WO2005010896A1 - Cable insulation system with flexibility, high temperature deformation resistance, and reduced degree of stickiness - Google Patents
Cable insulation system with flexibility, high temperature deformation resistance, and reduced degree of stickiness Download PDFInfo
- Publication number
- WO2005010896A1 WO2005010896A1 PCT/US2004/023723 US2004023723W WO2005010896A1 WO 2005010896 A1 WO2005010896 A1 WO 2005010896A1 US 2004023723 W US2004023723 W US 2004023723W WO 2005010896 A1 WO2005010896 A1 WO 2005010896A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- cable
- degrees celsius
- insulation
- olefinic polymer
- range
- Prior art date
Abstract
Description
Claims