WO2004083471A2 - Alliage a base de cuivre - Google Patents
Alliage a base de cuivre Download PDFInfo
- Publication number
- WO2004083471A2 WO2004083471A2 PCT/CH2004/000051 CH2004000051W WO2004083471A2 WO 2004083471 A2 WO2004083471 A2 WO 2004083471A2 CH 2004000051 W CH2004000051 W CH 2004000051W WO 2004083471 A2 WO2004083471 A2 WO 2004083471A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- weight
- parts
- alloy
- alloy according
- heat treatment
- Prior art date
Abstract
Description
Claims