WO2004113403A1 - Functionalized polyalphaolefins - Google Patents
Functionalized polyalphaolefins Download PDFInfo
- Publication number
- WO2004113403A1 WO2004113403A1 PCT/US2004/018972 US2004018972W WO2004113403A1 WO 2004113403 A1 WO2004113403 A1 WO 2004113403A1 US 2004018972 W US2004018972 W US 2004018972W WO 2004113403 A1 WO2004113403 A1 WO 2004113403A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- tert
- functionalized
- polyalphaolefin
- functionalized polyalphaolefin
- alpha
- Prior art date
Abstract
Description
Claims