WO2005047564A2 - Method of improving post-develop photoresist profile on a deposited dielectric film - Google Patents
Method of improving post-develop photoresist profile on a deposited dielectric film Download PDFInfo
- Publication number
- WO2005047564A2 WO2005047564A2 PCT/US2004/033864 US2004033864W WO2005047564A2 WO 2005047564 A2 WO2005047564 A2 WO 2005047564A2 US 2004033864 W US2004033864 W US 2004033864W WO 2005047564 A2 WO2005047564 A2 WO 2005047564A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- approximately
- source
- substrate
- seem
- depositing
- Prior art date
Abstract
Description
Claims