WO2004096883A1 - Dow global technologies inc - Google Patents
Dow global technologies inc Download PDFInfo
- Publication number
- WO2004096883A1 WO2004096883A1 PCT/US2004/012529 US2004012529W WO2004096883A1 WO 2004096883 A1 WO2004096883 A1 WO 2004096883A1 US 2004012529 W US2004012529 W US 2004012529W WO 2004096883 A1 WO2004096883 A1 WO 2004096883A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- groups
- polyol
- hydroxymethyl
- group
- average
- Prior art date
Abstract
Description
Claims