WO2004009689A2 - Carbon blacks and uses thereof - Google Patents
Carbon blacks and uses thereof Download PDFInfo
- Publication number
- WO2004009689A2 WO2004009689A2 PCT/US2003/022432 US0322432W WO2004009689A2 WO 2004009689 A2 WO2004009689 A2 WO 2004009689A2 US 0322432 W US0322432 W US 0322432W WO 2004009689 A2 WO2004009689 A2 WO 2004009689A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- carbon black
- approximately
- particle size
- primary particle
- polymer
- Prior art date
Abstract
Description
Claims