WO2003102042A1 - High-temperature olefin polymerisation process in solution - Google Patents
High-temperature olefin polymerisation process in solution Download PDFInfo
- Publication number
- WO2003102042A1 WO2003102042A1 PCT/US2003/014395 US0314395W WO03102042A1 WO 2003102042 A1 WO2003102042 A1 WO 2003102042A1 US 0314395 W US0314395 W US 0314395W WO 03102042 A1 WO03102042 A1 WO 03102042A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- group
- indenoindolyl
- activator
- complex
- transition metal
- Prior art date
Abstract
Description
Claims