WO2005063841A1 - Process for producing polyurethane products autocatalytic using tertiary amine capped polyether polyols - Google Patents
Process for producing polyurethane products autocatalytic using tertiary amine capped polyether polyols Download PDFInfo
- Publication number
- WO2005063841A1 WO2005063841A1 PCT/US2004/043463 US2004043463W WO2005063841A1 WO 2005063841 A1 WO2005063841 A1 WO 2005063841A1 US 2004043463 W US2004043463 W US 2004043463W WO 2005063841 A1 WO2005063841 A1 WO 2005063841A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- polyol
- reaction
- tertiary amine
- polyols
- amine
- Prior art date
Abstract
Description
Claims