WO2004058857A2 - Branched polymers from organohydrogensilicon compounds - Google Patents
Branched polymers from organohydrogensilicon compounds Download PDFInfo
- Publication number
- WO2004058857A2 WO2004058857A2 PCT/US2003/040277 US0340277W WO2004058857A2 WO 2004058857 A2 WO2004058857 A2 WO 2004058857A2 US 0340277 W US0340277 W US 0340277W WO 2004058857 A2 WO2004058857 A2 WO 2004058857A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- integer
- group
- formula
- subscript
- groups
- Prior art date
Abstract
Description
Claims