WO2005097318A1 - A process for preparing a silver catalyst, the catalyst, and its use for oleffin oxidation - Google Patents
A process for preparing a silver catalyst, the catalyst, and its use for oleffin oxidation Download PDFInfo
- Publication number
- WO2005097318A1 WO2005097318A1 PCT/US2005/010996 US2005010996W WO2005097318A1 WO 2005097318 A1 WO2005097318 A1 WO 2005097318A1 US 2005010996 W US2005010996 W US 2005010996W WO 2005097318 A1 WO2005097318 A1 WO 2005097318A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- catalyst
- support
- rhenium
- silver
- promoter
- Prior art date
Abstract
Description
Claims