WO2004069533A1 - Thin film lamination-delamination process for fluoropolymers - Google Patents
Thin film lamination-delamination process for fluoropolymers Download PDFInfo
- Publication number
- WO2004069533A1 WO2004069533A1 PCT/US2004/001872 US2004001872W WO2004069533A1 WO 2004069533 A1 WO2004069533 A1 WO 2004069533A1 US 2004001872 W US2004001872 W US 2004001872W WO 2004069533 A1 WO2004069533 A1 WO 2004069533A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- layer
- base layer
- receiver sheet
- support layer
- mil
- Prior art date
Abstract
Description
Claims