WO2005031459A1 - 感光性フレキソ版用ブロック共重合体組成物 - Google Patents
感光性フレキソ版用ブロック共重合体組成物 Download PDFInfo
- Publication number
- WO2005031459A1 WO2005031459A1 PCT/JP2004/013939 JP2004013939W WO2005031459A1 WO 2005031459 A1 WO2005031459 A1 WO 2005031459A1 JP 2004013939 W JP2004013939 W JP 2004013939W WO 2005031459 A1 WO2005031459 A1 WO 2005031459A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- block copolymer
- weight
- composition
- flexographic plate
- photosensitive flexographic
- Prior art date
Abstract
Description
Claims