinations. The words used in this specification to describe the invention and its various embodiments are to be understood not oniy in the sense of their commonly defined meanings, but to include by special definition in this specification structure, material or acts beyond the scope of the commonly defined meanings. Thus if an element can be understood in the context of this specification as including more than one meaning, then its use in a claim must be understood as being generic to all possible meanings supported by the specification and by the word itself. The definitions of the words or elements of the following claims are, therefore, defined in this specification to include not only the combination of elements which are literally set forth, but all equivalent structure, material or acts for performing substantially the same function in substantially the same way to obtain substantially the same result. In this sense it is therefore contemplated that an equivalent substitution of two or more elements may be made for any one of the elements in the claims below or that a single element may be substituted for two or more elements in a claim. Although elements may be described above as acting in certain combinations and even initially claimed as such, it is to be expressly understood that one or more elements from a claimed combination can in some cases be excised from the combination and that the claimed combination may be directed to a subcombination or variation of a subcombination. Insubstantial changes from the claimed subject matter as viewed by a person with ordinary skill in the art, now known or later devised, are expressly contemplated as being equivalent^ within the scope of the claims. Therefore, obvious substitutions now or later known to one with ordinary skill in the art are defined to be within the scope of the defined elements. The claims are thus to be understood ϊo include what is specifically illustrated and described above, what is conceptionally equivalent, what can be obviously substituted and also what essentially incorporates the essential idea of the invention.

Claims

We claim:
1. A nanowire strain gauge comprising: a piezoresistive wire having a cross sectional area of the order of 100 nm2or • less; and means for measuring resistance change in the piezoresistive wire in response to a transverse force applied to the piezoresistive wire.
2. The nanowire strain gauge of claim 1 where the piezoresistive wire comprises a free standing nanowire clamped at opposing ends.
3. The nano vire strain gauge of claim 2 further comprising a biofunctionalized element suspended by and connected to the free standing nanowire.
4. The nanowire strain gauge of claim 1 further comprising a flexure element and where the piezoresistive wire comprises an embedded piezoresistive wire in the flexure element.
5. The nanowire strain gauge of claim 4 where the flexure element comprises at
least one arm in a notched nanocantilever.
6. The nanowire strain gauge of claim 1 further comprising a flexure element and where the piezoresistive wire comprises an array of piezoresistive wires embedded in the flexure element.
7. The nanowire strain gauge of claim i where the piezoresistive wire comprises a thin metal film.
8. The nanowire strain gauge of claim 7 where the thin metal film comprises a film with a thickness of the order of tens of angstroms or less.
9. The nanowire strain gauge of claim 7 where the thin metal film has a thickness such that the film comprises a discontinuous metal island structure.
10. The nanowire strain gauge of claim 8 where the thin metal film comprises a pure metal composition selected from the group consisting of Au, Cr, Ag, Pd, Ni, Pt, Mn and alloys, Au-Ni,' NiCr, Bi-Sb, Ag-Ni, Cu-Ni, and Pt-Cr.
11. The nanowire strain gauge of claim 4 where the piezoresistive wire comprises a thin metal film included in a bimorph structure comprised of a top layer comprised of the thin metal film and a bottom layer comprised of a higher resistive metal layer than the top layer, a semiconductor layer or an insulating layer.
12. The nanowire strain gauge of claim 1 where the piezoresistive wire comprises doped crystalline silicon.
13. The nanowire strain gauge of claim 1 where the piezoresistive wire comprises doped silicon carbide.
14. The nanowire strain gauge of claim 1 where the piezoresistive wire comprises doped GaAs.
15. I he nanowire strain gauge of claim 1 where the piezoresistive wire comprises doped GaxAlι-xAs, where 0 < x < 1.
16. The nanowire strain gauge of claim 1 where the piezoresistive wire comprises a doped AlGaN/GaN, AIN/GaN/lnM or GaN/AIN/GaN heterostructure.
17. A nanowire strain gauge comprising: a free standing piezoresistive nanowire having a cross sectional area of the order of 100 nm2 or less and clamped at opposing ends; and means for measuring resistance change in the piezoresistive wire in response to a transverse force applied to the piezoresistive wire.
18. The nanowire strain gauge of claim 17 further comprising a biofunctionalied element suspended by and connected to the free standing nanowire.
9. The nanowire strain gauge of claim 17 where the piezoresistive wire comprises a thin metal film with a thickness of the order of tens of angstroms or less, doped crystalline silicon, doped silicon carbide, doped GaAs, doped GaxAlι.xAs, where 0 < x < 1 , or a doped AIGaN/Gatf, AIN/GaN/lnN or GaN/AlN/GaN heterostructure.
20. A nanowire strain gauge comprising: a flexure element; a piezoresistive wire embedded in the flexure element, the piezoresistive wire having a cross sectional area of the order of 100 nm2 or less; means for measuring resistance change in the piezoresistive wire in response to a transverse force applied to the piezoresistive wire.
21. The nanowire strain gauge of claim 20 further comprising a plurality of piezoresistive wires forming an array of embedded piezoresistive wires in the flexure
element.
22. The nanowire strain gauge of claim 20 where the piezoresistive wire comprises a thin metal film included in a bimorph structure comprised of a top layer comprised of the thin metal film and a bottom layer comprised of a higher resistive metal layer than the top layer, a semiconductor layer or an insulating layer, doped crystalline silicon, doped silicon carbide, doped GaAs, doped GaxAlι-xAs, where 0 < x < 1 or a doped AlGaN/GaN, AIN/GaN/lnN or GaN/AIN/GaN hetero structure.
23. A method of measuring strain at nanoscales comprising: providing nanowire strain gauge comprised of a piezoresistive wire having a cross sectional area of the order of 100 nm2 or less; stressing the piezoresistive wire with a force having a transverse component; and measuring resistance change in the piezoresistive wire in response to the transverse component of the force applied to the piezoresistive wire.
24. The method of claim 23 where providing nanowire strain gauge comprised of a piezoresistive wire comprises providing a free standing nanowire clamped at opposing ends and where stressing the piezoresistive wire comprises applying the force to the nanowire between the opposing ends.
25. The method of claim 24 further comprising reacting a biofunctionalized element suspended by and connected to the free standing nanowire with a target molecule, oscillating the nanowire at a resonant frequency, and measuring modification of the resonant frequency of the nanowire due to the reaction with the target molecule.
26. The method of claim 13 further comprising providing a flexure element in which the piezoresistive wire comprises an embedded piezoresistive wire so that stressing the piezoresistive wire comprises stressing the flexure element.
27. The method of claim 26 where providing a flexure element comprises providing at least one arm in a notched nanocantilevers to serve as the flexure element.
28. The method of claim 23 further comprising providing a flexure element and where the piezoresistive wire further comprises an array of piezoresistive wires embedded in the flexure element.
29. The method of claim 23 where providing nanowire strain gauge comprised of a piezoresistive wire comprises a thin metal film.
30. The method of claim 29 where providing the thin metal film comprises providing a film with a thickness of the order of tens of angstroms or less.
31. The method of claim 29 where providing the thin metal film provides a film with a discontinuous metal island structure.
32. The method of claim 30 where providing the thin metal film comprises providing a film with a pure metal composition selected from the group consisting of Au, Cr, Ag, Pd, Ni, Pt, Mn and alloys, Au-Ni, MiCr, Bi-Sb, Ag-Ni, Cu-Ni, and Pt-Cr.
33. The method of claim 26 where providing the piezoresistive wire comprises providing a thin metal film included in a bimorph structure comprised of a top layer comprised of the thin metal film and a bottom layer comprised of a higher resistive metal layer than the top layer, a semiconductor layer or an insulating layer.
34. I he method of claim 23 where providing the piezoresistive wire comprises providing doped crystalline silicon.
35. The method of claim 23 where providing the piezoresistive wire comprises providing doped silicon carbide.
36. The method of claim 23 where providing the piezoresistive wire comprises providing doped GaAs.
37. The method of claim 23 where providing the piezoresistive wire comprises
providing doped GaxAl^ s, where 0 < x < 1.
38. The method of claim 23 where providing the piezoresistive wire comprises
providing a doped AlGaN/GaN, AlN/GaN/lnN or GaN/AIN/GaN heterostructure.
PCT/US2004/039302 2004-04-16 2004-11-24 Strain sensors based on nanowire piezoresistor wires and arrays WO2005106417A2 (en)